itsallgoodjames
Hazard to Others
Posts: 276
Registered: 31-8-2020
Location: America Lite
Member Is Offline
|
|
How to cut 1oz silver bar into pieces that will fit in a test tube
So I'm planning to synthesize a handful of silver salts. In anticipation of this, I bought a 1oz bar of silver. If one wanted to cut said bar into
approximately 1cm3 pieces, how would one go about that? I've already tried with wire cutters, and while they put a decent dent in the
silver, they didn't cut all the way through. I guess the silver is too hard. So how would one cut it? A hacksaw would probably work, but I'd
imagine that I'd lose quite a lot of silver doing it they way.
Thanks!
Nuclear physics is neat. It's a shame it's so regulated...
Now that I think about it, that's probably a good thing. Still annoying though.
|
|
|
Texium
Administrator
Posts: 4619
Registered: 11-1-2014
Location: Salt Lake City
Member Is Offline
Mood: PhD candidate!
|
|
Well any silver salt you make is going to necessarily go through silver nitrate as an intermediate, so you might as well toss the entire bar in a
beaker and dissolve the whole thing in nitric acid (outside though, as lots of NO2 will be produced too).
|
|
|
itsallgoodjames
Hazard to Others
Posts: 276
Registered: 31-8-2020
Location: America Lite
Member Is Offline
|
|
That was the plan originally, but the issue is that it'll go through nearly all of my nitric acid to dissolve the whole thing. I guess having to
distill some more acid wouldn't be that big of a deal though. I'm already nearly out.
Nuclear physics is neat. It's a shame it's so regulated...
Now that I think about it, that's probably a good thing. Still annoying though.
|
|
|
Metallophile
Hazard to Self
Posts: 87
Registered: 23-3-2018
Member Is Offline
Mood: No Mood
|
|
Maybe clamp the corner in a vice, and bend it back and forth until it breaks from fatigue?
|
|
|
itsallgoodjames
Hazard to Others
Posts: 276
Registered: 31-8-2020
Location: America Lite
Member Is Offline
|
|
That's a great idea. I'll definitely try it. Then I can conserve more of my nitric acid
Nuclear physics is neat. It's a shame it's so regulated...
Now that I think about it, that's probably a good thing. Still annoying though.
|
|
|
unionised
International Hazard
Posts: 5128
Registered: 1-11-2003
Location: UK
Member Is Offline
Mood: No Mood
|
|
Hammer it into a thinner sheet, and then cut with tin-snips.
Even simpler- put as much of your nitric acid as you wish to use for this project into a beaker, add the silver bar.
leave it to react.
When the initial reaction slows down, warm the solution.
The reaction will stop when you run out of acid.
You can remove the remaining silver- probably by pouring off the solution; you might have to filter it.
That will give you silver nitrate solution.
|
|
|
clearly_not_atara
International Hazard
Posts: 2800
Registered: 3-11-2013
Member Is Offline
Mood: Big
|
|
Agree with unionised, or at least try hammering it, it allows you to cut more accurately and it's easier to store and weigh metallic silver
than any of its salts.
Quote: Originally posted by Texium (zts16)  | | Well any silver salt you make is going to necessarily go through silver nitrate as an intermediate, so you might as well toss the entire bar in a
beaker and dissolve the whole thing in nitric acid (outside though, as lots of NO2 will be produced too). |
If you can obtain methanesulfonic acid, silver methanesulfonate is just as soluble without releasing any toxic gas. Same for trifluoroacetate and
probably for ethanesulfonate. In all of these acids you dissolve silver by adding some H2O2.
Silver pyroglutamate is also reported as "soluble in hot water" but no numbers were given in any papers I found. OTC, but speculative. I can find it
easily online as a dietary supplement.
[Edited on 30-10-2020 by clearly_not_atara]
|
|
|
Fulmen
International Hazard
Posts: 1726
Registered: 24-9-2005
Member Is Offline
Mood: Bored
|
|
I would try cutting it with a chisel. For softer metals it can be surprisingly effective.
We're not banging rocks together here. We know how to put a man back together.
|
|
|
phlogiston
International Hazard
Posts: 1379
Registered: 26-4-2008
Location: Neon Thorium Erbium Lanthanum Neodymium Sulphur
Member Is Offline
Mood: pyrophoric
|
|
Melt it and pour the molten metal into a large bucket of cold water. It will produce granules of silver, with the size problably depending on a few
factors like pouring speed and temperature, but typically they come out about the size of peas.
Its a common method to convert silver into a form thats very convenient for weighing out some amount to use.
[Edited on 30-10-2020 by phlogiston]
-----
"If a rocket goes up, who cares where it comes down, that's not my concern said Wernher von Braun" - Tom Lehrer |
|
|
itsallgoodjames
Hazard to Others
Posts: 276
Registered: 31-8-2020
Location: America Lite
Member Is Offline
|
|
That was one of the things I was thinking in the beginning, but I'd have to go buy a new chisel, because I accidentally blunted it trying to do that
with copper. From what I've read, silver is only a bit softer than copper, so I have a feeling it wouldn't work all that well
Nuclear physics is neat. It's a shame it's so regulated...
Now that I think about it, that's probably a good thing. Still annoying though.
|
|
|
itsallgoodjames
Hazard to Others
Posts: 276
Registered: 31-8-2020
Location: America Lite
Member Is Offline
|
|
| Quote: Originally posted by phlogiston | Melt it and pour the molten metal into a large bucket of cold water. It will produce granules of silver, with the size problably depending on a few
factors like pouring speed and temperature, but typically they come out about the size of peas.
Its a common method to convert silver into a form thats very convenient for weighing out some amount to use.
[Edited on 30-10-2020 by phlogiston] |
I would make it into shot, except for I don't have any way to melt it.
Nuclear physics is neat. It's a shame it's so regulated...
Now that I think about it, that's probably a good thing. Still annoying though.
|
|
|
itsallgoodjames
Hazard to Others
Posts: 276
Registered: 31-8-2020
Location: America Lite
Member Is Offline
|
|
| Quote: Originally posted by clearly_not_atara |
If you can obtain methanesulfonic acid, silver methanesulfonate is just as soluble without releasing any toxic gas. Same for trifluoroacetate and
probably for ethanesulfonate. In all of these acids you dissolve silver by adding some H2O2.
Silver pyroglutamate is also reported as "soluble in hot water" but no numbers were given in any papers I found. OTC, but speculative. I can find it
easily online as a dietary supplement.
[Edited on 30-10-2020 by clearly_not_atara] |
The NO2 isn't really all that much of a concern. I've worked with nitric acid numerous times in the past, so an alternative acid isn't really needed.
I checked, and all the other ones you mentioned are more expensive per gram than nitric acid, even if I wanted to buy the nitric rather than make it.
Plus, a lot of what I want to do with the silver requires it to be the nitrate salt anyways, so it doesn't really make any sense to go with any of
those. I'll probably end up flattening it with a hammer and cut it with tin snips or pliers
Nuclear physics is neat. It's a shame it's so regulated...
Now that I think about it, that's probably a good thing. Still annoying though.
|
|
|
Clear_horizons_glass
Harmless
Posts: 42
Registered: 30-9-2019
Location: Pullman, WA
Member Is Offline
Mood: Glass
|
|
So I cut silver for giving an iridized affect to glass all the time.
an easier solution I would suggest is to just go out and get a silver coin. Grab one end with some pliers, and beat the other end flat with a hammer
on something hard like concrete. Then you can just cut the silver with tin snips without to much effort.
[Edited on 30-10-2020 by Clear_horizons_glass]
[Edited on 30-10-2020 by Clear_horizons_glass]
Clear Horizons Laboratory Glassblowing Services
-------------------------------------------------------------
www.clearhorizonsglass.com
Phone and Fax:
(855) LAB-GLAS
(855) 522-4527
Have a glass project you want made? email me at
info@clearhorizonsglass.com
or message us here |
with a U2U |
message |
\/
|
|
|
clearly_not_atara
International Hazard
Posts: 2800
Registered: 3-11-2013
Member Is Offline
Mood: Big
|
|
| Quote: Originally posted by itsallgoodjames |
The NO2 isn't really all that much of a concern. I've worked with nitric acid numerous times in the past, so an alternative acid isn't really needed.
I checked, and all the other ones you mentioned are more expensive per gram than nitric acid |
I was unaware of your experience, of course. I mention the alternative acids all the time, because I think a lot of people won't even consider silver
chemistry for this reason, which is unfortunate because Ag is an entry point to some of the most interesting chemistry that is accessible with minimal
equipment -- obviously photography, but also lots of other stuff.
Pyroglutamic acid is apparently available as a dietary supplement, so maybe I can make my own data about how well it works.
|
|
|
Herr Haber
International Hazard
Posts: 1236
Registered: 29-1-2016
Member Is Offline
Mood: No Mood
|
|
Unless carefull and used to them you are going to have small losses by the chemical processes. Also, it involves waste management.
The hackswaw method isnt that bad and it avoids a lot of efforts. You might also lose some silver here but with a piece of paper under the vice you
should get most of it. I use the hacksaw to cut pieces I can put through the neck of my reactor so I'm certain all the nitric acid is used up.
In both cases you'll probably lose a bit but still will have probably more than 30 grams to experiment with including losses.
You seem to have only a little bit of acid left. Cut, bend, tear, flatten if you can and then use your acid. Go for a beaker if your samples are above
1-2 grams
Next time get a one ounce COIN 
The spirit of adventure was upon me. Having nitric acid and copper, I had only to learn what the words 'act upon' meant. - Ira Remsen
|
|
|
unionised
International Hazard
Posts: 5128
Registered: 1-11-2003
Location: UK
Member Is Offline
Mood: No Mood
|
|
The trouble with a hacksaw is iron contamination- especially of the "sawdust", if you plan to catch + re-use it.
I guess an HCl wash of the metal would strip Fe but leave Ag behind.
But I still think the easy "solution" is to put the metal in a beaker with however much nitric you want to "spare" for this purpose, and let it react.
Incidentally, does adding H2O2 to HNO3 work?
Does the NOx get oxidised back to HNO3?
|
|
|
B(a)P
International Hazard
Posts: 1139
Registered: 29-9-2019
Member Is Offline
Mood: Festive
|
|
I will give it a try later today and report back.
[Edited on 30-10-2020 by B(a)P]
In a flask1 g of silver was added to 2 mls dH2O and 2 mls HNO3 70%
In a beaker (that is all I had) 1 g of silver was added to 2 mls 35% H2O2 and 2 mls HNO3 70%
Very little happened at room temp, but upon heating both vessels were visibly reacting and no NO2 was visible from the vessel with peroxide.
I will check yields tomorrow and report back.
Next test might be to add more silver than the acid can dissolve and see which mix results in less silver.
[Edited on 31-10-2020 by B(a)P]
Sorry this post got a bit screwed up because of a passing lighting storm. Here is the comparison with a little heat.
[Edited on 31-10-2020 by B(a)P]
[Edited on 31-10-2020 by B(a)P]
|
|
|
Fulmen
International Hazard
Posts: 1726
Registered: 24-9-2005
Member Is Offline
Mood: Bored
|
|
There might be some language issues at play here. I was thinking of a stone chisel, not a wood chisel.
I discovered this while making some metal strips from stainless steel pipe (only suitable stock i had). Hacksaws don't really cut well in soft
stainless, so I ended up parting rings of steel tubing and then split them using a stone chisel before hammering them down into flat strips. It's
surprisingly effective on softer metals.
We're not banging rocks together here. We know how to put a man back together.
|
|
|
itsallgoodjames
Hazard to Others
Posts: 276
Registered: 31-8-2020
Location: America Lite
Member Is Offline
|
|
I think I'm going to hammer it reasonably thin, then cut it with tin snips. Next time I'll buy some silver shot on eBay and save all the effort. No
clue why I didn't do that beforehand, given I generally purchase metals in the form of turnings or powder. Not like that'll be any time soon though,
as I usually work on very small scales (less than a gram) for most things, due to cost, among other reasons. That's why I was asking about using a
test tube, rather than a beaker. Anyways, thanks for the help
Nuclear physics is neat. It's a shame it's so regulated...
Now that I think about it, that's probably a good thing. Still annoying though.
|
|
|
TriiodideFrog
Hazard to Others
Posts: 108
Registered: 27-9-2020
Member Is Offline
|
|
You could melt the silver and try to pour it into a quartz test tube. If you have to get the silver back out, you can just sacrifice the test tube.
|
|
|
symboom
International Hazard
Posts: 1143
Registered: 11-11-2010
Location: Wrongplanet
Member Is Offline
Mood: Doing science while it is still legal since 2010
|
|
Bolt cutters Will take a chunk out of it.
[Edited on 31-10-2020 by symboom]
|
|
|
j_sum1
Administrator
Posts: 6336
Registered: 4-10-2014
Location: At home
Member Is Offline
Mood: Most of the ducks are in a row
|
|
| Quote: Originally posted by TriiodideFrog | | You could melt the silver and try to pour it into a quartz test tube. If you have to get the silver back out, you can just sacrifice the test tube.
|
This would seem to be the worst of the suggestions so far. The prece difference between silver and quartz glassware would make this prohibitive.
I would think dissolving what you need in HNO3 as you need it would make the most sense.
|
|
|
unionised
International Hazard
Posts: 5128
Registered: 1-11-2003
Location: UK
Member Is Offline
Mood: No Mood
|
|
| Quote: Originally posted by TriiodideFrog | | You could melt the silver and try to pour it into a quartz test tube. If you have to get the silver back out, you can just sacrifice the test tube.
|
You could.
You could take your clothes off and run round naked.
It also wouldn't help.
It would have the advantage that you wouldn't need to waste money on a quartz tube and even more so, it wouldn't raise the problem of melting the
silver - which the OP said he couldn't do.
"
I would make it into shot, except for I don't have any way to melt it."
|
|
|
Fyndium
International Hazard
Posts: 1192
Registered: 12-7-2020
Location: Not in USA
Member Is Offline
|
|
Never cut any precious metals with sawing or grinding tools. You will lose a huge amount, even if you try to collect the dust.
Get bigger cutters, or borrow bolt cutters.
Try cold chiseling it in a vise.
Put it in a drill press, drill it with clean and sharp bit with low rpm and collect the turnings.
Cast it into round bar and turn it in a lathe for more turnings.
I used to squeeze metal into thinner form with 50 ton hydraulic press. Use smaller mandrels to get more pressure per area, with 10mm square HSS bars I
can form pretty much any metal, including non-hardened steel. If you've got even more access, you can turn a drawing mandrel and just press the metal
into a wire of desired diameter.
|
|
|
zed
International Hazard
Posts: 2284
Registered: 6-9-2008
Location: Great State of Jefferson, City of Portland
Member Is Offline
Mood: Semi-repentant Sith Lord
|
|
Easy. Just make some more Nitric Acid.
Or, employ a jewelers saw, to cut uo your bar. Hold it over a beaker, to catch any filings.
Owning a jewelers saw, is very handy. The hair-like blades are inexpensive, sharp and efficient.
https://www.ebay.com/itm/GERMAN-STYLE-SAW-FRAME-JEWELERS-SAW...
[Edited on 31-10-2020 by zed]
|
|
|
| Pages:
1
2 |
![[*]](images/xpblue/default_icon.gif){kind=icon}