veerenyadav
Harmless
Posts: 30
Registered: 1-3-2014
Member Is Offline
Mood: No Mood
|
|
Reduction of Fe(+3) in Fe(+2)
I have a solution which contain ferric oxalate and I want to reduced it to ferrous oxalate. I am doing it by photoreduction using sunlight .
Can anybody suggest cheap reducing agent ? But it must not contaminate the solution which I am going to recycle ? specially slats, etc.
Thanks
|
|
|
CHRIS25
National Hazard
Posts: 951
Registered: 6-4-2012
Location: Ireland
Member Is Offline
Mood: No Mood
|
|
As far as I am concerned setting the ferric oxalate under UV light is the most painless and quickest method. Don't use sunlight since most of the UV
is scattered. My cyanotypes would take up to 2 hours in this climate but less than 10 minutes under a UV. So that's the way to go. HOwever you would
need to place this , after the oxidation, in an inert an atmosphere as possible since the Iron 2 will turn back into iron 3 very quickly, if you don't
have anything inert then the best thing would simply be an air-tight container but "Filled" with the Iron 2 oxalate so as to limit volume of air
inside. By the way I have never done this, so look forward to your results.
[Edited on 18-12-2014 by CHRIS25]
‘Calcination… is such a Separation of Bodies by Fire, as makes ‘em easily reducible into Powder; and for that reason ‘tis call’d by some
Chymical Pulverization.’ (John Friend, Chymical Lectures London, 1712)
Right is right, even if everyone is against it, and wrong is wrong, even if everyone is for it. (William Penn 1644-1718)
The very nature of Random, Chance development precludes the existence of Order - strange that our organic and inorganic world is so well defined by
precision and law. (me)
|
|
|
unionised
International Hazard
Posts: 5126
Registered: 1-11-2003
Location: UK
Member Is Offline
Mood: No Mood
|
|
Have you considered using iron (metal) as the reducing agent?
Steel wool is cheap.
it's almost certainly worth a try unless someone here can explain why it wouldn't work.
|
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by unionised  | Have you considered using iron (metal) as the reducing agent?
Steel wool is cheap.
it's almost certainly worth a try unless someone here can explain why it wouldn't work.
|
It should work: I've used 2 Fe(III) + Fe === > 3 Fe(II) to make ferrofluid. You just filter off the excess steel wool.
Since as ferric oxalate is poorly soluble and the Fe<sup>3+</sup> concentration fairly small, it might take a while to complete. Heat
gently?
|
|
|
unionised
International Hazard
Posts: 5126
Registered: 1-11-2003
Location: UK
Member Is Offline
Mood: No Mood
|
|
Good point, given how low the solubilities are, sunlight might be quicker.
|
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
Didn't even know sunlight worked, TBH.
But ionic reactions in water are usually very fast, so even low concentration of Fe<sup>3+</sup> may not be a problem. Use lots of steel
wool, I guess.
|
|
|
veerenyadav
Harmless
Posts: 30
Registered: 1-3-2014
Member Is Offline
Mood: No Mood
|
|
thanks any experience about other conditions
thanks to all,
I think I should try steel wool but would anybody like to mention any think about other experimental conditions?
|
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
| Quote: Originally posted by veerenyadav |
thanks to all,
I think I should try steel wool but would anybody like to mention any think about other experimental conditions?
|
Use an excess of steel wool, warm to about 50 C. I think that should work.
|
|
|
![[*]](images/xpblue/default_icon.gif){kind=icon}