why not use tin as the substrate
Excuse me if this is obvious, but why go through the trouble of precoating titanium with SnO2 or similar compounds when it would be much
simpler to use a tin substrate directly?
I was thinking of simply taking a tin sheet and bake it with a heat gun to generate the oxide layer. It will be very thin compared to applying
multiple layers of thermally decomposed SnCl2 or SnCl4, but does the SnO2 thickness matter after you coat it with a
much thicker layer of PbO2?
|
|
|
UncleJoe1985
Hazard to Self
Posts: 88
Registered: 30-9-2008
Location: Sunnyvale, CA
Member Is Offline
Mood: No Mood
|
|
crap, I hit post new topic instead of reply.
Moderator, please move this to this thread:
http://www.sciencemadness.org/talk/viewthread.php?tid=2465&a...
|
|
|
hyfalcon
International Hazard
Posts: 1003
Registered: 29-3-2012
Member Is Offline
Mood: No Mood
|
|
Until you show the effort and read the available material that's available on this site, you will find that these questions have already been covered.
You need to read this LARGE post that's a sticky, then ask your questions.
http://www.sciencemadness.org/talk/viewthread.php?tid=5050
|
|
|
UncleJoe1985
Hazard to Self
Posts: 88
Registered: 30-9-2008
Location: Sunnyvale, CA
Member Is Offline
Mood: No Mood
|
|
I can't find it. Asking someone to read through 40 pages of unstructured information isn't reasonable. Someone should put a summary page at the
beginning or have sub threads.
|
|
|
hyfalcon
International Hazard
Posts: 1003
Registered: 29-3-2012
Member Is Offline
Mood: No Mood
|
|
If not willing to mine for the knowledge, then worthiness to posses it is suspect.
|
|
|
phlogiston
International Hazard
Posts: 1379
Registered: 26-4-2008
Location: Neon Thorium Erbium Lanthanum Neodymium Sulphur
Member Is Offline
Mood: pyrophoric
|
|
It will safe you time in the long run.
In the time it takes to actually test your tin substrate idea you could have read the entire 40 pages and found out exactly why it will not work, and
a lot more.
-----
"If a rocket goes up, who cares where it comes down, that's not my concern said Wernher von Braun" - Tom Lehrer |
|
|
morganbw
National Hazard
Posts: 561
Registered: 23-11-2014
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by UncleJoe1985  | | I can't find it. Asking someone to read through 40 pages of unstructured information isn't reasonable. Someone should put a summary page at the
beginning or have sub threads. |
I hear you sir. I suffered the same thoughts and a gentleman, sir Aga, suggested I might perhaps do as you suggested with the summary page.
It is what it is until you/me/someone else, has the energy/time/desire, to compact and make it more to the point.
In reality, this forum, has a wealth of info (mixed with some garbage) you have to read and see if your question has been answered.
Key to my post is that there is a WEALTH of info on the pages of this forum. You have to do a little mining to get some of it.
|
|
|
j_sum1
Administrator
Posts: 6334
Registered: 4-10-2014
Location: At home
Member Is Online
Mood: Most of the ducks are in a row
|
|
| Quote: Originally posted by morganbw | | Quote: Originally posted by UncleJoe1985 | | I can't find it. Asking someone to read through 40 pages of unstructured information isn't reasonable. Someone should put a summary page at the
beginning or have sub threads. |
I hear you sir. I suffered the same thoughts and a gentleman, sir Aga, suggested I might perhaps do as you suggested with the summary page.
It is what it is until you/me/someone else, has the energy/time/desire, to compact and make it more to the point.
In reality, this forum, has a wealth of info (mixed with some garbage) you have to read and see if your question has been answered.
Key to my post is that there is a WEALTH of info on the pages of this forum. You have to do a little mining to get some of it.
|
Let me add that that is part of the appeal of this board. As you read through some of these threads (maybe
just a small chunk at a time) you come across information and processes that you would never have thought of to search for.
Today's gem was CsCl3. I would never have guessed that existed. Now I know it is an interesting yellow colour. Whodathunkit?
|
|
|
phlogiston
International Hazard
Posts: 1379
Registered: 26-4-2008
Location: Neon Thorium Erbium Lanthanum Neodymium Sulphur
Member Is Offline
Mood: pyrophoric
|
|
By now, you would have also found the website by SM member Dann which is a great, information-dense resource.
You could have easily found this yourself, but never mind:
It used to be at http://oxidizing.110mb.com/, but there were some issues with hosting. You should be able to find its new location in a thread here somewhere.
Otherwise, you could use the wayback machine http://web.archive.org/web/20121202185409/http://oxidizing.1...
Edit: it is currently here: http://oxidizing.typhoonguitars.com/index.html
[Edited on 28-4-2015 by phlogiston]
-----
"If a rocket goes up, who cares where it comes down, that's not my concern said Wernher von Braun" - Tom Lehrer |
|
|
![[*]](images/xpblue/default_icon.gif){kind=icon}