xSJF1414
Harmless
Posts: 11
Registered: 19-9-2019
Member Is Offline
|
|
Sodium Ion Battery
I am planning on making a Sodium Ion Battery for a school project however I do not know if it is possible. I just need to make a very small charge and
it doesn't need to be small or very cost efficient. Does have any information about this being possible and/or how to make one, such as the
electrolyte solution I would need, type of anode and separator I would need that would be available for a home chemist.
I should be fine with the sodium, I am going to use Nurd Rage's method to generate it.
Thanks a lot for any help in advance!
|
|
|
clearly_not_atara
International Hazard
Posts: 2787
Registered: 3-11-2013
Member Is Offline
Mood: Big
|
|
How are you going to heat it?
|
|
|
xSJF1414
Harmless
Posts: 11
Registered: 19-9-2019
Member Is Offline
|
|
I'm not sure, honestly I didn't know it needed heating, I've been reading up about it but I definitely do not have nearly as much knowledge as I need
so I made this post to try and help this and to know if its too advanced to do at home.
|
|
|
B(a)P
International Hazard
Posts: 1139
Registered: 29-9-2019
Member Is Offline
Mood: Festive
|
|
I presume you are trying to make the equivalent of a lithium ion battery, but with sodium. The idea being that sodium and lithium are chemically
similar therefore they should be somewhat interchangeable?
A decent amount of research has gone into this given the relative abundance of sodium as compared to lithium.
If this is the route you are after the chemistry is not trivial unfortunately. It seems that making sodium will be the least of your worries.
https://onlinelibrary.wiley.com/doi/abs/10.1002/aenm.2020013...
https://pubs.acs.org/doi/10.1021/acsenergylett.0c02181#:~:text=The%20sodium%20ion%20battery%20(NIB,hinder%20their%20large%2Dscale%20applications.
You might also consider a sodium air battery
https://www.mdpi.com/2079-9292/8/10/1201/htm#:~:text=Sodium%...
|
|
|
WGTR
National Hazard
Posts: 971
Registered: 29-9-2013
Location: Online
Member Is Offline
Mood: Outline
|
|
Once upon a time, in a lab far, far away, I smeared some oxidized bits of tin/lead solder on the inside of a soda-lime glass test tube. I connected a
wire to this solder, dipped the tube in molten sodium nitrate, and electrolyzed a thin film of sodium into the solder, right through the glass. After
this I wrapped some adhesive-backed copper tape around the glass, connected a wire to it, and heated the tube with a heat gun. With a high impedance
voltmeter (10 gigaohms input) I measured about 2.5-2.6V across the cell. I could only get 1uA out of it short-circuited so it wasn't a practical cell
by any means, but it was neat to see the voltage that I expected.
I can't really explain how the cell worked from a chemistry perspective. Oxygen in the air around the copper tape may have had an effect. Maybe even
the tape adhesive itself. It was just a fun evening experiment. If you are starting from sodium metal then you can just put the metal into the tube
and not worry about electrolyzing molten nitrate.
|
|
|
j_sum1
Administrator
Posts: 6320
Registered: 4-10-2014
Location: At home
Member Is Offline
Mood: Most of the ducks are in a row
|
|
If this is a school project, I would consider something less ambitious but equally interesting.
I would suggest a zinc bromine cell except that you would have to work with bromine.
There are plenty of air batteries around.
|
|
|
xSJF1414
Harmless
Posts: 11
Registered: 19-9-2019
Member Is Offline
|
|
Quote: Originally posted by B(a)P  | I presume you are trying to make the equivalent of a lithium ion battery, but with sodium. The idea being that sodium and lithium are chemically
similar therefore they should be somewhat interchangeable?
A decent amount of research has gone into this given the relative abundance of sodium as compared to lithium.
If this is the route you are after the chemistry is not trivial unfortunately. It seems that making sodium will be the least of your worries.
https://onlinelibrary.wiley.com/doi/abs/10.1002/aenm.2020013...
https://pubs.acs.org/doi/10.1021/acsenergylett.0c02181#:~:text=The%20sodium%20ion%20battery%20(NIB,hinder%20their%20large%2Dscale%20applications.
You might also consider a sodium air battery
https://www.mdpi.com/2079-9292/8/10/1201/htm#:~:text=Sodium%...
|
I looked into sodium ion batteries and understand there are different problems when using sodium instead of Lithium, such as the material used for the
anode and electrolyte solution. I'm looking into using sodium perchlorate as the sodium salt but I am not sure on the solvent to dissolve it in.
However the idea of using a sodium air battery is very interesting and seems more do able, thanks.
|
|
|
xSJF1414
Harmless
Posts: 11
Registered: 19-9-2019
Member Is Offline
|
|
| Quote: Originally posted by j_sum1 | If this is a school project, I would consider something less ambitious but equally interesting.
I would suggest a zinc bromine cell except that you would have to work with bromine.
There are plenty of air batteries around. |
Its a project I'm planning to work on for a third party competition outside of school for fun and to help my UCAS for when applying for university.
This means I'm working at home and I am uncomfortable working with bromine at my level of chemistry at the moment. However I could see if I can get my
school to help but it would be easier for them to help if its seems like a developing field of research and might have key uses in the future. I
haven't looked into them much yet and don't have that much of an idea on them. Thanks!
|
|
|