Elecric arc colors of CaO + charcoal ?
Last weekend I made CaC2 with my DC welder using 120 amps by arcing crushed charcoal with CaO powder. The enclosure is YTONG cell concrete as I don't
have proper MgO refractory.
Most of the time the color is bright pink / magenta (03:30 in video below) but sometimes green (2:05).
Pink I can understand (calcium) but green ? No borax, barium, zinc or copper salts (which color flames green) were in the furnace. And the copper
tubes which hold the carbon rods were not immersed inside the furnace, otherwise it would melt. Close to the arc the temperature is over 2000 C.
Here a clip of the arc furnace inside my fumehood.
http://www.metallab.net/jwplayer/video.php?f=/clips/CaC2%20m...
|
|
phlogiston
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1377
Registered: 26-4-2008
Location: Neon Thorium Erbium Lanthanum Neodymium Sulphur
Member Is Offline
Mood: pyrophoric
|
|
Was it a virgin furnace, or is it possible that residue from previous experiments were present?
-----
"If a rocket goes up, who cares where it comes down, that's not my concern said Wernher von Braun" - Tom Lehrer
|
|
metalresearcher
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 737
Registered: 7-9-2010
Member Is Offline
Mood: Reactive
|
|
I have done previous experiments, but with the same chemicals, i.e. CaO and charcoal.
|
|
chloric1
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1090
Registered: 8-10-2003
Location: GroupVII of the periodic table
Member Is Offline
Mood: Stoichiometrically Balanced
|
|
Overall a success
This has been the most successful home brew carbide video I have seen yet. I bet you are so excited. You should next try calcium phosphide.
FYI. I have an Ebook copy of Moissons "The Electric Furnace". I find it is interesting that carbon can displace phosphide and sulfide with prolonged
heating. It's because calcium carbide is more thermodynamically stable. So you could use gypsum in a pinch. Would take quite a awhile though.
Maybe need more current?
Fellow molecular manipulator
|
|
NedsHead
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 409
Registered: 9-12-2014
Location: South Australia
Member Is Offline
Mood: No Mood
|
|
Hi metalresearcher,
your success making Calcium Carbide was the reason I gave it a go myself and I've noted a few things: the green glow is necessary and appears to
indicates there are enough amps for the reaction, (I'm curious why its green as well) but too many amps will destroy the product so adjust the amps
until the green glow first appears, for my DC welder it's 110A.
Next, keep the reaction as short as possible, 4 minutes is far too long and will destroy the end product, try 60-90 seconds, draw the arc around the
crucible to react as much of the carbon and CaO as possible (I use Calcium Hydroxide), hold the electrode in one spot until the carbon and caO
sublimate and then move the arc to a new spot and react.
This method yields me some very good calcium carbide https://youtu.be/IjQ_q8hg6ic
|
|
metalresearcher
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 737
Registered: 7-9-2010
Member Is Offline
Mood: Reactive
|
|
BTW, will tungsten rod electrodes not work better (i.e. less wear) ? They are available for a reasonable price on ebay.
|
|
phlogiston
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1377
Registered: 26-4-2008
Location: Neon Thorium Erbium Lanthanum Neodymium Sulphur
Member Is Offline
Mood: pyrophoric
|
|
What was the source of the graphite electrodes?
If you used gouging rods (gutselectroden in Dutch), they are typically plated with copper when you buy them. If you used those: did you strip their
copper layer off before use, and (if so), how?
-----
"If a rocket goes up, who cares where it comes down, that's not my concern said Wernher von Braun" - Tom Lehrer
|
|
m1tanker78
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 685
Registered: 5-1-2011
Member Is Offline
Mood: No Mood
|
|
The green emission is probably copper plating bath residue trapped within the graphite. Even if you peel the copper sheathing off the electrodes
without tearing it, there will be some copper salt(s) adhered beneath the surface.
Tungsten electrodes will work only in an inert atmosphere and at relatively low current with some form of heat sinking (or sweeping argon over them).
Carbon is hard to beat in an arc furnace. Unprotected/overheated tungsten will oxidize very quickly and aside from burning up, will contaminate your
product.
A robust resistive electric furnace can be made using some thin gouging rods and some high temp masonry. Have you considered making such a furnace?
Seems like your cement insulates fairly well. Might be worth a shot.
Chemical CURIOSITY KILLED THE CATalyst.
|
|
metalresearcher
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 737
Registered: 7-9-2010
Member Is Offline
Mood: Reactive
|
|
Quote: Originally posted by phlogiston ![](images/xpblue/lastpost.gif) | What was the source of the graphite electrodes?
If you used gouging rods (gutselectroden in Dutch), they are typically plated with copper when you buy them. If you used those: did you strip their
copper layer off before use, and (if so), how? |