"Liquid Armor"
Anyone know what they do to the Kevlar here? Or at least what the shear thickening fluid is composed of?
"Damn it George! I told you not to drop me!"
|
|
|
APO
National Hazard
Posts: 627
Registered: 28-12-2012
Location: China Lake
Member Is Offline
Mood: Refluxing
|
|
Is this: http://en.wikipedia.org/wiki/Shear_thickening#Silica_and_pol... it?
"Damn it George! I told you not to drop me!"
|
|
|
Prometheus23
Hazard to Self
Posts: 62
Registered: 6-6-2012
Member Is Offline
Mood: No Mood
|
|
The video actually tells you what it is made of at 3:10, just a third of the way into it.
You also seemed to have UTSFE and found the answer yourself just one minute later.
So I guess question answered?
|
|
|
violet sin
International Hazard
Posts: 1482
Registered: 2-9-2012
Location: Daydreaming of uraninite...
Member Is Offline
Mood: Good
|
|
interesting none the less. I wonder how well it would work on other fibers? with materials that cheap and available(quick ebay check) could be fun
to try. and a little more reading couldn't hurt.
google search came up with -EP 1633293 A1 (text from WO2004103231A1)-
http://www.google.com/patents/EP1633293A1?cl=en&dq=shear...
"[00026] The STF is the combination of the particles suspended in the solvent."
"[00027] The particles used can be made of various materials, such as, but not limited to, Si0 or other oxides, calcium carbonate, or polymers, such
as polystyrene or polymethylmethacrylate, or other polymers from emulsion polymerization. The particles can be stabilized in solution or dispersed by
charge, Brownian motion, adsorbed surfactants, and adsorbed or grafted polymers, polyelectrolytes, polyampholytes, or oligomers. Particle shapes
include spherical particles, elliptical particles, or disk-like or clay particles. The particles may be synthetic and/or naturally occurring minerals.
Also, the particles can be either monodisperse, bidisperse, or polydisperse in size and shape."
good reading. pants out of that stuff would be great for deer hunting. wading through fallen trees and brush can be a bit pokey.
|
|
|
Pyro
International Hazard
Posts: 1305
Registered: 6-4-2012
Location: Gent, Belgium
Member Is Offline
Mood: No Mood
|
|
its the same principle as corn starch and water. you guts ever tried this? take a handful of corn starch and add a little water, keep adding until
it's a thick paste that will flow off your hand. then roll it between them until it's a ball. it will fell hard until you stop rolling it!
all above information is intellectual property of Pyro.  |
|
|
violet sin
International Hazard
Posts: 1482
Registered: 2-9-2012
Location: Daydreaming of uraninite...
Member Is Offline
Mood: Good
|
|
Ya as a kid we use to make ziploc bags with a little cornstarch mix, simple but ammusing. in the reading I did(cited above), they mentioned different
thread types layered or woven, to provide more ballistics protection. Something about nylon being good b/c of a rougher surface. They also mentioned
surface treatements to roughen kevlar. Think it made for more resistive mats rather than just a shell that deforms but won't puncture. Which still
hurts.
So seems really easy to get some scrap nylon etc. from a thrift store and put it in a ziplock bag for a few tests. I'm sure there are FAR better
methods! So many cheap materials. Now I am not saying any one is going to make a BP vest. But the effect should be easy to see.
Edited-spelling-
[Edited on 24-3-2013 by violet sin]
|
|
|