-OH resistant anode
I am trying to make Na- and KOH through the one-cell electrolysis of their carbonates (for Na, the bicarbonate). Is there an anode material that is
resistant/immune to carbon dioxide and alkali hydroxides?
Elements Collected:52/87
Latest Acquired: Cl
Next in Line: Nd
|
|
elementcollector1
International Hazard
Posts: 2684
Registered: 28-12-2011
Location: The Known Universe
Member Is Offline
Mood: Molten
|
|
Never mind, nickel appears to work. Does not have an amphoteric oxide, metal, or hydroxide. Excellent!
Elements Collected:52/87
Latest Acquired: Cl
Next in Line: Nd
|
|
RadioTrefoil
Harmless
Posts: 16
Registered: 11-7-2012
Location: New Zealand
Member Is Offline
Mood: Inert
|
|
Graphite's the way to go. Nickel will corrode over time.
MESITYL FREAKING OXIDE
|
|
plante1999
International Hazard
Posts: 1936
Registered: 27-12-2010
Member Is Offline
Mood: Mad as a hatter
|
|
platinum.
I never asked for this.
|
|
woelen
Super Administrator
Posts: 8004
Registered: 20-8-2005
Location: Netherlands
Member Is Offline
Mood: interested
|
|
Nickel is good enough if you are electrolysing hydroxide solutions. Even plain copper wire works great with solutions of NaOH and makes O2 at the
anode without the copper dissolving.
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
Carbon is attacked by strong alkali. Platinum is overkill.
|
|
plante1999
International Hazard
Posts: 1936
Registered: 27-12-2010
Member Is Offline
Mood: Mad as a hatter
|
|
If you don't want to overkill, iron can do the job, but it will add some impurity.
I never asked for this.
|
|
hyfalcon
International Hazard
Posts: 1003
Registered: 29-3-2012
Member Is Offline
Mood: No Mood
|
|
I've got some grade 330 stainless steel that I'm trying to figure out how best to use in a cell myself. With it's high nickel content this might be a
good experiment.
|
|
plante1999
International Hazard
Posts: 1936
Registered: 27-12-2010
Member Is Offline
Mood: Mad as a hatter
|
|
Never use SS steel as an anode in alkaline electrolyte, the chromium will leach out as chromate and the resultant nickel-iron alloy is like sponge and
will make flocculent hydroxide, all this happening pretty fast. I don't even explain in acid sol., SS is very unuseful as an anode.
I never asked for this.
|
|
kristofvagyok
National Hazard
Posts: 659
Registered: 6-4-2012
Location: Europe
Member Is Offline
Mood: No Mood
|
|
I have never tried it, but a friend suggested Ti anode, what would be pretty cheap and it is highly resistant.
Or use Hg?
I have a blog where I post my pictures from my work: http://labphoto.tumblr.com/
-Pictures from chemistry, check it out(:
"You can’t become a chemist and expect to live forever."
|
|
phlogiston
International Hazard
Posts: 1378
Registered: 26-4-2008
Location: Neon Thorium Erbium Lanthanum Neodymium Sulphur
Member Is Offline
Mood: pyrophoric
|
|
I think Ti will passivate. Stay away from Hg if you value your grey cells. Only resort to it if it is the only thing in the world that will do the
job. Use Nickel or Platinum.
-----
"If a rocket goes up, who cares where it comes down, that's not my concern said Wernher von Braun" - Tom Lehrer
|
|
vmelkon
National Hazard
Posts: 669
Registered: 25-11-2011
Location: Canada
Member Is Offline
Mood: autoerotic asphyxiation
|
|
A nice graphite rod from a D cell non alkaline battery is probably the cheapest solution.
You can try silicon if you want but the conductivity is very low.
As for Hg, I've always been curious about that one as an anode. I have only used it as a cathode.
|
|