Mercury and chlorine gas at the age of 15 ...  hehe
Quote: Originally posted by XeonTheMGPony  |
the brine tank, Same bolt configuration, but the positive electrode was finely coiled SS welding wire that was 1.5 inches from the bottom of the tank.
|
As I understand it, you used SS welding wire as the anode where chlorine is generated. Did you find it to be resistant to chlorine? Maybe I could
replace the carbon electrode.
Thanks for sharing with us your findings.
|
|
|
XeonTheMGPony
International Hazard
Posts: 1640
Registered: 5-1-2016
Member Is Offline
Mood: No Mood
|
|
it held up well enough when I was running it, cant remember much more then that been so long.
and as for the stuff I was playing with at that age that was the safest! Advantages of growing up in remote heavy industry 
|
|
|
kt5000
Hazard to Others
Posts: 133
Registered: 27-3-2013
Location: Southwest US
Member Is Offline
Mood: Final exams
|
|
| Quote: Originally posted by MrHomeScientist | | I've done the "flower pot cell" before as an experiment to produce NaOH. It worked, albeit very slowly. The real problem I found is how to permanently
seal the hole in the bottom of the flower pot. Tape falls off and caulk quickly degrades in the basic environment! |
I tried the same thing last fall. My wife found a bisque clay shot glass at a craft store with no hole in the bottom, the type you'd paint and bake
in a kiln. It seemed to work well but the NaOH production was really, really slow.
|
|
|
Jstuyfzand
Hazard to Others
Posts: 166
Registered: 16-1-2016
Location: Netherlands
Member Is Offline
Mood: Learning, Sorta.
|
|
I was wondering you could just bubble the chlorine into the water, making HCl and HClO, and simultaneously expose the water to UV, I read somewhere
that the HclO then turns into Hcl and o2 or just leaves the solution as chlorine gas.(?)
|
|
|
Zandins
Harmless
Posts: 25
Registered: 18-6-2016
Member Is Offline
Mood: No Mood
|
|
My attempt at chlor-alkali process:v0.1
Greetings sciencemadness community,
For a while now, I have contemplated and tested various chloralkali setups, and seem to have found one that somewhat works.
The electrolytic cell is an empty ice-cream box with a total volume of 1.2 L. The cell is partitioned by an asbestos fiber diaphragm, held in place by
epoxy resin glue. I originaly tried filter paper, which proved vulnerable to the strongly alkaline conditions. Asbestos,however, works well.
The cathode component is 4 times larger that the anode compartment, to accomodate more NaOH. For the cathode, a stainless steel strip with a surface
area of 20 cm2 was used. The anode is a carbon rod taken from a battery. The anode corrodes in the acidid condictions, forming a paste of carbon
particles on the surfac3 of the anode compartment.
Power is provided by 3 parallel PSUs on the 12V rail. After running the electrolysis for 6 hours at around 6A, circa 1L of 1.1M NaOH solution has been
produced. This corresponds to 81.1% efficiency.
Once I get my gas-collection system running, I will start producing HCl by collecting the gases and exposing them to UVC.
Current problems with the setup:
1)Erosion of the graphite electrode. Here to stay until I get my PbO2 done;
2)Copper cable providing current to the anode is attacked by the Cl2 gas, producing CuCl2.
Would love to hear any thoughts, suvgestions, etc!
Zandins
[Edited on 2-7-2016 by Bert]
Please re-size your pictures to just large enough to show the details relevant to your post!!! You blew the margins, are you a mass nerderer or
something...
http://www.sciencemadness.org/talk/viewthread.php?tid=66853#...
[Edited on 2-7-2016 by Bert]
[Edited on 2-7-2016 by Bert]
|
|
|
Jstuyfzand
Hazard to Others
Posts: 166
Registered: 16-1-2016
Location: Netherlands
Member Is Offline
Mood: Learning, Sorta.
|
|
| Quote: Originally posted by Zandins | Greetings sciencemadness community,
For a while now, I have contemplated and tested various chloralkali setups, and seem to have found one that somewhat works.
The electrolytic cell is an empty ice-cream box with a total volume of 1.2 L. The cell is partitioned by an asbestos fiber diaphragm, held in place by
epoxy resin glue. I originaly tried filter paper, which proved vulnerable to the strongly alkaline conditions. Asbestos,however, works well.
The cathode component is 4 times larger that the anode compartment, to accomodate more NaOH. For the cathode, a stainless steel strip with a surface
area of 20 cm2 was used. The anode is a carbon rod taken from a battery. The anode corrodes in the acidid condictions, forming a paste of carbon
particles on the surfac3 of the anode compartment.
Power is provided by 3 parallel PSUs on the 12V rail. After running the electrolysis for 6 hours at around 6A, circa 1L of 1.1M NaOH solution has been
produced. This corresponds to 81.1% efficiency.
Once I get my gas-collection system running, I will start producing HCl by collecting the gases and exposing them to UVC.
Current problems with the setup:
1)Erosion of the graphite electrode. Here to stay until I get my PbO2 done;
2)Copper cable providing current to the anode is attacked by the Cl2 gas, producing CuCl2.
Would love to hear any thoughts, suvgestions, etc!
Zandins
[Edited on 2-7-2016 by Bert]
Please re-size your pictures to just large enough to show the details relevant to your post!!! You blew the margins, are you a mass nerderer or
something...
http://www.sciencemadness.org/talk/viewthread.php?tid=66853#...
[Edited on 2-7-2016 by Bert]
[Edited on 2-7-2016 by Bert] |
12V seems a bit high, have you tried 5V?
Corrosion should be less.
May I ask what route to PbO2 you are taking?
|
|
|
Zandins
Harmless
Posts: 25
Registered: 18-6-2016
Member Is Offline
Mood: No Mood
|
|
12V probably is overkill, although they were necessary to push any sizable current through the cell due to the small surface area of the carbon rod.
As for the PbO2, I plan to cast a lead plate and electroplate it with PbO2 in H2SO4 solution in-situ. There are varying accounts on the feasibility of
this method, so I intend to try it out before moving to more sophisticated approaches.
The general problem seems to be the flaking of the PbO2 layer in strongly corrosive conditions. However, if the coating would be grown thick enough to
prevent any of the substrate from being exposed, I conjecture it could hold, at least in a chlor-alkali cell(opposed to chlorate of perchlorate).
Meanwhile I am also looking into platinized titanium - if any were to be found at a reasonable price, all the aforementioned problems would be
eliminated.
|
|
|
Jstuyfzand
Hazard to Others
Posts: 166
Registered: 16-1-2016
Location: Netherlands
Member Is Offline
Mood: Learning, Sorta.
|
|
I saw something about graphite rods and anodes being corroded faster in basic environments, I guess chloralkali would be less harsh on the electrodes
since the anode bath stays neutral when you are using a separated cell.
|
|
|
hissingnoise
International Hazard
Posts: 3940
Registered: 26-12-2002
Member Is Offline
Mood: Pulverulescent!
|
|
| Quote: | | I saw something about graphite rods and anodes being corroded faster in basic environments |
A graphite cathode in a chlorate cell is quite unaffected by the high pH which arises in a working cell!
Acidity at the anode is damaging, obviously...
|
|
|
Fleaker
International Hazard
Posts: 1252
Registered: 19-6-2005
Member Is Offline
Mood: nucleophilic
|
|
Have you tried just plain ol' titanium for the anode of a chlorate cell?
Reason I ask is I have several hundred square foot worth of 16 gauge titanium CP2 sheet that I can easily shear up.
Neither flask nor beaker.
"Kid, you don't even know just what you don't know. "
--The Dark Lord Sauron
|
|
|
Jstuyfzand
Hazard to Others
Posts: 166
Registered: 16-1-2016
Location: Netherlands
Member Is Offline
Mood: Learning, Sorta.
|
|
| Quote: Originally posted by Fleaker | Have you tried just plain ol' titanium for the anode of a chlorate cell?
Reason I ask is I have several hundred square foot worth of 16 gauge titanium CP2 sheet that I can easily shear up. |
Titanium will passivate and no current will flow, wont work.
By the way, how are you all using these asbestos plates as diaphrams when that stuff is carcinogenic and prohibited?
|
|
|
Zandins
Harmless
Posts: 25
Registered: 18-6-2016
Member Is Offline
Mood: No Mood
|
|
Passivation
As far as I am aware, titanium passivates in anodic conditions as it is oxidised to TiO2,which is nonconductive. Therefore, it can only be used as a
cathode.
|
|
|
Texium
|