Iron

Iron,  ₂₆Fe

Two easily available iron sources, with very different surface areas: Steel wool and railroad spikes.
General properties
Name, symbol	Iron, Fe
Appearance	Metallic gray
Iron in the periodic table
↑ Fe ↓ Ru Manganese ← Iron → Cobalt
Atomic number	26
Standard atomic weight (Ar)	55.845(2)
Group, block	, d-block
Period	period 4
Electron configuration	[Ar] 3d6 4s2
per shell	2, 8, 14, 2
Physical properties
Metallic gray
Phase	Solid
Melting point	1811 K ​(1538 °C, ​​2800 °F)
Boiling point	3134 K ​(2862 °C, ​5182 °F)
Density near r.t.	7.874 g/cm3
when liquid, at	6.98 g/cm3
Heat of fusion	13.81 kJ/mol
Heat of	340 kJ/mol
Molar heat capacity	25.1 J/(mol·K)
pressure
Atomic properties
Oxidation states	−4, −2, −1, +1, +2, +3, +4, +5, +6, +7 ​(an amphoteric oxide)
Electronegativity	Pauling scale: 1.83
energies	1st: 762.5 kJ/mol 2nd: 1561.9 kJ/mol 3rd: 2957 kJ/mol
Atomic radius	empirical: 126 pm
Miscellanea
Crystal structure	​Bbody-centered cubic (bcc) a=286.65 pm
Crystal structure	​Face-centered cubic (fcc) Between 1185–1667 K
Speed of sound thin rod	5120 m/s (at ) (electrolytic)
Thermal expansion	11.8 µm/(m·K) (at 25 °C)
Thermal conductivity	80.4 W/(m·K)
Electrical resistivity	9.61·10-8 Ω·m (at 20 °C)
Curie point	1043 K
Magnetic ordering	Ferromagnetic
Young's modulus	211 GPa
Shear modulus	82 GPa
Bulk modulus	170 GPa
Poisson ratio	0.29
Mohs hardness	4
Vickers hardness	608 MPa
Brinell hardness	200–1180 MPa
CAS Registry Number	7439-89-6
History
Before 5000 BC

Iron (chemical symbol Fe) is element number 26 on the periodic table. It is one of the elements known since antiquity, and has long been prized for its strength and ability to form even stronger alloys, such as steel. In the lab, iron can be either a useful reagent or an annoying contaminant. Its coordination chemistry is not as extensive as that of some other transition metals, but several complexes are known.

Properties

Physical

Iron is a silvery gray metal. It has a melting point of 1538 degrees C. It is commonly known to be ferromagnetic, the word being partially derived from the Latin word for iron. It is known to exist in four allotropes, and it may exist in a fifth. Very pure single-crystal iron, used for research purposes, is far weaker structurally than aluminum metal.

Chemical

Iron forms compounds most commonly found in it's ferrous(II) and ferric(III) oxidation states, but it can exist in the (IV) and (VI) valence states as ferrates. Other oxidation states are possible present no interest to the amateur chemist.

Iron reacts with air in the presence of water to form Fe₂O₃, commonly known as rust. It also will form mixed valence compounds like magnetite (Fe₃O₄), that contain both ferrous and ferric state iron in their structure. Magnetite may be produced by ignition of steel wool. Iron reacts with the halogens to form its halide salts. It will also react with sulfur at elevated temperatures if finely divided to form iron sulfide (FeS). In solution, iron tends to form ferrous salts, but the addition of hydrogen peroxide (and often atmospheric oxygen) will promote the formation of ferric compounds.

Iron metal will react with diluted acids, such as hydrochloric acid, but passivates in contact with concentrated acids, such as nitric acid or phosphoric acid.

The ferrous state of iron is normally soluble in water and is resistant to oxidation in acidic solution. In basic solution, however, iron(II) oxide will precipitate and be oxidized by water to iron(III) oxide. Solid iron(II) sulfate may oxidize in air to form iron(III) oxide deposits.

The ferric state of iron is only soluble in acidic solutions and will quickly convert to hydrous iron(III) oxide if the acidity is reduced. This is a source of annoyance for most chemists. However, interesting color changes may occur due to complex formation. One example is iron(III) nitrate: it is lavender in the solid state, but dissolves to form a rust-colored solution, with the dominant iron species being [Fe(H₂O)₅OH]²⁺. A small amount of acid will turn this solution clear as the [Fe(H₂O)₅OH]²⁺ is converted to [Fe(H₂O)₆]³⁺. Ferric compounds, such as iron(III) chloride, are strongly Lewis acidic.

Iron(III) iodide is unstable with respect to disproportionation. When an iodide-containing solution is added to a solution containing ferric ion, iron(II) iodide and iron precipitate.

A relatively sensitive test for ferric iron is the addition of thiocyanates, which form a deep red complex. This can be used to make fake blood as a party trick.

Both oxidation states readily from complexes with water, cyanide, nitrous oxide (ferrous only) and oxalates (ferric only)[1]

Ferrates(VI) are compounds of iron in the +6 state. These are only stable in strongly basic solutions and will degrade after about a day. However, they can be produced at home by using bleach, and can be stabilized by precipitation with barium. Anhydrous ferrates are stable if they are pure; if impure, they quickly decompose even in an anhydrous state, unless the contaminant is a strong alkali, which, on the contrary, works as a stabilizer. Although ferrates are powerful oxidizers, they are mild and will not ignite organic materials.

Ferrates are salts of ferric acid H₂FeO₄, which is so unstable that it immediately decomposes on formation. The anhydride, FeO₃, is also so far impossible to isolate.

Availability

Due to the superior mechanical and chemical properties of steel, most items that contain iron are normally alloys. Some sources of steel wool however, use pure iron metal. Despite sounding like it contains less carbon than steel, "cast iron" contains at least twice as much carbon as high-carbon steel, making it less usable than steel as an iron source. Railroad spikes, cleaned with a file, can serve as bulk iron electrodes for producing solutions of soluble iron compounds, and are totally free. Occasionally pieces of discarded iron can be found near welded railway tracks, which are high purity iron. However, most pieces of iron tend to be lodged in slag, which should be removed.

Preparation

Pure iron can be prepared via the classical thermite reaction.

Fe₂O₃ + Al → Fe + Al₂O₃

High purity iron powder can be produced by reducing an iron salt with hydrogen. A more accessible way is via decomposition of iron(II) oxalate. This yields iron carbon dioxide, carbon monoxide, iron(III) oxide (if oxygen is present) and pyrophoric black iron.

Projects

• Making pyrophoric iron via ferrous oxalate
• Prussian blue
• Ferric-thiosulfate complexes 
• Thiocyanate complexes
• Making fake blood
• Making ferrates
• Making and using ferric chloride etchants
• Thermite
• Extracting iron from breakfast cereal or dirt
• Making a heating pack

Handling

Safety

Iron in the form of steel wool or powder is highly flammable. Caution must be taken when working with it near an open flame. Its oxides and halides will stain clothing.

Iron is a necessary trace element, found in nearly all living organisms. Iron-containing enzymes and proteins, often containing heme prosthetic groups, participate in many crucial biological oxidations and in transport. Iron is the metal ion in the haemoglobin organometallic complex.

Storage

Iron metal can be stored in open air, but will rust in moist or polluted air. Iron that was cleaned with an acid will quickly rust in air, unless protected. Iron powder can be pyrophoric and should be stored in closed bottles.

Disposal

Iron and iron compounds can be safely dumped in the environment, as they pose little toxicity. Iron halides however, will hydrolyze to release their respective acids and should be neutralized before disposal.

Gallery

Element

• 

  Tools made of steel, the most common form of iron encountered.

Compounds

• 

  Potassium Ferrioxalate - Made by SM user Hegi

• 

  Iron(II) oxalate

References

Relevant Sciencemadness threads

• How would I Extract Iron from Bog Iron
• Preperation of powdered Iron
• Reason why iron and acid smells bad.
• Iron Oxalate