Obtain different sulfates from gypsum?
Perhaps the title confuses you, I will explain better:
I want to obtain copper sulphate, nickel sulphate and sulfo-aluminate (alum) of any metal, from
gypsum, since gypsum is calcium sulphate.
I would like to know if there is any more or less simple method (based on ion exchange or something similar) to obtain these sulfates.
The methode of manufacture that I search should not make use of non-commercia usuall substances (such as nitric acid, etc), since the objective of
making different sulfates from gypsum is to avoid the use of sulfuric acid or others substances hard to obtain/manufacture.
Electrolysis is accepted.
[Edited on 11-10-2017 by Alquimia]
|
|
gdflp
|
Thread Moved 11-10-2017 at 08:34 |
MrHomeScientist
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1806
Registered: 24-10-2010
Location: Flerovium
Member Is Offline
Mood: No Mood
|
|
I'd expect pulling the sulfate ion off CaSO<sub>4</sub> to be very difficult. It's extremely insoluble, and tough to get it back into
solution. I think CaCO<sub>3</sub> is even more insoluble, so you could try mixing finely powdered gypsum with a carbonate solution and
stirring for several hours. Some of the sulfate will go into solution over a long time. It'll be hard to tell, though, since the carbonate and sulfate
are both white powders. Test the liquid after a while by adding a drop of calcium chloride solution and seeing if anything precipitates.
|
|
Alquimia
Harmless
Posts: 13
Registered: 5-5-2017
Member Is Offline
Mood: No Mood
|
|
Carbon is more electropositive than sulfur (and calcium is more electropositive than nickel, copper, aluminium...).
I would say that the reaction will be extremelly slow (if endothermic) or non-spontaneus, since calcium will go where there is more electronegativity
(to sulphur).
Will it work really?
Could I use copper, nickel and aluminium chlorides instead of carbonates (it is easier of obtain for me)?
[Edited on 11-10-2017 by Alquimia]
|
|
MrHomeScientist
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1806
Registered: 24-10-2010
Location: Flerovium
Member Is Offline
Mood: No Mood
|
|
I think solubility will be the main driver here, not electronegativity. I haven't found exact values, but CaS is commonly cited as "slightly soluble"
which I infer is more soluble than CaSO<sub>4</sub>'s known very low solubility. Meaning nothing would happen when mixing gypsum with a
soluble sulfide. But if you have the reagents, feel free to experiment.
The point of using carbonates is that calcium carbonate is very insoluble, so the sulfate ion will go into solution.
CaSO<sub>4</sub>(s) + CO<sub>3</sub><sup>2-</sup> == CaCO<sub>3</sub>(s) +
SO<sub>4</sub><sup>2-</sup>
Chlorides won't have any effect. You would need a soluble carbonate salt, or a way to gas the solution with CO<sub>2</sub>. Either way,
it's going to take a while.
Depending on what exact sulfates you are trying to make, some can be found in common products. Root killer for septic tank systems, for example, is
copper sulfate.
|
|
violet sin
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1477
Registered: 2-9-2012
Location: Daydreaming of uraninite...
Member Is Offline
Mood: Good
|
|
gypsum + steel. I know from continued occurrence, drywall mud will turn green/black around the steel mixing spade overnight. When you pull it up to
break clumping before a mix in the morning, it's always colored. I had assumed it was iron sulfate and iron oxide. The spade/paddle get superficial
corrosion easily when pulled out and dried, indicating abrasive and chemical reactions attack freshly exposed iron. They are galvanized, so that
probably has an impact.
This probably helps very little, but it's a common sight to me, perhaps the green coloration is promising. It doesn't stay green if the mud dries.
Wonder what copper powder would do overnight in some? Would it be leachable? After boiling with Epsom salt? Pretty low tec but that just means easy
to check.
|
|
j_sum1
Administrator
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 6256
Registered: 4-10-2014
Location: Unmoved
Member Is Offline
Mood: Organised
|
|
There are easier sulfate sources than gypsym.
Epsom salt is available everywhere.
Copper sulfate is not too hard to come by - root killer or pottery supplies.
Manganese sulfate is an (unusual) otc item in the fertiliser aisle of my hardware store.
You can also make it by reaction of sulfur dioxide with battery paste. SO2 from burning sulfur.
Any of these would be a better start point.
|
|
ave369
Eastern European Lady of Mad Science
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 596
Registered: 8-7-2015
Location: No Location
Member Is Offline
Mood: No Mood
|
|
Boiling gypsum with sodium carbonate totally works, though you have to boil it for a long time, preferably under reflux. However, car battery acid is
a much more convenient source of the sulfate ion, and it is available in any car parts shop. It is 36% sulfuric acid.
[Edited on 12-10-2017 by ave369]
Smells like ammonia....
|
|
MrHomeScientist
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1806
Registered: 24-10-2010
Location: Flerovium
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by violet sin ![](images/xpblue/lastpost.gif) | gypsum + steel. I know from continued occurrence, drywall mud will turn green/black around the steel mixing spade overnight. When you pull it up to
break clumping before a mix in the morning, it's always colored. I had assumed it was iron sulfate and iron oxide. The spade/paddle get superficial
corrosion easily when pulled out and dried, indicating abrasive and chemical reactions attack freshly exposed iron. They are galvanized, so that
probably has an impact. |
I'd hypothesize that's just the iron rusting due to the moisture in the mud. To know for sure, of course, you'd have to test the colored substance for
sulfates.
|
|
violet sin
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1477
Registered: 2-9-2012
Location: Daydreaming of uraninite...
Member Is Offline
Mood: Good
|
|
Challenge accepted.
|
|
NEMO-Chemistry
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1559
Registered: 29-5-2016
Location: UK
Member Is Offline
Mood: No Mood
|
|
Sorry for being stupid, but what is drywall mud?
|
|
unionised
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 5109
Registered: 1-11-2003
Location: UK
Member Is Offline
Mood: No Mood
|
|
If you reflux gypsum in a solution of ammonium carbonate (you will need a good condenser) you will convert at least some of it to ammonium sulphate
and calcium carbonate.
If you filter off the calcium salts and then dry down the solution the excess ammonium carbonate will sublime and you will get ammonium sulphate.
If you heat that with iron oxide you should get ammonia and iron sulphate.
This is vastly more trouble than it is worth, since iron sulphate can be obtained as a moss killer.
|
|
violet sin
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1477
Registered: 2-9-2012
Location: Daydreaming of uraninite...
Member Is Offline
Mood: Good
|
|
Mud used in the construction field for seamwork on drywall. Aka, gypsum mud for use on gypsum board. The panels come 4' x 8' and are taped together
on the joints with the mud.
It is corrosive, abrasive and not much fun. Now, when I say corrosive, I mean it will rust metals at least superficially. Dust left after sanding
will settle on clean copper pipes causing a patina when it absorbs moisture from the air. It will cause rust spots on exposed nailheads, brackets,
non-stainless steel. The nails we use are galvanized, or phosphated as well as oiled usually. When a nail is sunk to depth with a hammer, the
resulting scuff through that coating will rust.
Point is we use a lot of stainless and aluminum tools. There is more than gypsum in the mud and board, so it's not a strictly fair comparison to the
accessible mineral. My idea was to use snack sized sandwich bags to test small amounts of copper scrap and metal bits from the bottom of our tub of
screws. Maybe a piece of standard steel.
I'm fairly certain there is some free sulfate in the mix, and that more is involved in this corrosion from the bulk material. I have access to
calcium chloride, to check for sulfate. Figure mud plus water mixed and decanted after settling will show a cloudy salute if the chloride is dropped
in forming basically gypsum. Frankly, that seems like a waste of time but I'll try it. Not like the rest of this group here has the materials just
sitting in the truck outside.
I'm not gonna race to get this done, busy guy. But I will throw a touch of time at it and report back with any observations. Remember I work~ 200mi
from home so my equipment isn't just in the other room. Only have what my curiosity demands I bring with me... On the off chance of science few chems and some electronics stuff.
|
|
vmelkon
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 669
Registered: 25-11-2011
Location: Canada
Member Is Offline
Mood: autoerotic asphyxiation
|
|
I don't suppose you have an easy way of reaching high temperatures?
CaSO4 + SiO2 → CaSiO3 + SO3
That probably requires over 1000 °C.
Another one:
https://chemiday.com/en/reaction/3-1-0-3980
"Calcium sulfate react with carbon monoxide to produce calcium sulfide and carbon dioxide. This reaction takes place at a temperature of 600-800°C."
and probably this would work as well at high temp:
CaSO4 + 2 C → CaS + 2 CO2
Signature ==== Is this my youtube page? https://www.youtube.com/watch?v=tA5PYtul5aU
We must attach the electrodes of knowledge to the nipples of ignorance and give a few good jolts.
Yes my evolutionary friends. We are all homos here.
|
|