Forgability of chromium
I'm trying to forge a sputtering target out of chromium metal, I melt chromium powder into blobs and then hammer them on an anvil. The problem is they
don't seem to be forgeable at all, when I hit them reasonably hard they don't deform, when I hit them really hard they shatter. All of this is
happening at almost the melting point of chromium (I'm heating it with a TIG welding torch until it's just starting to melt).
Anyone know what's going on?
|
|
|
Fulmen
International Hazard
Posts: 1716
Registered: 24-9-2005
Member Is Offline
Mood: Bored
|
|
Nitrogen embrittlement perhaps? Or are you using an inert blanket?
https://en.wikipedia.org/wiki/Chromium#Passivation
We're not banging rocks together here. We know how to put a man back together.
|
|
|
DoctorOfPhilosophy
Hazard to Others
Posts: 130
Registered: 12-6-2012
Location: Ontario, Canada
Member Is Offline
Mood: enthralled
|
|
Looks like that might be it. I used argon for the initial melt but the metal dust was not compressed prior to melting. Also no protective gas was used
during forging, another pathway for N2 to enter.
Can I remove the nitrogen and reuse the chromium metal?
[Edited on 29-6-2016 by DoctorOfPhilosophy]
|
|
|
Fulmen
International Hazard
Posts: 1716
Registered: 24-9-2005
Member Is Offline
Mood: Bored
|
|
Could be. According to wiki chromium nitride decomposes at 1770C, so prolonged heating could release the nitrogen. Would probably take some time
though.
https://en.wikipedia.org/wiki/Chromium_nitride
We're not banging rocks together here. We know how to put a man back together.
|
|
|
Fleaker
International Hazard
Posts: 1252
Registered: 19-6-2005
Member Is Offline
Mood: nucleophilic
|
|
Chromium is brittle. All the sputtering targets I used to get in of pure Cr I beat up with a hammer before further pulverizing.
If you're going to make a sputtering target out of it, best to vacuum induction cast it and then EDM it to size.
Neither flask nor beaker.
"Kid, you don't even know just what you don't know. "
--The Dark Lord Sauron
|
|
|
DoctorOfPhilosophy
Hazard to Others
Posts: 130
Registered: 12-6-2012
Location: Ontario, Canada
Member Is Offline
Mood: enthralled
|
|
I already destroyed half the machine shop trying to shape chromium using conventional tools. I'm just going to grind it to the correct size using an
angle grinder and later a dremel to get the shape right.
|
|
|
Fleaker
International Hazard
Posts: 1252
Registered: 19-6-2005
Member Is Offline
Mood: nucleophilic
|
|
Beware the dust!
Neither flask nor beaker.
"Kid, you don't even know just what you don't know. "
--The Dark Lord Sauron
|
|
|
DoctorOfPhilosophy
Hazard to Others
Posts: 130
Registered: 12-6-2012
Location: Ontario, Canada
Member Is Offline
Mood: enthralled
|
|
Right, another chemist already warned me about that. In the end my project partner ordered a huge slab of chromium. It appears to have machining marks
on it, so I wonder what parameters they used to make that work.
|
|
|
Bezaleel
Hazard to Others
Posts: 444
Registered: 28-2-2009
Member Is Offline
Mood: transitional
|
|
I'm sorry if this is a silly question, but is this a general remark, or is chromium dust particularly harmful? I would guess it's just in the +0
charge state, so from that perspective no more harmful than other metal dust.
|
|
|
Fantasma4500
International Hazard
Posts: 1681
Registered: 12-12-2012
Location: Dysrope (aka europe)
Member Is Offline
Mood: dangerously practical
|
|
i think chromium hype derives from the nefarious chromium six (hexavalent) which is produced in smaller amounts from welding (tig-wig especially iirc)
although they have recently stepped down the toxicity opinion regarding hexavalent chromium, potential carcinogen is main concern i'd guess, so be
very careful with ethanol too, another carcinogen.
maybe look up some "how its made" videos of chromium or the like? there has to be videos around of it, electrodeposition onto metals that you can
easily dissolve with chemicals would be a way around getting violent with the chrome, although conc H2SO4 and CrO3 seems to be the way to electroplate
chromium, quite different from many other metals where you can oftenly bypass having the metal in its ionic form in the electrolyte from start
|
|
|
Fleaker
International Hazard
Posts: 1252
Registered: 19-6-2005
Member Is Offline
Mood: nucleophilic
|
|
Machining Cr probably gives mostly Cr2O3 fume but perhaps some higher chromium oxides can form.
Neither flask nor beaker.
"Kid, you don't even know just what you don't know. "
--The Dark Lord Sauron
|
|
|
Texium
|
Thread Moved
27-11-2023 at 10:45 |
![[*]](images/xpblue/default_icon.gif){kind=icon}