Identifying lead compositions?
Is there way to identify lead compositions other than using a hardness tester? I want to know what’s in my lead. Curious to see if there’s a way
to tell how much lead is in the “unknown” contents of my lead ingots.
|
|
CharlieA
National Hazard
Posts: 646
Registered: 11-8-2015
Location: Missouri, USA
Member Is Offline
Mood: No Mood
|
|
Maybe you could search for the quantitative analysis of solid lead/lead alloy samples. Unless you have access to high-powered analytical
instrumentation, you might try looking in older quantitative inorganic analysis texts.
Also, I would guess that there are standard tests recommended by the ASTM
(American Standards for Testing Materials?).
If you suspect certain metals are present in your specimen, perhaps you could identify them with spot tests. I think the more specific the spot test
is, the more complicated the necessary reagent is (usually an organic compound).
Just a few ideas off of the top of my (bald) head.
|
|
j_sum1
Administrator
Posts: 6252
Registered: 4-10-2014
Location: Unmoved
Member Is Offline
Mood: Organised
|
|
There is an awful lot that will dissolve in lead. And all will have the effect of making the alloy harder even at low concentrations. For this
reason, a physical test is not going to tell you much.
If you are doing a chemical test and do not have modern analytical gear, (who does?) then the first step is to narrow down the possibilities of what
you believe might be in there. Then look for qualitative tests for those elements. Good luck. This is not likely to be easy.
For starters, lead ores generally have a lot of other metals from neighbouring elements: tin, antimony, bismuth in particular. Unless these are
deliberately removed in a refining process, they will still be present to some extent. But there is a truckload of other possibilities as well. What
is the source of your lead?
|
|
Darth-Vang
Harmless
Posts: 22
Registered: 28-6-2019
Member Is Offline
|
|
Quote: Originally posted by j_sum1 | There is an awful lot that will dissolve in lead. And all will have the effect of making the alloy harder even at low concentrations. For this
reason, a physical test is not going to tell you much.
If you are doing a chemical test and do not have modern analytical gear, (who does?) then the first step is to narrow down the possibilities of what
you believe might be in there. Then look for qualitative tests for those elements. Good luck. This is not likely to be easy.
For starters, lead ores generally have a lot of other metals from neighbouring elements: tin, antimony, bismuth in particular. Unless these are
deliberately removed in a refining process, they will still be present to some extent. But there is a truckload of other possibilities as well. What
is the source of your lead? | Lead is supposedly pure lead, possibly has tin or antimony in there, but I
swage bullets with it with no problem.(swaging dies can only use pure lead or close to it)
|
|