After etching the copper from some circuit boards with FeCl<sub>3</sub>, I decided to reduce the resulting copper(II) chloride with some
steel rods from some lever door handles (I have many to spare), as I've done previous times. The copper would precipitate as a powder or short
needles, but a few times it precipitated as sheets, with a sintered-like aspect and very fragile. One time however, the copper sheets were thick
enough to not crumble when dry. My last reduction I did a few days ago also yielded some copper sheets.
Does anyone have any idea why the copper would sometimes precipitate as sheets?
Could it be impurities? The electronics I etched also contained solder, and given they are old ones, they must have tin-lead.
|
|
Zombie
Forum Hillbilly
Posts: 1700
Registered: 13-1-2015
Location: Florida PanHandle
Member Is Offline
Mood: I just don't know...
|
|
I found this PDF on Spangolite. It's a copper sulfate sheet crystal...
http://www.minsocam.org/ammin/am78/am78_649.pdf
I didn't read thru the entire PDF but I believe it applies.
[Edited on 4-2-2015 by Zombie]
They tried to have me "put to sleep" so I came back to return the favor.
Zom.
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
He's talking copper (Cu(0)), not copper sulphate, Zomb.
|
|
Mabus
Wiki Master
Posts: 238
Registered: 3-11-2013
Member Is Offline
Mood: Energetic
|
|
I didn't have any copper sulfate, so I don't think that applies.
|
|
Hawkguy
Hazard to Others
Posts: 326
Registered: 10-10-2014
Location: British Columbia (Canada eh!)
Member Is Offline
Mood: Body is Ready
|
|
well shieeet thats crazy
|
|
Zombie
Forum Hillbilly
Posts: 1700
Registered: 13-1-2015
Location: Florida PanHandle
Member Is Offline
Mood: I just don't know...
|
|
Admittedly I have a limited understanding of this.
My thought in posting the PDF is perhaps there is something that can tie Mobus;s method into the the formation of these sheeting crystals.
Obviously there is some anomaly at play to " sometimes precipitate as sheets".
I'll catch up... No doubt.
They tried to have me "put to sleep" so I came back to return the favor.
Zom.
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
If the "steel rods from some lever door handles" are indeed flat surfaced then the copper will deposit on them as "sheets", which will eventually
flake off. This will happen if the rate of copper formation is slow (low reagent concentration, e.g.)
'Nothing to see here', as far as I'm concerned...
[Edited on 5-2-2015 by blogfast25]
|
|
Zombie
Forum Hillbilly
Posts: 1700
Registered: 13-1-2015
Location: Florida PanHandle
Member Is Offline
Mood: I just don't know...
|
|
Nice.
They tried to have me "put to sleep" so I came back to return the favor.
Zom.
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
Caption competition:
'The blueprint for a set of 'ear speakers' that connect straight through the wearer's head. Volume adjustment knobs can be seen.'
[Edited on 5-2-2015 by blogfast25]
|
|
maleic
Harmless
Posts: 20
Registered: 24-12-2014
Member Is Offline
Mood: No Mood
|
|
Maybe it is just dirty..... Okay, In fact, I don't know the answer
|
|
Zombie
Forum Hillbilly
Posts: 1700
Registered: 13-1-2015
Location: Florida PanHandle
Member Is Offline
Mood: I just don't know...
|
|
The whole time I was looking right at the square stock in the Picts. I assumed it was part of the crystal structure...
Should have used Captain Obvious, rather than Competitive.
Maybe it just compacted as per BlogFast.
They tried to have me "put to sleep" so I came back to return the favor.
Zom.
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
If you run this plating business in the right conditions, the copper simply sticks to the substrate. IIRW, electrolytic chroming is done on an
undercoat of copper.
[Edited on 6-2-2015 by blogfast25]
|
|
Dan Vizine
National Hazard
Posts: 628
Registered: 4-4-2014
Location: Tonawanda, New York
Member Is Offline
Mood: High Resistance
|
|
Many steel items are plated with various thin metals to improve durability. Is this pile of steel pieces unlike your usual reductant pieces.
Delamination of such a layer may be the cause.
"All Your Children Are Poor Unfortunate Victims of Lies You Believe, a Plague Upon Your Ignorance that Keeps the Youth from the Truth They
Deserve"...F. Zappa
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by Dan Vizine | Many steel items are plated with various thin metals to improve durability. Is this pile of steel pieces unlike your usual reductant pieces.
Delamination of such a layer may be the cause. |
And if these steel bars aren't too clean that is even more likely to occur. Bits of oil or grease easily ruin adhesion of the Cu coating to the steel.
|
|