Best type of magnet for a stirrer/hotplate?!
Investing in a mag. stirrer hotplate thats fully functioning besides the fact the magnet inside was lost. I'm going to try to repair it by purchasing
a new magnet to bind to it, but the problem I have is finding the right magnet. I can't figure out what kind of magnet most stirrer/hotplates use.
Sorry for the novel, thanks.
|
|
thesmug
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 370
Registered: 17-1-2014
Location: Chicago, Il (USA)
Member Is Offline
Mood: No Mood
|
|
I think a regular neodymium magnet would work. You can look online for instructions on making your own stirrers. They will tell you which kind to use.
|
|
bismuthate
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 803
Registered: 28-9-2013
Location: the island of stability
Member Is Offline
Mood: self reacting
|
|
Neodymium is to strong I wouldn't recomend it. You should order a teflon coated stir bar online.
|
|
gdflp
Super Moderator
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1320
Registered: 14-2-2014
Location: NY, USA
Member Is Offline
Mood: Staring at code
|
|
Neodymium magnets will definitely not work I believe due to their magnetism being greatly reduced at higher temperature http://en.wikipedia.org/wiki/Neodymium_magnet . I remember a thread on here somewhere discussing this.
EDIT : Ah it's samarium cobalt magnets, though they are quite pricey.
[Edited on 1-4-2014 by gdflp]
|
|
copperastic
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 158
Registered: 15-3-2014
Location: In your basement
Member Is Offline
Mood: Good
|
|
Guys neodymium magnets can only operate at low temperatures so it might not be the best choice. Also if anyone has a stir/hotplate they are willing to
sell i will buy it. My one takes 3 hours to get to 100 degrees c and the max is 110 degrees c and if you run it for a hour you start smelling burning
rubber (low amounts).
|
|
Zephyr
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 341
Registered: 30-8-2013
Location: Seattle, WA
Member Is Offline
|
|
The magnet inside my Nuova Thermolyne hotplate/stirrer is about 3 inches long and is located directly under the heating rods, the magnet is made made
of a samarium cobalt alloy.
Over all I am very happy with this hotplate. I got it for $120 on eBay last year and the only problem with it is that the heating surface is a bit
corroded. I have never had any mechanical problems with it and it can reach 100oC in 7 minutes.
I highly recommend searching eBay for a new hotplate or just a new magnet.
What is your price range for the magnet?
|
|
copperastic
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 158
Registered: 15-3-2014
Location: In your basement
Member Is Offline
Mood: Good
|
|
sorry i didnt see you post gdflp.
|
|
copperastic
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 158
Registered: 15-3-2014
Location: In your basement
Member Is Offline
Mood: Good
|
|
pink hippo could you post a picture of it because its the same brand as mine (Thermolyne).
|
|
thesmug
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 370
Registered: 17-1-2014
Location: Chicago, Il (USA)
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by gdflp ![](images/xpblue/lastpost.gif) | Neodymium magnets will definitely not work I believe due to their magnetism being greatly reduced at higher temperature http://en.wikipedia.org/wiki/Neodymium_magnet . I remember a thread on here somewhere discussing this.
EDIT : Ah it's samarium cobalt magnets, though they are quite pricey.
[Edited on 1-4-2014 by gdflp] |
I never knew that! Sorry about my suggestion.
|
|
Steam
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 238
Registered: 25-3-2014
Location: Minnesota
Member Is Offline
Mood: Triple Point
|
|
You could possibly try cutting open a larger stir bar for it's magnet?
If I were you though I would just invest in a new hotplate, although I know they are kinda pricey. Maybe shop around on ebay and labx to see if you
can get yourself a deal!
DISCLAIMER: The information in this post is provided for general informational purposes only and may not reflect the current law in your jurisdiction.
No information contained in this post should be construed as legal advice from the individual author, nor is it intended to be a substitute for legal
counsel on any subject matter. No reader of this post should act or refrain from acting on the basis of any information included in, or accessible
through, this post without seeking the appropriate legal or other professional advice on the particular facts and circumstances at issue from a lawyer
licensed in the recipient’s state, country or other appropriate licensing jurisdiction.
|
|
BobD1001
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 182
Registered: 29-3-2013
Member Is Offline
Mood: No Mood
|
|
I have been using a neodymium magnet sourced from an old hard drive for my home-built PID controlled magnetic stirrer & hotplate. I have taken it
up to 400C with no ill effects to the magnet. Having said that, the magnet sits on a large aluminum heat-sink which I machined on my lathe, to help
dissipate heat, so if the heat is left to build up in the magnet as could be the case for you, it may not work. It also has about an 3/16" air gap
between itself and the base of the hotplate.
Heres a video of mine, it shows the heat-sink and magnet configuration, and may be of some help to you.
|
|
MrHomeScientist
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1806
Registered: 24-10-2010
Location: Flerovium
Member Is Offline
Mood: No Mood
|
|
The Curie temperature of neodymium magnets is listed as 310 oC on the low end. As long as your hot plate doesn't get too close to that I'd
think there wouldn't be any problems. Approaching the Curie temperature too closely would likely weaken the magnet over time, but if you're just
trying to boil water (say) then you should be good to go. Having a heat sink like BobD1001 mentioned is a great idea too.
|
|
Nasalguad
Harmless
Posts: 7
Registered: 15-12-2013
Member Is Offline
Mood: nice
|
|
Found a SmCo magnet for pretty cheap, the problem I see it posing is the division of the poles, not on either end but vertical. Would this completely
differ its use? http://www.magnet4sale.com/smco-magnets-2x1-2x1-2-samarium-c...
|
|
Chemosynthesis
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1071
Registered: 26-9-2013
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by BobD1001 ![](images/xpblue/lastpost.gif) | I have been using a neodymium magnet sourced from an old hard drive for my home-built PID controlled magnetic stirrer & hotplate. I have taken it
up to 400C with no ill effects to the magnet. Having said that, the magnet sits on a large aluminum heat-sink which I machined on my lathe, to help
dissipate heat, so if the heat is left to build up in the magnet as could be the case for you, it may not work. It also has about an 3/16" air gap
between itself and the base of the hotplate.
Heres a video of mine, it shows the heat-sink and magnet configuration, and may be of some help to you. |
Wow, that looks like a really fun project. I might try for that later this summer just for kicks.
|
|
gdflp
Super Moderator
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1320
Registered: 14-2-2014
Location: NY, USA
Member Is Offline
Mood: Staring at code
|
|
Yes, stir bars are basically small magnets with a pole at each end. The magnet when it is spinning must have the poles spinning at opposite
horizontal ends aka, the plane connecting the poles must be parallel to the surface of the hot plate.
|
|
Zephyr
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 341
Registered: 30-8-2013
Location: Seattle, WA
Member Is Offline
|
|
Here are some pictures of my Nuova hotplate;
![](https://sites.google.com/site/g1rafcultchemistrypictures/pis/Goodhotplate1.png)
Here is the inside from the bottom;
![](https://sites.google.com/site/g1rafcultchemistrypictures/pis/Goodhotplate2.png)
And lastly, the best view that I could get of the magnet. I was mistaken in my previous post, the heating element on top of the stir magnet. I could
not take it off further without straining the wires.
|
|
Chemosynthesis
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1071
Registered: 26-9-2013
Member Is Offline
Mood: No Mood
|
|
Wow, thanks, Pinkhippo11. Those are excellent pictures. It's interesting compare/contrast designs.
|
|
WeaponsRx
Harmless
Posts: 35
Registered: 29-12-2014
Member Is Offline
Mood: No Mood
|
|
Hell yea I just converted a Nuova hot plate I got off ebay like almost new condition for $32 into a awesome stirring hot plate using your stirring
ones wiring schematics hahaha they are the same just your terminals were all used mine were waiting to be! thanks for the pics!
|
|
WeaponsRx
Harmless
Posts: 35
Registered: 29-12-2014
Member Is Offline
Mood: No Mood
|
|
Alright so I'm having an issue here, I converted my Nuova hot plate into a stirring one like I mentioned above, but the issue im facing is simply
finding a magnet that's strong enough to grab through the actual heating element. The magnets im using are 3/4"x3/4" and about 74lbs holding power
each. My stir bar doesn't quite spin yet but the magnets are just under the aluminum plate that is between the heating element and the magnets. How
large or what kind of strength magnets do you guys think will actually do the job? Everything came out so perfect, besides the most important part I
guess Huh hahaha it's not grabing a hold of my bar. I have plenty of room to fit larger magnets as I am already raising the magnets up to where they
are. I'll snap some pics and show anyone who's interested
|
|
WeaponsRx
Harmless
Posts: 35
Registered: 29-12-2014
Member Is Offline
Mood: No Mood
|
|
Btw it's the exact same as Pinkhippo's. Only if he could just tell me how large those are Id be good to go haha.
|
|
DJF90
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 2266
Registered: 15-12-2007
Location: At the bench
Member Is Offline
Mood: No Mood
|
|
You've got a north and a south pole facing the stirbar, right?
|
|
Dr.Bob
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 2690
Registered: 26-1-2011
Location: USA - NC
Member Is Offline
Mood: No Mood
|
|
I thought you needed the east and west face going towards the stirbar, or is that only in the southern hemisphere? :-)
Sorry, it's been a snowy week here.
|
|
WeaponsRx
Harmless
Posts: 35
Registered: 29-12-2014
Member Is Offline
Mood: No Mood
|
|
Yea when the plate is removed the magnets are very very strong, both magnets attract each side of my stir bar... Thats how I simply obvioiusly know
which side to mount the magnets by testing prior to mounting of course
|
|
WeaponsRx
Harmless
Posts: 35
Registered: 29-12-2014
Member Is Offline
Mood: No Mood
|
|
but I noticed that the magnets I have dont really begin to attract my stir bar until they are about an inch away, or significantly should I say...
otherwise the stir bar just stays magnetized to the surface of the hot plate
|
|
WeaponsRx
Harmless
Posts: 35
Registered: 29-12-2014
Member Is Offline
Mood: No Mood
|
|
wonder if my magnets are to close to one another? theres about 1/4" in between them both...
|
|