symboom
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1143
Registered: 11-11-2010
Location: Wrongplanet
Member Is Offline
Mood: Doing science while it is still legal since 2010
|
|
sodium chlorate production questions
so i have a chlorate cell platinum titanium anode why do i get chlorates at 5 volt 20 amp but at 36 volt 36 amp power source
i only get hydrogen and oxygen.both solutions are hot and concentrated
also my platinum anode electrode got partly melted under water and the melted part is black on the platinum what formed from it melting when the two
electrodes accidentally touched
|
|
woelen
Super Administrator
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 7991
Registered: 20-8-2005
Location: Netherlands
Member Is Offline
Mood: interested
|
|
Stupid you ![:D](./images/smilies/biggrin.gif)
Higher voltage only adds more heat and destruction of electrodes! Do not use more than 5 (maybe 6) volts. All excess voltage is converted to heat and
nothing more. If you want higher currents, then place electrodes closer to each other, use even higher concentration, or use parallel cells.
Increasing voltage is not the way to go!
Btw, please search the forums for more information. On sciencemadness there are tons of posts about chlorate production and many of these will be very
helpful.
This may also be interesting: http://www.oxidizing.110mb.com/chlorate/chlorate.html
|
|
symboom
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1143
Registered: 11-11-2010
Location: Wrongplanet
Member Is Offline
Mood: Doing science while it is still legal since 2010
|
|
an interesting discovery
well it was not all bad the black part of my platinum anode when it melted figured out it is platinum oxide and it seems to make the chlorate in a
shorter amount of time at 5v and if i use it as the cathode i can electroplate platinum on what ever i use as a anode
|
|
pjig
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 155
Registered: 25-5-2010
Member Is Offline
Mood: always learning
|
|
"or use parallel cells. "
Could you elaborate on this?
I have two power sources and was considering running two cells independent of each-other. But what you describe sounds more energy efficient, and I'd
like to know more.
Are you are describing one power source in parallel to 2 cells? .... forgive me for the misunderstanding if so.
[Edited on 30-3-2011 by pjig]
|
|
symboom
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1143
Registered: 11-11-2010
Location: Wrongplanet
Member Is Offline
Mood: Doing science while it is still legal since 2010
|
|
parallel cells
what he means parallel cells if you have a 12 volt you take two wire leads from the negative and positive side and connected to two cells. both cells
will have around 6 volt or less depending on factors that allow it. simultaneously creating (per)chlorate in both containers. but ive read that
battery chargers are not good to use because they fluctuate in wattage which is good for charging batteries bad for electrodes though
|
|
m1tanker78
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 685
Registered: 5-1-2011
Member Is Offline
Mood: No Mood
|
|
Battery chargers have high ripple which is perfectly fine for lead-acid batteries by not so good for circuits that are sensitive to it. If you can get
your hands on some beefy capacitors, you can reduce the ripple at the output even at higher currents.
As far as series and parallel....
The electrochemical cell is essentially a resistor. Series resistors add up their resistance. Parallel divide. If you have a 12v source you should put
the 2 cells in series. If you have a 5 or 6v source but want to run at a higher current, put the 2 cells in parallel.
You can also combine series and parallel resistances to match your needs.
Tom
|
|
roamingnome
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 363
Registered: 9-9-2006
Member Is Offline
Mood: No Mood
|
|
quote by symboom
platinum oxide and it seems to make the chlorate in a shorter amount of time at 5v
i cannot speak to the potential chemistry happening at the helmholtz layer, maybe the oxide lowers the saddle points of the free energy needed to
add oxygen atoms to the Chlorine
|
|
symboom
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1143
Registered: 11-11-2010
Location: Wrongplanet
Member Is Offline
Mood: Doing science while it is still legal since 2010
|
|
very useful book
useful book on perchlorates http://ia600301.us.archive.org/23/items/pwechloratesthei0017...
|
|
woelen
Super Administrator
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 7991
Registered: 20-8-2005
Location: Netherlands
Member Is Offline
Mood: interested
|
|
Quote: Originally posted by symboom ![](images/xpblue/lastpost.gif) | what he means parallel cells if you have a 12 volt you take two wire leads from the negative and positive side and connected to two cells. both cells
will have around 6 volt or less depending on factors that allow it. simultaneously creating (per)chlorate in both containers. but ive read that
battery chargers are not good to use because they fluctuate in wattage which is good for charging batteries bad for electrodes though
| No, I did not mean this. What you describe is a series connection of cells.
With parallel cells I mean using one powerful 5 ... 6 V power supply, which drives multiple cells, each cell connected to the plus and minus of the
power supply. In this way you can make more (per)chlorate per munit of time if your anodes and cathodes are not capable of handling the big current on
their own.
[Edited on 31-3-11 by woelen]
|
|
symboom
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1143
Registered: 11-11-2010
Location: Wrongplanet
Member Is Offline
Mood: Doing science while it is still legal since 2010
|
|
your right i am mistaken
|
|
grndpndr
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 508
Registered: 9-7-2006
Member Is Offline
Mood: No Mood
|
|
Can the battery charger be used to keep the battery volts/amps high while using the battery itself to power the cell?Avoiding fluctuations and
interruptions in the battery charger circuitry?
Im about to start up my own cell using a computer power supply/2 gallon HDPE bucket?Poor boy so treated graphite gouging rods and SS cathode along
with altered computer supply unit that was altered by a friend for trade material he was interested in.
But as I recall somewhere it was suggested the battery charger be used in conjunction with a battery(automotive of course)And the battery itself be
used to power the cell.![:o](./images/smilies/shocked.gif)
Ive read as much as I can lay my hands on..and absorb! Concerning electrolytic production of chlorates but i still have concerns with storing
possibly a few kilos of sodium or K chlorate.Mainly Fire concerns but even explosions if somehow the chlorates contain dangerous impuritys copper
being a main concern. I had planned on using rock salt to produce sodium chlorate then metathesis the Na chlorate to whatever might be needed for use
in flares,tracer material etc.
Lastly anyone whos using graphite anodes are you also using K dichromate to help in protecting your anode or is the toxicity problematic versus the
benefit?
[Edited on 5-4-2011 by grndpndr]
|
|
pjig
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 155
Registered: 25-5-2010
Member Is Offline
Mood: always learning
|
|
Quote: Originally posted by woelen ![](images/xpblue/lastpost.gif) | Quote: Originally posted by symboom ![](images/xpblue/lastpost.gif) | what he means parallel cells if you have a 12 volt you take two wire leads from the negative and positive side and connected to two cells. both cells
will have around 6 volt or less depending on factors that allow it. simultaneously creating (per)chlorate in both containers. but ive read that
battery chargers are not good to use because they fluctuate in wattage which is good for charging batteries bad for electrodes though
| No, I did not mean this. What you describe is a series connection of cells.
With parallel cells I mean using one powerful 5 ... 6 V power supply, which drives multiple cells, each cell connected to the plus and minus of the
power supply. In this way you can make more (per)chlorate per munit of time if your anodes and cathodes are not capable of handling the big current on
their own.
[Edited on 31-3-11 by woelen] |
Ya thats what I was thinking you where implying.. Would a computer power supply be able to take that kind of abuse ? I have 2 that run 200-230W And
was considering running 2 independent cells instead of one that was in parallel, but if the power sources can handle it I will give it a go.
|
|
woelen
Super Administrator
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 7991
Registered: 20-8-2005
Location: Netherlands
Member Is Offline
Mood: interested
|
|
Yes, a computer power supply can take that load as long as the total current remains well below the maximum rated current. The maximum rated current
is specified for each of the different voltage rails and usually there also is a grand maximum over the entire power supply, either in terms of total
current, or in terms of total supplied power.
Mordern power supplies can deliver at least 10 A of current from the 5V rail, but there are supplies which go as far as 30 A. Check the data, printed
on the label, attached to the side of the power supply.
|
|
pjig
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 155
Registered: 25-5-2010
Member Is Offline
Mood: always learning
|
|
I believe that mine is producing 15A to the cell, my tester is giving me trouble, but the last reading was 14.75A.. I have had excessive wear on the
anode, and I know that the kc1 levels are very high. That leaves me to believe that the graphite anode and graphite cathode are either too close (3")
and or the amperage is to high. Both rods are treated with linseed oil, to reduce wear, but after 12 days I have lost 1/3 of my anode ...I have not
maintained the ph with acid.
I switched the polarity and am hoping to finish the run w/o having to do a rod swap.
Any suggestions ?
|
|
symboom
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1143
Registered: 11-11-2010
Location: Wrongplanet
Member Is Offline
Mood: Doing science while it is still legal since 2010
|
|
industrial power supply
ive gone the way of computer supplies as they do not provide not much amperage they take a long time to produce any reasonable amount of perchlorate
in a small container in 6 hours i get a bit of an amount at 20A 5 volt Industrial Switching Power Supply which i like the device has no fan so much
quieter and more efficient in being able to adjust the amperage defiantly worth the investment.
|
|
White Yeti
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 816
Registered: 20-7-2011
Location: Asperger's spectrum
Member Is Offline
Mood: delocalized
|
|
If you're running 20A through a chlorate cell, YOU'RE CRAZY!
Normally you should have some sort of control over the current that flows through the electrodes. The ideal current that should be flowing through
your electrodes should be limited to about 90mA/cm2. In that case, your anode could take a current of 20A if it had a surface area of 222cm2, or about
a quarter the size of a mouse pad (if you count both sides). Needless to say that your anode would be outrageously expensive. Keep in mind that even
platinum isn't indestructible in a chlorate cell. Interestingly enough, platinum has a high electrical resistivity, passing dozens of amps through it
would cause it to generate heat and melt. This is the kind of experiment that you have to watch over for several days, and limit the voltage and
current that flows through it. Practically, you can run a chlorate cell on only 3 volts. Considering the fact that you are probably also using a small
platinum electrode, you shouldn't be using much more than 1A.
|
|
Nitro-esteban
Harmless
Posts: 39
Registered: 10-4-2013
Location: Fifth dimension
Member Is Offline
Mood: inert
|
|
The electrodes I am using are titanium coated with ruthenium and iridium oxide, I run my cell at 20A and 10V with very good results. I have tested
graphite from zinc-carbon cells but they seem to erode quite quickly. How can I treat it to reduce erosion?
|
|
AndersHoveland
Hazard to Other Members, due to repeated speculation and posting of untested highly dangerous procedures!
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1986
Registered: 2-3-2011
Member Is Offline
Mood: No Mood
|
|
Just to state the obvious, if you pass chlorine gas into an alkaline solution it will form hypochlorite and chloride. A gentle boil for a few minutes
will disproportionate the hypochlorite into chlorate.
|
|
ElectroWin
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 224
Registered: 5-3-2011
Member Is Offline
Mood: No Mood
|
|
the chemistry is highly dependent on the current density at the electrode surface.
you must measure the anode surface area that is in contact with the electrolyte,
and use the recommended amount of amperes per square metre.
if current density is too low or too high, you wont make the product you want.
high current densities also degrade anode materials faster.
|
|
Pulverulescent
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 793
Registered: 31-1-2008
Member Is Offline
Mood: Torn between two monikers ─ "hissingnoise" and the present incarnation!
|
|
Quote: | I have tested graphite from zinc-carbon cells but they seem to erode quite quickly. |
Battery cathodes are compressed carbon and are unsuitable as anodes!
Some gouging rods are good quality graphite and stand up well especially if soaked overnight in light linseed oil prior to use . . .
Graphite is easily identifiable by its greyish, rather than black, colour!
"I know not with what weapons World War III will be fought, but World War IV will be fought with sticks and stones"
A Einstein
|
|
Fantasma4500
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1681
Registered: 12-12-2012
Location: Dysrope (aka europe)
Member Is Offline
Mood: dangerously practical
|
|
i have seen stated that nanofibre cloth, wrapped around a graphite anode or cathode should keep it from falling apart, i suppose this would need it to
be very well pressed around?
for this some normal organic wire or even plastic should do the job keeping it together
by logic this should work, the the bottom is sealed aswell, when the graphite starts to fall apart, it cannot fall away, and it will still act as
electrode, as it keeps the shape
as i have discovered magnetite, Fe3O4 to be found in beach sand (the black type of beach sand) it can easily be taken out by a magnet, this should be
done a few times to get a decently pure powder
i suppose same thing could be done with Fe3O4 and nanofibre cloth
keep in mind that there are nobody reporting of having tried this, yet..
can someone tell me why this wouldnt work? just seems too OP.. i mean.. a piece of cloth.. some graphite or magnetite powder and some salt water and a
week later add sugar to dry crystals and you got a secondary
there must be something making this impossible, there always is!
|
|