Ti substrate ThO2 anode for perchlorate cell. Good idea?
This is a thought that I came up with at two in the morning, so sorry it if it's completely absurd. I was thinking that one might be able to use a
ThO2 anode in a perchlorate cell.
One could take a titanium electrode, coat it in Th(NO3)4, and thermally decompose it into ThO2. Now the question is, would the electrode be any good?
I'm thinking that they likely would, as ThO2 is quite chemically resistant, and would likely be resistant in a perchlorate cell. The other question
is as to whether or not they would actually make perchlorates. I have no clue how I would predict this ahead of time, so if someone could educate me
as to that, it'd be greatly appreciated.
Thanks!
edit - My greatest concern with this is small amounts of the ThO2 coming off the electrode and getting stuck in the perchlorate, as Th is radioactive.
[Edited on 16-1-2021 by itsallgoodjames]
Nuclear physics is neat. It's a shame it's so regulated...
Now that I think about it, that's probably a good thing. Still annoying though.
|
|
Fyndium
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1192
Registered: 12-7-2020
Location: Not in USA
Member Is Offline
|
|
First came in mind the TIG tungsten thorium alloy rods. They are being phased out, though, and are very small for electrolysis.
There will always be small contaminations of all that it put in contact with the solution. The amounts may be insignificant, in order of parts per
billion, or so, though, and anything that does not dissolve, is usually readily filtered out. For example carbon rods corrode, but I haven't found
filtering the solution an issue.
|
|
Jome
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 154
Registered: 10-6-2004
Location: Soutwest sweden
Member Is Offline
Mood: desiccated
|
|
Two questions need answers:
First and foremost, what is the conductivity of ThO2?
If you look at a pourbaix diagram of thorium, is there something ThO2 can be oxidized into without the pH being insanely high?
|
|
wg48temp9
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 774
Registered: 30-12-2018
Location: not so United Kingdom
Member Is Offline
|
|
Judging by the white colour of ThO2 in a bright light even at a red heat it has low conductivity. Its an insulator.
Confirmed by https://www.osti.gov/servlets/purl/4605090
I am wg48 but not on my usual pc hence the temp handle.
Thank goodness for Fleming and the fungi.
Old codger' lives matters, wear a mask and help save them.
Be aware of demagoguery, keep your frontal lobes fully engaged.
I don't know who invented mRNA vaccines but they should get a fancy medal and I hope they made a shed load of money from it.
|
|
itsallgoodjames
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 276
Registered: 31-8-2020
Location: America Lite
Member Is Offline
|
|
Oh, I didn't see that. I searched for it's electrical conductivity, but couldn't find anything. Thanks
Nuclear physics is neat. It's a shame it's so regulated...
Now that I think about it, that's probably a good thing. Still annoying though.
|
|