chemoleo
Biochemicus Energeticus
Posts: 3005
Registered: 23-7-2003
Location: England Germany
Member Is Offline
Mood: crystalline
|
|
Would you like to summarise this here so that it's on record forever, if it is such an easy and effective method?
Never Stop to Begin, and Never Begin to Stop...
Tolerance is good. But not with the intolerant! (Wilhelm Busch)
|
|
|
gilbert pinkston
Harmless
Posts: 9
Registered: 22-9-2004
Member Is Offline
Mood: No Mood
|
|
such an easy and effective method?
that possibly implies its a piece of cake and its not but it will get you O4 when you dont have any and all you care to make and it is cheap!!!! some
people from what ive read have spent a fortune on this subject i use a $3 power supply or cheap battery charger and homemade Pb(NO3)2 .......i could
go on but would just be repeating what ive already posted (with some pix) and should be avaliable
|
|
|
12AX7
Post Harlot
Posts: 4803
Registered: 8-3-2005
Location: oscillating
Member Is Offline
Mood: informative
|
|
| Quote: | | Originally posted by gilbert pinkstonand homemade Pb(NO3)2 ....... |
So it's the same old "plate PbO2 out of nitrate solution" trick?
Tim
|
|
|
gilbert pinkston
Harmless
Posts: 9
Registered: 22-9-2004
Member Is Offline
Mood: No Mood
|
|
So it's the same old "plate PbO2 out of nitrate solution" trick?
Tim
yep it works for me but it ain't purty
|
|
|
neutrino
International Hazard
Posts: 1583
Registered: 20-8-2004
Location: USA
Member Is Offline
Mood: oscillating
|
|
Could you clarify your last couple of posts? They make no sense.
|
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
Plating PbO2 from Pb Acetate
Well, I'm getting ready to try to plate PbO2 onto a tantalum rod and also onto platinum wire.
I would like to use a lead acetate plating bath, as mentioned here:
http://www.geocities.com/CapeCanaveral/Campus/5361/chlorate/...
Unfortunately this web page doesn't go into too much detail regarding the process and composition of the plating bath. All it says is: "The
lead acetate should be at a concentration of 0.5 mol/dm^3, + acetic acid and the current density fairly low".
I wonder about things like optimum temperature, current density, pH, whether stirring is required, cathode materials, additives, etc.
Does anyone have access to the references mentioned on the page: "Journal of Applied Chemistry 16 (1966) p180. See also Metallurgical
Transactions, vol 16B, (1985) PP 489 - 496".
I would really like to see the Journal of Applied Chemistry article on the subject before trying it.
BTW, there's a guy selling 12 inches of 0.5 mm diameter pure platinum wire on ebay right now for $33.00. With platinum now being at $921.00 per
ounce (and moving steadily upward), this seems like a fairly good deal.
http://cgi.ebay.com/PLATINUM-WIRE-12-inches-99-9-PURE_W0QQit...
|
|
|
vulture
Forum Gatekeeper
Posts: 3330
Registered: 25-5-2002
Location: France
Member Is Offline
Mood: No Mood
|
|
Quickie question? Why do you want to coat platinum or tantalum with PbO2? They are both good enough as is for chlorate electrolysis, if that's
the intended purpose.
One shouldn't accept or resort to the mutilation of science to appease the mentally impaired.
|
|
|
12AX7
Post Harlot
Posts: 4803
Registered: 8-3-2005
Location: oscillating
Member Is Offline
Mood: informative
|
|
Doesn't tantalum kinda anodize in solution?
You didn't mention perchlorate either, cheap graphite can be used all day for chlorate. Most PbO2 goes for perc.
Tim
|
|
|
gilbert pinkston
Harmless
Posts: 9
Registered: 22-9-2004
Member Is Offline
Mood: No Mood
|
|
NaClO4 crystals made with graphite then PbO2 from NaCl
http://eseephoto.com/albums/47156/019294_189044.jpg
|
|
|
12AX7
Post Harlot
Posts: 4803
Registered: 8-3-2005
Location: oscillating
Member Is Offline
Mood: informative
|
|
Those are quite large indeed. Wouldn't it be cool if they were colored? 
|
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
I think platinum is only suitable as an anode for chlorate production in cases where low chloride ion concentration cannot occur, right? This would
apparently make platinum not a good choice for a batch process (which is what most of us would probably have, I think).
Regarding tantalum, other than as a substrate for platinum or PbO2, I haven't heard of it being used directly as an anode for chlorate
production.
Anyway, I'd like to go directly from Cl to ClO4, which apparently rules out everything but PbO2.
I want to try to build up a robust layer of PbO2, and then mechanically remove the substrate.
Does anyone have access to the article: Journal of Applied Chemistry 16 (1966) p 180? I'd really appreciate any details regarding the Pb Acetate
plating bath that might be in this paper.
| Quote: | Originally posted by vulture
Quickie question? Why do you want to coat platinum or tantalum with PbO2? They are both good enough as is for chlorate electrolysis, if that's
the intended purpose. |
|
|
|
Cyrus
Hazard to Others
Posts: 397
Registered: 24-4-2004
Location: Ancient Persia
Member Is Offline
Mood: No Mood
|
|
PbO2 ceramic substrate anode progress
I fired all of the ceramic substrates I described earlier. Some cracked, but that's what you get for firing ceramics in a 6" wide
"kiln". But I did make enough that I have plenty. 
Next, I tried to get lead nitrate to dip the substrates in, after which I would have let them dry and then dipped them in bleach to fill the ceramic
with PbO2.
I figured that nitric acid ought to attack lead, since lead nitrate is soluble in water. I stuck about 105 g (IIRC) of lead in a 600 ml beaker, added
water until it read at 150 ml, and then slowly added 70 ml of 61-70% nitric acid. It bubbled vigorously at first, probably because of the corroded
lead surface, but after a while the reaction seemed so significantly slow down, with little bubbling visible. (20 ml of acid had been added) I added
the rest of the nitric acid, and bubbles still formed really slowly. It doesn't make sense that lead would be passivated if lead nitrate is
soluble. The bubbles formed were clear and odorless as far as I could tell, but I didn't sniff much.
Cyrus
|
|
|
Twospoons
International Hazard
Posts: 1324
Registered: 26-7-2004
Location: Middle Earth
Member Is Offline
Mood: A trace of hope...
|
|
I made my lead nitrate with 60% acid - no dilution at all. The lead dissolved nicely - though there was some NO2 released. You can speed the process
by first pouring the molten lead into a bucket of water, slowly, from a height of about 1 metre. The lead drops deform into thin flat
'splats' and freeze in the water, giving you a huge reaction surface.
Helicopter: "helico" -> spiral, "pter" -> with wings
|
|
|
Fleaker
International Hazard
Posts: 1252
Registered: 19-6-2005
Member Is Offline
Mood: nucleophilic
|
|
Additionally, lead can easily be pounded/rolled out flat for a higher surface area. Much safer than casting shot.
Believe it or not, casting shot isn't exactly as straightforward as it would seem and I wouldn't recommend doing it without wearing long
sleeves/pants, face shield, and a heavy apron. Lead isn't too bad since it's dense and at a reasonably low temperature. Aluminum, however,
is not a good metal to pour into water as getting molten aluminum on your skin is worse than molten iron. (Aluminum will stick onto your flesh while
iron will pop off because of the water content.)
|
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
Why Not Conductive Substrates For PbO2?
I've read of ceramic substrates being used to avoid the problem of conductor erosion due to pin holes and cracks in the PbO2 coating. But would
this still be a problem if the electrical connection was made only to the PbO2 layer?
IOW, what difference would it make if the substrate were a conductor (say almost any convenient metal), or a nonconductor, so long as the electrical
connection is made to the PbO2 layer itself and not the conductor?
|
|
|
Cyrus
Hazard to Others
Posts: 397
Registered: 24-4-2004
Location: Ancient Persia
Member Is Offline
Mood: No Mood
|
|
What are you thinking of using? Metals tend to erode in a perchlorate bath, and getting a perfect lead dioxide coating is pretty hard.
Why not ceramic AND conducting? 
The lead nitrate is still just sitting in a beaker, and there are lots of fine white crystals on the bottom. I'm betting that after a month or
so, the reaction is complete. The ceramic substrates have been fired. I guess I can make PbO2 anodes now... I'll just need to find time.
Cyrus
|
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
I was thinking you could use almost any metal that would hold up during the PbO2 plating process; even graphite.
When I eventually get around to it, I plan on using a lead acetate/acetic acid plating bath.
My question is: Would pin holes really matter very much if, during operation of the perchlorate cell the electrical connection is made to the PbO2
itself and not to the conducting substrate?
|
|
|
MadHatter
International Hazard
Posts: 1339
Registered: 9-7-2004
Location: Maine
Member Is Offline
Mood: Enjoying retirement
|
|
Pinholes
Electricity flows along the surface so any pinholes in contact with the PbO2 would
become part of that surface and be attacked in the process. It's essential that there
be no pinholes or use a non-conducting substrate. I found this to be true even using
graphite. With pinholes it's like telling the chlorine/oxygen - ATTACK HERE !
[Edited on 13-11-2005 by MadHatter]
From opening of NCIS New Orleans - It goes a BOOM ! BOOM ! BOOM ! MUHAHAHAHAHAHAHA !
|
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
Madhatter, when you were using your graphite substrate lead dioxide anodes (GSLD), where did you make your electrical connection, to the graphite or
to the PbO2 layer itself?
As I understand it, the problem with pinholes in a conventional GSLD anode is that the substrate will eventually disintegrate, thereby shutting off
power to the PbO2 layer. But if you're not depending on the substrate to be an electrical conductor, then I don't see how pinholes would be
a problem. Maybe I'm missing something obvious here and if so I apologize.
|
|
|
BromicAcid
International Hazard
Posts: 3245
Registered: 13-7-2003
Location: Wisconsin
Member Is Offline
Mood: Rock n' Roll
|
|
This usually isn't my style but I haven't gone through all of the posts on PbO<sub>2</sub> and therefore this may already be
posted somewhere or be on the FTP. Never the less, here is a link to a review that I found on the lead dioxide electrode, lots and lots of
information, it's a pdf, 2.7 megs or so, 25 pages, however only a few are specificaly on making the electrodes, many are on their properties and
uses:
http://www.destructve.com/sciencemadness/cr60280a003%5B1%5D....
|
|
|
MadHatter
International Hazard
Posts: 1339
Registered: 9-7-2004
Location: Maine
Member Is Offline
Mood: Enjoying retirement
|
|
Lead Dioxide
Bromic, Thanks for the link ! I downloaded and pushed a copy to my FTP under
the "CHEMISTRY - INORGANIC" folder.
From opening of NCIS New Orleans - It goes a BOOM ! BOOM ! BOOM ! MUHAHAHAHAHAHAHA !
|
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
Hmmm...unless I've misunderstood, that article apparently claims that you can't plate PbO2-beta from a lead acetate solution; only the
less-than-desireable alpha form.
Does anyone have access to the following references: "Journal of Applied Chemistry 16 (1966) p180. See also Metallurgical Transactions, vol 16B,
(1985) PP 489 - 496". It would be much appreciated.
|
|
|
SAM4CH
Hazard to Others
Posts: 162
Registered: 16-7-2004
Location: TA
Member Is Offline
Mood: PERFECT
|
|
installation lead dioxide anodes!
I made few anodes of lead dioxide on Gouging rods "20cm*0.8cm" the thickness of plating layer was "0.9-1.5mm" but I faced many mechanical and
electrical problems:
1. high temperature in DC electric connection with the head of anodes.
2. longitudinal cracking in some anodes after the first process and other in the 2nd and 3th...
3. strange brown layer on anodes.
Notes:
Current density was 15-18mA/cm2, and the temperature of solution was 45-50ºC, The cathode was 316 stainless steel, the electrolysis cell was closed
and there was an outlet for hose.
I added water "not slaty water" for increasing the level of solution which was evaporating during electrolysis peocess.
I used NaCl "techinical grade" and tape water.
I was test the time for electrolysis by using Methylene blue, and at the end of process I used AgNO3 as indicator for Cl- ions but there was not any
precipitate!!?
[Edited on 10-3-2006 by SAM4CH]
|
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
So, how much perchlorate did you get?
Also, I'm wondering, did you get a lot of chlorine gas from your cell during the chloride to chlorate phase?
I turned my pool chlorinator based cell on for the first time yesterday, but it made more chlorine than I expected, and even though I did it outside,
I had to turn it off until I can find a better spot for it.
|
|
|
SAM4CH
Hazard to Others
Posts: 162
Registered: 16-7-2004
Location: TA
Member Is Offline
Mood: PERFECT
|
|
I got about 250g sodium perchlorate from 170g NaCl
I used a buffer "NaF" So, it was not much of chlorine gas but at first 10minutes I noted it was so much.
|
|
|
| Pages:
1
..
3
4
5
6
7
..
47 |
![[*]](images/xpblue/default_icon.gif){kind=icon}