Jerry Bennett
Harmless
Posts: 5
Registered: 5-1-2015
Member Is Offline
Mood: No Mood
|
|
Interested in alloys via thermite.
Hello. New to the forum.
I was wondering if there are any members who have dabbled with alloying metals with a thermite powered furnace? That is my interest. It has been a
while, but would like to try again. Have a few alloys I would like to try and make. Maybe exchange notes. Thanks, Jerry
Edit to say, I am not sure which forum I should use for this topic. I hope this is the one.
[Edited on 5-1-2015 by Jerry Bennett]
|
|
|
Bert
Super Administrator
Posts: 2821
Registered: 12-3-2004
Member Is Offline
Mood: " I think we are all going to die. I think that love is an illusion. We are flawed, my darling".
|
|
What alloys do you want to make?
There are some interesting effects to be had by using combinations of metal oxides (and other adjuncts) for thermite mixtures, one such is the "pyronol torch" composition of Iron oxide, Nickel, Aluminum and powdered PTFE.
Rapopart’s Rules for critical commentary:
1. Attempt to re-express your target’s position so clearly, vividly and fairly that your target says: “Thanks, I wish I’d thought of putting it
that way.”
2. List any points of agreement (especially if they are not matters of general or widespread agreement).
3. Mention anything you have learned from your target.
4. Only then are you permitted to say so much as a word of rebuttal or criticism.
Anatol Rapoport was a Russian-born American mathematical psychologist (1911-2007).
|
|
|
Jerry Bennett
Harmless
Posts: 5
Registered: 5-1-2015
Member Is Offline
Mood: No Mood
|
|
Thanks for that. 
For your entertainment, here are a few vids showing my progression using a thermite furnace.
https://www.youtube.com/watch?v=3_Q_IcBhHTA
https://www.youtube.com/watch?v=aVV5U14ju5A
https://www.youtube.com/watch?v=9JbIeTxaY6s
The second one, got me a patent. Well, a provisional patent. 
EDIT: Here is a sketch of the final furnace design. I left out one, VERY important item though. You must insulate the thermite reaction crucible from
the charcoal fire below. If you heat the reaction crucible too hot, it can react all at once. The least you will get is an awful sunburn. I use a
layer of insa wool.
[Edited on 6-1-2015 by Jerry Bennett]
[Edited on 6-1-2015 by Jerry Bennett]
|
|
|
Bert
Super Administrator
Posts: 2821
Registered: 12-3-2004
Member Is Offline
Mood: " I think we are all going to die. I think that love is an illusion. We are flawed, my darling".
|
|
Well, GODAMN. We're having some fun now...
Could you provide some background on any engineering parameters calling for the class of alloys involved, along with your hypothesis leading to these
experiment- Site policy is to provide such background information on processes and reactions proposed for discussion (outside of "beginnings", at any
rate).
http://www.sciencemadness.org/madscifaq.html#2.1_Board_topic...
Are you aware of the "exotic thermites & analogues" sticky in the energetic materials sub forum? And would you like this thread merged with that
one.
https://www.sciencemadness.org/whisper/viewthread.php?tid=10...
Rapopart’s Rules for critical commentary:
1. Attempt to re-express your target’s position so clearly, vividly and fairly that your target says: “Thanks, I wish I’d thought of putting it
that way.”
2. List any points of agreement (especially if they are not matters of general or widespread agreement).
3. Mention anything you have learned from your target.
4. Only then are you permitted to say so much as a word of rebuttal or criticism.
Anatol Rapoport was a Russian-born American mathematical psychologist (1911-2007).
|
|
|
Jerry Bennett
Harmless
Posts: 5
Registered: 5-1-2015
Member Is Offline
Mood: No Mood
|
|
Sure thing. Merging with the proper forum sounds fine.
I am no professional. Just a hobbyist. My intentions are making exotic alloys with iron thermite. I have had a small bit of success, as I made an
iron-rhenium-niobium nickle alloy back in 07. I call it "Rhenaissance steel". A play on spelling due to the rhenium.
More of a metallurgist, than a chemist. Some one called me a comic book metallurgist once, as an insult. I rolled with that. 
I think I can alloy very dissimilar metals and/or semi metals with the thermite system. I have a hunch that the highly excited ions and electrons in
the violent environment of thermite, may cause them to create more of a covalent bond than a classic metallic bond.
I make my own refractory through much trial and error. Safety is paramount. Nothing like watching, (and feeling), a 12# thermite charge to scare
common sense in a guy.
|
|
|
Mesa
Hazard to Others
Posts: 264
Registered: 2-7-2013
Member Is Offline
Mood: No Mood
|
|
I remember seeing that 3rd video early last year. Did you ever get it, or any other projects done using your awesome home-made equiptment assayed?
I get the feeling it'd be insanely difficult to get the ratio of metals to within a decent accuracy for most anything more than 2 different metals due
to variability of temp during the burns.
That being said, I have no experience with thermite alloys, and only minimal experience with binary thermites themselves.
|
|
|
franklyn
International Hazard
Posts: 3026
Registered: 30-5-2006
Location: Da Big Apple
Member Is Offline
Mood: No Mood
|
|
http://www.sciencemadness.org/talk/viewthread.php?tid=17625&...
|
|
|
Jerry Bennett
Harmless
Posts: 5
Registered: 5-1-2015
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by Mesa  | I remember seeing that 3rd video early last year. Did you ever get it, or any other projects done using your awesome home-made equiptment assayed?
I get the feeling it'd be insanely difficult to get the ratio of metals to within a decent accuracy for most anything more than 2 different metals due
to variability of temp during the burns.
That being said, I have no experience with thermite alloys, and only minimal experience with binary thermites themselves. |
It's actually fairly easy to get proper ratios of desired alloys. If you look at my furnace design, at the bottom above the catch crucible, there is
an "alloying chamber". It contains whatever alloys you wish. It also keeps them from reacting to the thermite. It is separated from the thermite mix
with a simple melt door. Also a melt door at the bottom of the alloying chamber.
I did get the last few ingots tested, both with spectro and SEM. They came out quite close to what I wanted to make.
|
|
|
Jerry Bennett
Harmless
Posts: 5
Registered: 5-1-2015
Member Is Offline
Mood: No Mood
|
|
Yo Bert. Would you kindly move this to the proper place. I have something in mind I would like to try. Reactive stuff. Ordered chaos, you know. Only
stuff the theoretical Physicists and mad bombers know. Thanks in advance.
|
|
|
Texium
|
Thread Moved
22-11-2023 at 19:08 |
chloric1
International Hazard
Posts: 1146
Registered: 8-10-2003
Location: GroupVII of the periodic table
Member Is Offline
Mood: Stoichiometrically Balanced
|
|
I like yo suggest making master alloys. These are super concentrated feedstocks meant to be added to melted metal to make a special alloy and
controlling how much alloying element you’re adding. A perfect example would be adding ferrosilicon(95%silicon) to molten copper to make silicon
bronze. Only 3% silicon and trace of iron needed to do this. Other master alloys could be ferrochrome, ferrovanadium, ferrotitanium etc etc.
Fellow molecular manipulator
|
|
|
chornedsnorkack
National Hazard
Posts: 564
Registered: 16-2-2012
Member Is Offline
Mood: No Mood
|
|
For binary alloys, how about
https://himikatus.ru/art/phase-diagr1/AcB-AlSr.php
Al is conveniently near the start of Al-phabet, so the binary systems including Al are together, not scattered under the earlier element. Check the
link on the right for Al-Tl and beyond. Note that while the frames are in Russian Cyrillic, the discussions of individual systems are English.
|
|
|
knowledgevschaos
Harmless
Posts: 41
Registered: 9-8-2023
Location: Sci-Hub and the hardware store
Member Is Offline
Mood: Hungry for information
|
|
A few people have gotten their iron oxide by rusting iron in an electrochemical cell, Nurdrange has a video on this. Could someone rust an already
alloyed metal like stainless steel in this way to get the right mix of oxides for a thermite reaction that generates the alloy again?
Might be a waste of time but it sounds like an interesting idea.
|
|
|
chornedsnorkack
National Hazard
Posts: 564
Registered: 16-2-2012
Member Is Offline
Mood: No Mood
|
|
Now I am wondering how thermite can ever work in the first place...
https://himikatus.ru/art/phase-diagr1/Al-Fe.php
Looks like Al readily alloys with Fe.
Why does thermite produce Fe, not Fe-Al alloys?
|
|
|
Fulmen
International Hazard
Posts: 1725
Registered: 24-9-2005
Member Is Offline
Mood: Bored
|
|
Because the Al is oxidized to Al2O3 while the iron oxide is reduced to base metal.
We're not banging rocks together here. We know how to put a man back together.
|
|
|
chornedsnorkack
National Hazard
Posts: 564
Registered: 16-2-2012
Member Is Offline
Mood: No Mood
|
|
Does it mean that thermite must always contain correct stoichiometric amount of Al? Any excess of Al, and unreacted Al alloys with Fe. Any shortage of
Al, and iron oxide is reduced only to FeO, not Fe?
|
|
|
EF2000
Hazard to Others
Posts: 153
Registered: 10-5-2023
Location: The Steppes
Member Is Offline
Mood: Taste testing the Tonka fuel
|
|
| Quote: Originally posted by chornedsnorkack |
Does it mean that thermite must always contain correct stoichiometric amount of Al? Any excess of Al, and unreacted Al alloys with Fe. Any shortage of
Al, and iron oxide is reduced only to FeO, not Fe? |
Absolutely not.
When there's not enough Al, some Fe2O3 remains unreacted. When there's excess Al, it mostly burns off in the air, producing the same Al2O3 slag as the
main reaction. Maybe some of Al gets into molten iron (like 0.1% or so). I don't see how it can interfere with the reaction. Millions of experiments
across the world (mostly conducted by railway workers) prove that it doesn't interfere a bit.
Wroom wroom
"The practice of pouring yourself alcohol from a rocket fuel tank is to be strongly condemned encouraged"
-R-1 User's Guide
|
|
|
![[*]](images/xpblue/default_icon.gif){kind=icon}