NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
Borax and PVA
I am trying out the polymer experiment with PVA glue and borax to make the poor mans 'flubber'.
I have u2ed aga to see if he would copy this and rack the product on his stretcher he made for the commercial stuff.
My question though is..
What else apart from Borax can i use with PVA to make a polymer? I am trying to see how it compares with polymers like the one they tried out on the
rack.
The Borax/PVA experiment is common, but i wondered if any other polymers could be made with PVA?
|
|
|
aga
Forum Drunkard
Posts: 7030
Registered: 25-3-2014
Member Is Offline
|
|
Erm, doesn't the 'P' part of PVA stand for polymer ?
Sure i'll copy your synth, when documented/posted and stretch it to bits.
With data.
Edit:
What kind of stretchy-snappy-o-meter owner wouldn't ?
[Edited on 8-9-2016 by aga]
|
|
|
j_sum1
Administrator
Posts: 6325
Registered: 4-10-2014
Location: At home
Member Is Offline
Mood: Most of the ducks are in a row
|
|
To answer your question NEMO, you need to know what is happening with the borax to form the cross-linking. In all honesty, I forget the details but
it is googleable. There are undoubtedly plenty of other cross-linking agents but borax happens to be particularly accessible.
If you are trying to duplicate the experiment elsewhere in the world you need to be aware that not all PVA is the same. The composition -- and in
particular the water content does vary a lot. The polymer chain length and the amount of branching present is also likely to be different. This
makes duplication difficult -- unless you send aga some bottles of your reagents. And even then, it is 42°C in aga's shed and -3 in Scotland.
Reproducibility is an issue.
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
I was kind of interested in how the stuff compares with the other polymer he racked. So i figure for that any PVA will do as long as he uses the same
brand each time.
When i get home i will dig up the info from the Royal society where i saw the experiment.
I have seen PVA described as Poly Vinyl Alcohol and Poly Vinyl Acrylate, so i am not too sure what it actually stands for!
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
This is the first one
http://www.rsc.org/learn-chemistry/resource/res00000756/pva-...
There is also one using PVA to make a harder polymer, i will track that down again.
From memory the RSC one is more of a slime than something to stretch. I will find the other one but it mostly comes down to how much Borax you add (up
to a point), add too much and it breaks down again.
[Edited on 9-9-2016 by NEMO-Chemistry]
|
|
|
aga
Forum Drunkard
Posts: 7030
Registered: 25-3-2014
Member Is Offline
|
|
Doesn't sound too hard to find out how much ... let's see ...
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
A little bit left field but, having read a couple of papers it looks like various versions of PVA with formaldehyde and other additives have been used
in medicine.
One use is for a temporary skin covering for compound fractures etc, the PVA is turned into a kind of foam.
Another use seems to be immobilizing yeast/microbes in waste water treatment. As it can be made into a very thin film this got me thinking, i wonder
if a water proof version could be used as a Ion exchange membrane or a kind of 'salt bridge in a electrolysis cell?
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
You have beaten me!! Off to the shops at 8:30am to grab some more PVA  .
Slime is apparently 8% Borax, i will grab what info i can find tonight. I have also seen mention of curing with heat.
Can you link to the stuff you did with your stretchO meter? Turns out to be handy Gizmondo you made there.
|
|
|
aga
Forum Drunkard
Posts: 7030
Registered: 25-3-2014
Member Is Offline
|
|
Percentages are a bit hard to calculate as this wood glue bottle just says 'Good for sticking any kind of wood, paper, cardboard etc. Do Not Eat' on
it.
Edit:
Snappy Sugru thing :-
http://www.sciencemadness.org/talk/viewthread.php?tid=66382&...
[Edited on 9-9-2016 by aga]
|
|
|
aga
Forum Drunkard
Posts: 7030
Registered: 25-3-2014
Member Is Offline
|
|
Hmm. Mabye Less is More after all ...
Left to right we have PVA samples A B C D
14.3g, 17.6g, 18.8g, 15.4g wood glue respectively.
(the glue 'dollops' rather than pours)
All were diluted to 100g with distilled water, then mixed thoroughly.
A borax solution was made from 10g borax decahydrate made up to 100g with water.
This was stuck in a 650W microwave for 30 seconds as the borax did not want to dissolve. After heating it dissolved completely.
Sample A had 30g of the borax solution added, stirred vigorously.
Immediately on stopping stirring a precipitate formed.
Sample B had 20g, C had 10g and D had 5g of the borax solution and all were treated in the same way with a fresh disposable stirrer.
For good measure all samples were put in the microwave for 90 seconds and mixed again, then left to settle.
After decanting off the water, the samples were dumped onto aluminium foil.
Only samples C and D exhibit any cohesivity.
A and B are more like pastes.
Conclusion:-
Mess with it some more to see if it can be cross-linked enough to make it stretchy, probably bash it a bit to get more water out.
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
I found PVA glue as a non brand bottle, off to town to look in builders merchants for larger amount of a branded one.
My thinking is the RSC mention 4% and 8% solutions (presumably of glue), a branded product 'might' have a MSDS so that 'might' tell me the %.
I will modify your experiment slightly, test tubes same length and same amount in each, glue unwatered first and time how long for it to exit an
upturned tube.
I might also try and use a microwave to gently dry it a little, i dont have formaldehyde so cant try that yet.
Apart from that i will use same amounts as you did and also some with no water added.
I found several references to it stretched slowly, so i take it we just have to mess with amounts until we get it right .
Thanks for the 'RACK' thread, once i get something that resembles a rubber/polymer, i will know what shape to cut. I can get the rest of the stuff
ready while i wait for the bus!!
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
Havnt tracked it down yet but looks like there is some info in the Journal of chemical education.
Journal of Chemical Education, Jan. 1986, #63, pp. 57-60
I will see if i can find it on scihub.
Sci-Hub seems down for me, i will try again later!
Found the article reference though
10.1021/ed063p57
[Edited on 10-9-2016 by NEMO-Chemistry]
Found a working server, the article dosnt say much more than is already known. Out of interest if i post any papers do i do it in the thread or in
references?
[Edited on 10-9-2016 by NEMO-Chemistry]
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
Should have checked first!! shop shuts at lunchtime on a Saturday! I will have to grab some Monday now  . Gives me a chance to look into a couple of things i want to try out .
|
|
|
aga
Forum Drunkard
Posts: 7030
Registered: 25-3-2014
Member Is Offline
|
|
Might not be a great result this here PVA + Borax.
This afternoon the precipitates are basically lumps of white rock, having sat out in 38+ C all day.
If the material needs the water, yet loses it, i doubt i'll be able to make any standard conditions under which to test it.
Hmm. Maybe it likes oil ...
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
We might manage 3.8C here but i doubt its going to go past 5C this week lol.
As always there seems to be conflicting advice on how to prepare! Got some old glue from the back of the shed, not much in it so maybe worth spending
my time reading up and getting the 'slope 'O' Meter built'.
|
|
|
aga
Forum Drunkard
Posts: 7030
Registered: 25-3-2014
Member Is Offline
|
|
Just measure, mix and observe.
There isn't much more to it than that.
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
I might have got it entirely wrong. I tried with a small amount of the white PVA and didnt get anything worth while.
reading up some more it looks like i should use the clear PVA glue like the elmers stuff. I am not positive but i think they are slightly different.
Anyway apparently in acid they fall apart and in alkali they dont, i will grab some on the way home tomorrow and get cracking on it.
if i get it working we hit another problem......Turns out it is meant to be a non Newtonian fluid, so if we stretch it slowly it will stretch and
stretch and stretch. But try and stretch it quickly and it breaks.
So i will give it a go, but its likely not to work out how i was hoping.
|
|
|
wg48
National Hazard
Posts: 821
Registered: 21-11-2015
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by NEMO-Chemistry  | I might have got it entirely wrong. I tried with a small amount of the white PVA and didnt get anything worth while.
reading up some more it looks like i should use the clear PVA glue like the elmers stuff. I am not positive but i think they are slightly different.
Anyway apparently in acid they fall apart and in alkali they dont, i will grab some on the way home tomorrow and get cracking on it.
if i get it working we hit another problem......Turns out it is meant to be a non Newtonian fluid, so if we stretch it slowly it will stretch and
stretch and stretch. But try and stretch it quickly and it breaks.
So i will give it a go, but its likely not to work out how i was hoping. |
I think the white glue is an emulsion of polyvinyl acetate while the clear glue is a solution of polyvinyl alcohol. I would expect the borax to
combine with the alcohol more easily than the acetate. Does the acetate work?
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
| Quote: Originally posted by wg48 | | Quote: Originally posted by NEMO-Chemistry | I might have got it entirely wrong. I tried with a small amount of the white PVA and didnt get anything worth while.
reading up some more it looks like i should use the clear PVA glue like the elmers stuff. I am not positive but i think they are slightly different.
Anyway apparently in acid they fall apart and in alkali they dont, i will grab some on the way home tomorrow and get cracking on it.
if i get it working we hit another problem......Turns out it is meant to be a non Newtonian fluid, so if we stretch it slowly it will stretch and
stretch and stretch. But try and stretch it quickly and it breaks.
So i will give it a go, but its likely not to work out how i was hoping. |
I think the white glue is an emulsion of polyvinyl acetate while the clear glue is a solution of polyvinyl alcohol. I would expect the borax to
combine with the alcohol more easily than the acetate. Does the acetate work? |
The acetate does work 'i think', i didnt have enough to fully try it but one lot got close.
I think the acetate is alot more fussy about quantity of Borax than the alcohol. I will know later when i get home, i managed to grab a bottle at the
start of lunch.
The confusion came from a number of web sites that stated both the clear and the white glue were the same thing, as you point out this isnt so.......
I found alot of reference to the clear stuff coming in 4% and 8% concentrations, but i think the acetate is different.
|
|
|
careysub
International Hazard
Posts: 1339
Registered: 4-8-2014
Location: Coastal Sage Scrub Biome
Member Is Offline
Mood: Lowest quantum state
|
|
I have no experimental experience with slime production, so cannot say how well Elmer's Glue polyvinyl acetate white glue works with borax (if at
all), but the literature seems to be clear that polyvinyl alcohol clear glue is required.
It is unfortunate that PVA is used indiscriminately for both polyvinyl acetate and polyvinyl alcohol, indeed I have run across articles that deal with
both, but use the acronym without explanation making it unclear what they are saying.
And although polyvinyl alcohol adhesive is a real thing (used for document conservation use for example) it is scarce on the market, acetate white
glues overwhelming predominate. I think Elmer's clear school glue may be polyvinyl alcohol, but their SDS does not say what is in it - just
asserting that it is 100% "Non-hazardous substance" (Love that non-hazardous substance! Use it all the time!).
You can find real polyvinyl alcohol adhesive on Amazon by searching on that phrase, and there are many vendors of polyvinyl alcohol solution and
powder on eBay (mostly marketed for slime use).
Here is the Journal of Chemical Education article about slime AND one for making the alcohol from the acetate by alkaline hydrolysis.
Attachment: casassa1986.pdf (3.3MB)
This file has been downloaded 856 times
Attachment: chen2006.pdf (87kB)
This file has been downloaded 391 times
[Edited on 12-9-2016 by careysub]
[Edited on 12-9-2016 by careysub]
|
|
|
wg48
National Hazard
Posts: 821
Registered: 21-11-2015
Member Is Offline
Mood: No Mood
|
|
| Quote: Originally posted by NEMO-Chemistry | | Quote: Originally posted by wg48 | | Quote: Originally posted by NEMO-Chemistry | I might have got it entirely wrong. I tried with a small amount of the white PVA and didnt get anything worth while.
reading up some more it looks like i should use the clear PVA glue like the elmers stuff. I am not positive but i think they are slightly different.
Anyway apparently in acid they fall apart and in alkali they dont, i will grab some on the way home tomorrow and get cracking on it.
if i get it working we hit another problem......Turns out it is meant to be a non Newtonian fluid, so if we stretch it slowly it will stretch and
stretch and stretch. But try and stretch it quickly and it breaks.
So i will give it a go, but its likely not to work out how i was hoping. |
I think the white glue is an emulsion of polyvinyl acetate while the clear glue is a solution of polyvinyl alcohol. I would expect the borax to
combine with the alcohol more easily than the acetate. Does the acetate work? |
The acetate does work 'i think', i didnt have enough to fully try it but one lot got close.
I think the acetate is alot more fussy about quantity of Borax than the alcohol. I will know later when i get home, i managed to grab a bottle at the
start of lunch.
The confusion came from a number of web sites that stated both the clear and the white glue were the same thing, as you point out this isnt so.......
I found alot of reference to the clear stuff coming in 4% and 8% concentrations, but i think the acetate is different. |
Not the best source but wiki thinks they both work.
Apparently there are different grades of PVAl depending how much acetate is left in them. This suggests that there are also different grades of PVAc
depending on the acetate content.
Perhaps borax is sufficiently alkaline to catalyze the replacement or hydrolysis of the acetate.
Of cause you can dry a sample of your PVA and weigh it before and after to determine its water content.
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
Thanks for that, yes some of the sites are confusing. I will get some powder and make some, i also found a paper that says you can use acetate but it
dosnt seem as straightforward.
Some sites just refer to white wood glue, this i have always taken to mean the Acetate and the clear glue to be the alcohol.
Acetate does link but it isnt what i am after by a long way!! Thanks for the links. Time to go spending on ebay .
|
|
|
careysub
International Hazard
Posts: 1339
Registered: 4-8-2014
Location: Coastal Sage Scrub Biome
Member Is Offline
Mood: Lowest quantum state
|
|
| Quote: Originally posted by wg48 | ...
Not the best source but wiki thinks they both work.
Apparently there are different grades of PVAl depending how much acetate is left in them. This suggests that there are also different grades of PVAc
depending on the acetate content.
Perhaps borax is sufficiently alkaline to catalyze the replacement or hydrolysis of the acetate.
Of cause you can dry a sample of your PVA and weigh it before and after to determine its water content.
|
Yes the presence of some alcohol in a white glue might account for its "sliming", and also perhaps the borax does do some hydrolysis also.
Perhaps someone can attempt a two-step process with hydrolysis with a strong alkali, followed by cross-linking with borax?
|
|
|
NEMO-Chemistry
International Hazard
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
| Quote: Originally posted by careysub | | Quote: Originally posted by wg48 | ...
Not the best source but wiki thinks they both work.
Apparently there are different grades of PVAl depending how much acetate is left in them. This suggests that there are also different grades of PVAc
depending on the acetate content.
Perhaps borax is sufficiently alkaline to catalyze the replacement or hydrolysis of the acetate.
Of cause you can dry a sample of your PVA and weigh it before and after to determine its water content.
|
Yes the presence of some alcohol in a white glue might account for its "sliming", and also perhaps the borax does do some hydrolysis also.
Perhaps someone can attempt a two-step process with hydrolysis with a strong alkali, followed by cross-linking with borax? |
I will give it a go, I found some similar information on the glues containing different amounts of Acetates and alcohol.
Might get it working after all!
|
|
|
aga
Forum Drunkard
Posts: 7030
Registered: 25-3-2014
Member Is Offline
|
|
What will 'working' be ?
A rubbery thing ?
|
|
|