Curious glass electrical conduction effect
I was testing an old power triode with a12kV electronic neon sign transformer to see if the vacuum was good by connecting the 12kV between anode and
cathode.
Unfortunately the 12kV was flashing across in the air between my connections so I put a short piece of glass tube of the cathode connection to
insulate it. The glass tube was very thin from fluorescent tube with the phosphor removed. The 12kV punctured the glass producing a yellow arc ether
side of the puncture. Then on one side of the glass the arc moved away from the puncture leaving two separated arcs on either side of the glass with
nothing visible between them as if the glass was conductive. Ater few experiments it was apparent that there was a hot conductive filament between the
separated arc points in the glass. But surprisingly the filament was not hot enough to produce a detectable glow.
After the arc was removed and the glass had cooled down the path of the filament was just visible as fine (<1mm) line. Usually the glass cracked or
shattered as it cooled down.
Yes I know that molten glass is conductive but I would have assumed it would have to be glowing at least red hot to be sufficiently conductive.
Perhaps it was red hot but being so thin the intensity was so low that it was not visible.
I will set up an experiment to take pics of the effect.
Sorry I made a mistake. The electronic neon sign transformer is specified as 10kV, 30mA. That usually means the voltage with no load and the short
circuit current.
[Edited on 10/13/2021 by wg48temp9]
I am wg48 but not on my usual pc hence the temp handle.
Thank goodness for Fleming and the fungi.
Old codger' lives matters, wear a mask and help save them.
Be aware of demagoguery, keep your frontal lobes fully engaged.
I don't know who invented mRNA vaccines but they should get a fancy medal and I hope they made a shed load of money from it.
|
|
Vomaturge
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 285
Registered: 21-1-2018
Member Is Offline
Mood: thermodynamic
|
|
I don't think it has a well defined melting point. This video shows conductivity (ion mobility?) before it actually gets hot enough to be a free flowing liquid.
I've laid a glass bottle in a wood fire (not an especially vigorous one) and it slowly deformed into a "puddle," all while acting totally hard and
solid when poked with a stick.
Again, it doesn't have to be a great conductor, just enough to pass <100mA with 12 kV across the glass.
I now have a YouTube channel. So far just electronics and basic High Voltage experimentation, but I'll hopefully have some chemistry videos soon.
|
|
Morgan
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1675
Registered: 28-12-2010
Member Is Offline
Mood: No Mood
|
|
The dielectric strength of soda lime glass is sort of on the cusp of insulating at a mm thickness if your glass was that. And with heat and perhaps
some high voltage surface crawling failure was likely. But I don't know how your setup was.
https://www.makeitfrom.com/compare/High-Voltage-Borosilicate...
|
|
Tsjerk
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 3026
Registered: 20-4-2005
Location: Netherlands
Member Is Offline
Mood: Mood
|
|
There was a sticky made not too long ago about checking stress in glass. Maybe you have the means to check the glass that way?
|
|
wg48temp9
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 771
Registered: 30-12-2018
Location: not so United Kingdom
Member Is Offline
|
|
Vomaturge: Yes the glass does not need to be a great conductor.
Given the specification of the transformer is 10kV, 30mA that corresponds to a source resistance of 300 Mohm. Maximum power dissipation will
correspond to a load equal to that resistance, Due to positive feedback the conduction increases with an increase in temperature and temperature
increases due to heating caused by the conduction. If the feedback is greater than one then the temperature will increase until the the feedback
decreases to one. This will result in a temperature such that the resistance is about 300 Mohm, the point of maximum dissipation.
I found a paper on on the electrical properties of soda lime glass at 600C
Attachment: soda-lime-glass-con-.pdf (1.1MB) This file has been downloaded 281 times
600C is a dark red colour of steel Probably even darker glass.
Morgan: The looks glass I used looked less than a 1mm thick. According to the link you gave, soda-lime glass has an dielectric strength of 13kV/mm The
10kV of my transformer is probably an rms value the peak would be much higher. So 13kV/mm would have been easily exceeded resulting in the puncture
happening.
Tsjerk: yes using two sheets of polarizing material. It is possible to peel of the polarizing material on some flat screen monitors. It would be
interesting to see the stress develop as the glass cooled.
PS: The electrical conduction of sodium silicate is why at mains voltages heating elements wound on steel tubes and insulated with silicon dioxide and
sodium containing ceramic fail at high temperatures.
[Edited on 10/14/2021 by wg48temp9]
I am wg48 but not on my usual pc hence the temp handle.
Thank goodness for Fleming and the fungi.
Old codger' lives matters, wear a mask and help save them.
Be aware of demagoguery, keep your frontal lobes fully engaged.
I don't know who invented mRNA vaccines but they should get a fancy medal and I hope they made a shed load of money from it.
|
|
wg48temp9
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 771
Registered: 30-12-2018
Location: not so United Kingdom
Member Is Offline
|
|
Video of the effect
I dropped a glass mixing bowl which broke. It about 4mm thick with 6mm thick lip. So I thought it would be perfect to try to puncture it with the
10kV.
Initially a brush discharge formed either side of the glass, then after about 15s the an arc formed through the glass and started to create a short
filament.
The video below is of an other piece of the bowl. The discharge initially forms a surface discharge round the bottom edge of the glass. The discharge
then punctures the glass and forms a filament.
Sorry I have chopped up the video to make it smaller so I can upload some of it. They are only a wnv files.
Discharge round bottom edge.
Attachment: con-glass2.wmv (2.6MB) This file has been downloaded 271 times
Discharge thru glass and formation of the conducting filament.
Attachment: con-glass-e.wmv (4.7MB) This file has been downloaded 271 times
[Edited on 10/19/2021 by wg48temp9]
I am wg48 but not on my usual pc hence the temp handle.
Thank goodness for Fleming and the fungi.
Old codger' lives matters, wear a mask and help save them.
Be aware of demagoguery, keep your frontal lobes fully engaged.
I don't know who invented mRNA vaccines but they should get a fancy medal and I hope they made a shed load of money from it.
|
|
OldNubbins
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 136
Registered: 2-2-2017
Location: CA
Member Is Offline
Mood: Comfortably Numb
|
|
First video the lip of the bowl is intact and the arc goes around. Second video I see two cracks have formed and the arc appears to be going through
the one on the right. Then, as the arc on the interior melts the surface of the glass, you can see the arc travel up and leave a path of
melted/solidified glass behind it. I don't think the arc punctured the glass, more like the temperature gradient weakened it enough to form a crack
which allowed enough ions to flow through and allow the arc to conduct.
|
|
wg48temp9
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 771
Registered: 30-12-2018
Location: not so United Kingdom
Member Is Offline
|
|
OldNubbins:
I think you may be right about the cracking. Meaning the glass cracks due to the heat of the surface discharge which then allows the discharge to go
thru the glass. This would account for the apparent low dielectric strength of the glass.
Assuming the glass is soda lime glass its dielectric strength should be about 10kV/mm so 4mm thick glass should withstand 40kV. I will be very
surprised if a chinese neon sign transformer rated at 10kV is actually more like 40kV.
Though i doubt it now, I originally thought the glass cooking bowl was probably a borosilicate glass which is 20kV/mm to 40kV/mm dielectric strength.
I am wg48 but not on my usual pc hence the temp handle.
Thank goodness for Fleming and the fungi.
Old codger' lives matters, wear a mask and help save them.
Be aware of demagoguery, keep your frontal lobes fully engaged.
I don't know who invented mRNA vaccines but they should get a fancy medal and I hope they made a shed load of money from it.
|
|
wg48temp9
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 771
Registered: 30-12-2018
Location: not so United Kingdom
Member Is Offline
|
|
Apparently it does conduct thru the glass. If its turned off immediately after it conducts thru the glass there is no obvious sign within the glass
just a mark on on each surface. Its almost instantaneously thru a pyrex test tube with a wall thickness of about 1mm.
I decided the attempt to measure the voltage using a 10kV 100 megohm resistor but it flashed over. So I tried with a spark gap. It can spark across a
30mm gap which suggests the voltage is at least about 83kV. WOW and its still working. It was probably designed to operate with a neon tube which
would limit the voltage.
I am wg48 but not on my usual pc hence the temp handle.
Thank goodness for Fleming and the fungi.
Old codger' lives matters, wear a mask and help save them.
Be aware of demagoguery, keep your frontal lobes fully engaged.
I don't know who invented mRNA vaccines but they should get a fancy medal and I hope they made a shed load of money from it.
|
|
Junk_Enginerd
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 250
Registered: 26-5-2019
Location: Sweden
Member Is Offline
|
|
When it comes to high voltage, glass is significantly conductive >400°C or so to begin with.
But what's most likely going on is due to your high voltage source presumably being AC. AC can be conducted even through infinite resistances due to
capacitive effects. Glass has a relatively high permittivity and will because of this gladly conduct alternating currents, more so
the higher the frequency is. The glass is acting as a capacitor dielectric, between capacitor plates made up of your plasma electrical arc.
If one puts a sufficiently large capacitor between the poles of an AC source, it is indistinguishable from a hard short circuit.
At a high enough frequency, the whole concept of currents needing to return to ground starts to get weird. A typical example is the air discharges
that tesla coils can produce. The electrical current seemingly just goes straight out into the air, despite there being no path to ground. Where to?
The answer is that it actually isn't going anywhere except back and forth very quickly. The frequency is high enough that even with a substantial
current, it just doesn't move enough charge to deplete even the air before putting it right back again. The air may have a very small capacitance, but
at sufficiently high frequency and voltage, it's enough to be significant.
|
|
wg48temp9
National Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 771
Registered: 30-12-2018
Location: not so United Kingdom
Member Is Offline
|
|
Junk_Enginerd:
The initial discharge to the surface of the 4mm thick glass , if it can not reach round the edge is probably due to the capacitance between the two
surfaces.
For example a parallel plate capacitor made from soda lime glass 4mm thick with a dielectric constant of 7.7 and an area 1000mm^2 (about 30mmx30mm)
has a capacitance of 17pF. At a frequency 100kHz that will have an impedance of about 94kohm, which is small compared to the output impedance of the
electronic neon sign transformer assumed to be 330kohm.
I don't know what the switching frequency is but a round 100kHz would be typical for a switching converter. That would be the fundamental frequency,
as the output is unlikely to be a pure sine wave it will have lots of higher frequency harmonics.
[Edited on 10/25/2021 by wg48temp9]
I am wg48 but not on my usual pc hence the temp handle.
Thank goodness for Fleming and the fungi.
Old codger' lives matters, wear a mask and help save them.
Be aware of demagoguery, keep your frontal lobes fully engaged.
I don't know who invented mRNA vaccines but they should get a fancy medal and I hope they made a shed load of money from it.
|
|