Beware eBay aluminum
5lb Aluminum Powder Flake SMOKE ALUM. (250 Mesh Approx)
Seller tacticalchemical
It's aluminum paste looking up la MSDS —
35% mineral spirits, which explains its odd odour.
The mineral spirits are hard to remove, tired acetone...
problem... due to its small particle size ... it has a v/ v/ high
surface area and absorbs acetone like a sponge. Leaving
it out in the sun for a few days might help, if I had any
sun - sun without strong winds.
It does not work in a thermite composition.
|
|
chief
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 630
Registered: 19-7-2007
Member Is Offline
Mood: No Mood
|
|
Easy aluminum-powder, east-german way:
==> Just stirr the melt when it cools down ..., gives granules of up to 1 mm size, but mostly smaller ...
==> burns at least with MnO2, slowly ... (didn't try any other oxide ...)
![:D](./images/smilies/biggrin.gif)
[Edited on 2-5-2010 by chief]
|
|
hissingnoise
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 3940
Registered: 26-12-2002
Member Is Offline
Mood: Pulverulescent!
|
|
Cigarette foil or any delicate alufoil can be ball-milled to a fine flake with lead media.
The thin paper backing will form small balls like cordite grains and these can be filtered out if required but leaving them in doesn't significantly
affect the performance. . .
|
|
chochu3
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 185
Registered: 21-10-2003
Location: South Side Tejas [Cloverland]
Member Is Offline
Mood: Inside looking out
|
|
ultrasonic some aluminum foil and gather your powdered grey aluminum.
\"Abiding in the midst of ignorance, thinking themselves wise and learned, fools go aimlessly hither and thither, like blind led by the blind.\" -
Katha Upanishad
|
|
grndpndr
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 508
Registered: 9-7-2006
Member Is Offline
Mood: No Mood
|
|
are we talking a reloading vibratory brass polisher using the lead balls/other material as media for a fine mesh AL powder?
Thell run forever would seem an obvious solution with the right media?I havent looked to see if thier ultrasonic,they do put a hell of a shine to
brass in short order w/polishing media.
[Edited on 3-5-2010 by grndpndr]
|
|
chief
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 630
Registered: 19-7-2007
Member Is Offline
Mood: No Mood
|
|
With melt-stirring the production of Al-powder is easily in the kg-range ...
|
|
The WiZard is In
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1617
Registered: 3-4-2010
Member Is Offline
Mood: No Mood
|
|
And now — Something completely different.
Preparation of fine aluminum powders by solution methods
Kelvin T. Higa et al
US Patent 5 885 321
Fine aluminum powders are prepared by decomposing alane-adducts
in organic solvents under an inert atmosphere to provide highly
uniform particles and believed particularly effective as fuels and
additives, in pyrotechnics, and in energetic materials. Effective
adduct species are trialkyl amines...
Inventors: Kelvin T. Higa, Curtes E. Johnson, Richard A. Hollins
Assignee: The United States of America as represented by the
Secretary of the Navy
For da how alulminium powder dobe made I recommend —
Aluminum Powders and Pastes
"The Tale of the Pig"
Reynolds Metals Company
1960
|
|
Picric-A
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 796
Registered: 1-5-2008
Location: England
Member Is Offline
Mood: Fuming
|
|
Please could somebody explain how this 'melt-stirring' method is done to aquire Al-powder in 'kg' quantities?
thanks
|
|
The WiZard is In
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1617
Registered: 3-4-2010
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by Picric-A ![](images/xpblue/lastpost.gif) |
Please could somebody explain how this 'melt-stirring' method is done to aquire Al-powder in 'kg' quantities?
thanks |
Just a WAG —
Google -> solid-assisted melt disintegration SAMD aluminum.
|
|
Nicodem
Super Moderator
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 4230
Registered: 28-12-2004
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by The WiZard is In ![](images/xpblue/lastpost.gif) |
It's aluminum paste looking up la MSDS —
35% mineral spirits, which explains its odd odour.
The mineral spirits are hard to remove, tired acetone...
|
Acetone does not dissolve much paraffin oil. Petroleum ether dissolves it efficiently. This is what is generally used to remove oil from oil coated
reactive materials (like from NaH/oil mixture).
|
|
Fleaker
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1252
Registered: 19-6-2005
Member Is Offline
Mood: nucleophilic
|
|
Aluminum metal has a "hot short" state right around a dull red heat, or just as it's cooling. It's very, very brittle at the point and literally
crushes like stale potato chips. I suppose you could get some mm sized granules which would be sufficient for further ballmilling.
Neither flask nor beaker.
"Kid, you don't even know just what you don't know. "
--The Dark Lord Sauron
|
|
FrankRizzo
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 203
Registered: 9-2-2004
Member Is Offline
Mood: No Mood
|
|
Thanks Wiz. ![:)](./images/smilies/smile.gif)
For those of you too lazy...
Attachment: Solid-assisted melt disintegration (SAMD), a novel technique for metal powder production.pdf (1.4MB) This file has been downloaded 672 times
[Edited on 5/3/2010 by FrankRizzo]
|
|
The WiZard is In
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1617
Registered: 3-4-2010
Member Is Offline
Mood: No Mood
|
|
I was going to suggest
http://www.justfuckinggoogleit.com/ [A legit URL]
|
|
chief
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 630
Registered: 19-7-2007
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by Picric-A ![](images/xpblue/lastpost.gif) |
Please could somebody explain how this 'melt-stirring' method is done to aquire Al-powder in 'kg' quantities?
thanks |
Well, I did it like this:
==> Had a melt (electric furnace)
==> stirred it with some more aluminum ...
The Al-Stirring-rod melted until the temp was down to the melting point ... (saving a lot of time by quickly cooling to the right temperature )
==> Then 10 or 15 more minutes of stirring
... gives Al-Powder ...
It works because the air oxidizes the Al-surface, and with the stirring air gets everywhere into the melt ... ; the oxide-layer isolates the droplets,
result is a fine powder ...
==========
Only it's _work_ to stirr the melt by hand, so on subsequent runs I used a drilling-engine with some iron-rod ... and threw Al-pieces into the melt
until it nearly was at 651 [Cels] ...
==========
When everything was a fine powder and the temp below the melting point I used to quickly get it out of the furnace, to avoid any sintering or whatever
...
==> ... that's when it sometiomes can ignite, at least the finer fractions ...
Generally a thing to be done outside, because of the vapors..., but it will work with a 10- or 50-kg melt as well ...
[Edited on 4-5-2010 by chief]
[Edited on 4-5-2010 by chief]
|
|
Picric-A
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 796
Registered: 1-5-2008
Location: England
Member Is Offline
Mood: Fuming
|
|
Surly the oxide coating will leave the powder relativly unreactive compared to Al powder that has been ground down, thus it will be useless for things
like thermite?
|
|
chief
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 630
Registered: 19-7-2007
Member Is Offline
Mood: No Mood
|
|
It works fine with MnO2 ...; didn't try anything else ...
|
|
Microtek
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 849
Registered: 23-9-2002
Member Is Offline
Mood: No Mood
|
|
If the Al powder is to be used for themite there is another way:
Use Al foil as is.
Determine how much Al is in one meter of foil, then roll out however much you require. Figure out how much oxide you need based on a suitable
stoichiometry, then sprinkle it onto the Al foil. Then roll the foil into a long "sausage" or tube while crimping or twisting it with your hands to
make sure the oxide stays where it is.
Stuff the "sausage" into a suitable container, but make sure there is room enough for a booster of traditional powder thermite, as this is quite
difficult to ignite.
I had this idea when I read somewhere that Al and Fe2O3 reacts in the liquid phase in the thermite reaction, which would imply that finely powdered
reagents only really promote ease of ignition and burn rate. I've tested it a number of times and it seems to work just fine.
Of course by this reasoning, you could also add big chunks of aluminum scrap as long as there was enough regular thermite to get it molten.
|
|
chief
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 630
Registered: 19-7-2007
Member Is Offline
Mood: No Mood
|
|
Al-foil: This works ! ![:D](./images/smilies/biggrin.gif)
... wrote a small but useful program to calculate the mass of MnO2 (Al-MnO2-thermite), to be compiled with a fortran-compiler:
Attachment: MnO2_Al_therm.F (652B) This file has been downloaded 590 times
|
|
peach
Bon Vivant
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1428
Registered: 14-11-2008
Member Is Offline
Mood: No Mood
|
|
You've Mc Owned the thread in one sentence, I hope you're proud! ![:)](./images/smilies/smile.gif)
Guess it doesn't produce it at a particularly high rate.
Ask the guys who sell materials for home brewing fireworks, they've got mountains of the stuff and in every form, grain size or mesh you'll ever want.
Here's one example I've been drooling over since I was about 13;
http://www.skylighter.com/
[Edited on 13-5-2010 by peach]
|
|