The density was calculated by my teacher when she received the sample. I was incorrect when I said that she recieved it with that label.
|
|
|
opfromthestart
Harmless
Posts: 46
Registered: 23-12-2018
Member Is Offline
Mood: tetranitrammmonium chlorate
|
|
Quote: Originally posted by ScienceHideout  |
Also, looking at the bottle, it is probably a single metal and not an alloy. It has an analysis on it that says 100.0%...
[Edited on 2-5-2019 by ScienceHideout] |
I hadn't noticed that. However, as elementcollector1 said, the only pure metal with that density is terbium, which is the first thing I tested it for.
Since it did not react I suspect it is not a pure metal.
Also, the container itself may be not specific to the metal and may have been intended for something else, if that is a possibility.
|
|
|
opfromthestart
Harmless
Posts: 46
Registered: 23-12-2018
Member Is Offline
Mood: tetranitrammmonium chlorate
|
|
I heated some scrapings of the metal in a crucible with a Bunsen burner. It didn't appear to melt but quickly oxidized when I held the inner blue cone
of the flame. It oxidized into a black solid.
I will try dissolving the solid in nitric and hydrochloric acid to see if it has any distinctive metal ion colors.
|
|
|
fusso
International Hazard
Posts: 1922
Registered: 23-6-2017
Location: 4 ∥ universes ahead of you
Member Is Offline
|
|
Small pieces of scrapings would probably completely oxidize before they could melt. Try larger pieces.
[Edited on 190502 by fusso]
|
|
|
elementcollector1
International Hazard
Posts: 2684
Registered: 28-12-2011
Location: The Known Universe
Member Is Offline
Mood: Molten
|
|
Assuming that black isn't soot, it's a good start. Metals with black oxides, according to the list, are:
-Chromium (II) oxide. Very unlikely owing to the nature of its existence.
-Chromium (IV) oxide. Also unlikely.
-Cobalt oxide. Hardness of the metal is entirely wrong for cobalt.
-Iron (II) oxide. Hardness is wrong, same as cobalt.
-Iron (II, III) oxide - magnetite. See above.
-Copper(II) oxide. Color is wrong.
-Lead (IV) oxide. Now this is a possible candidate.
-Manganese (IV) oxide. See cobalt and iron.
-Silver (I) oxide. I might almost believe this one, honestly. Pure silver is more dense than the sample, but alloyed silver is still on the table.
-Tin (II) oxide. Apparently it's flammable, burning to tin (IV) oxide, so if the black color remained after burning for a while it's probably not
this.
Of those, the two best candidates are lead and silver, and my money's definitely on lead, alloyed with something lighter like tin.
[Edited on 5/3/2019 by elementcollector1]
Elements Collected:52/87
Latest Acquired: Cl
Next in Line: Nd
|
|
|
ScienceHideout
Hazard to Others
Posts: 391
Registered: 12-3-2011
Location: In the Source
Member Is Offline
Mood: High Spin
|
|
| Quote: Originally posted by opfromthestart | | The density was calculated by my teacher when she received the sample. I was incorrect when I said that she recieved it with that label.
|
I understand, but...
1. We are dealing with a pure metal, according to the analysis.
2. The only metal with a density close to that is terbium.
3. It was determined that said metal is not terbium.
So something is wrong: it is either the label, the density, or the confirmation of not-terbium.
Unless the bottle was recycled (unlikely), the analysis is probably correct. You tested for terbium and got a negative result, which I believe for
several reasons.
Density, on the other hand...
We are all human. Your AP chemistry teacher is, too. She may have made a mistake while determining the density. This is why analysts often do
measurements in triplicate when applicable. This is not to say she is stupid, just that accidents happen! In situations like this in particular, an
experimental blunder could go unnoticed because it wouldn't propagate a big, blatant, questionable error: Something as simple as forgetting to tare
the balance, or pressing the wrong button on the calculator could have given her the wrong density, and we have no way of knowing since it was
measured only once.
It doesn't take very long to put a piece on a scale, and then submerge it in water. Sure, you might find that your teacher's analysis was correct, and
you still cannot confirm the identity. BUT, there is also a chance that you come up with a different number, and those couple minutes of double
checking could provide a definite answer. If you have time to play around with corrosive acids and fire, you have time to do this. 
TL;DR- It pays to double check. Take another density measurement to assure that your teacher didn't overlook a simple mistake. It only takes a few
seconds.
hey, if you are reading this, I can't U2U, but you are always welcome to send me an email!
|
|
|
Fulmen
International Hazard
Posts: 1725
Registered: 24-9-2005
Member Is Offline
Mood: Bored
|
|
What lead you to that conclusion?
[Edited on 3-5-19 by Fulmen]
We're not banging rocks together here. We know how to put a man back together.
|
|
|
opfromthestart
Harmless
Posts: 46
Registered: 23-12-2018
Member Is Offline
Mood: tetranitrammmonium chlorate
|
|
She just tested the densities of two of the samples and they came back as 6.407 g/cm^3 and 7.337 g/cm^3. Since this disparity seems too great to be
due to measurement error and I did the calculations myself(and checked it), I believe the samples may be different metals or at least different
compositions of a similar alloy. One of my classmates will be testing the other 4 samples later today.
College student and hobby chemist
|
|
|
OldNubbins
Hazard to Others
Posts: 136
Registered: 2-2-2017
Location: CA
Member Is Offline
Mood: Comfortably Numb
|
|
Those are either solder bars/sticks for making stained glass windows or babbitt in extruded wire form
|
|
|
ScienceHideout
Hazard to Others
Posts: 391
Registered: 12-3-2011
Location: In the Source
Member Is Offline
Mood: High Spin
|
|
Fulmen, I don't believe that bottle was recycled because I have seen metal sticks packaged in that type of bottle before. So unless someone took some
sticks out, and put others in, I doubt it was recycled.
Opfromthestart, That is certainly interesting. I'd be willing to bet that they all are the same metal: I don't see why there would be different ones
in the same bottle that look the same, and again, unlikely that there are various alloy compositions due to "100%" being on the bottle. That being
said, both 6.407, 7.337, and 8.19 are all very different measurements. I am really looking forward to the results from your classmates- this could
provide one single accurate measurement. Out of curiosity, have you guys ever tried either a pycnometric method, or hydrostatic weighing? These could
both help improve your density measurements by omitting the need for volume measurement.
OldNubbins, They do certainly look like that! Does stained glass solder normally come in a bottle like that, though? What is the typical melting point
of stained glass solder?
[Edited on 3-5-2019 by ScienceHideout]
hey, if you are reading this, I can't U2U, but you are always welcome to send me an email!
|
|
|
OldNubbins
Hazard to Others
Posts: 136
Registered: 2-2-2017
Location: CA
Member Is Offline
Mood: Comfortably Numb
|
|
Regular 50/50 or 60/40 solder (no rosin core) is used, nothing special. Melting point around 400°. Comes in various sizes depending on the
application. i have seen bars larger then the OP's. You can tell the OP's material is extruded because of the seams on the sides and tapered ends.
There's no way to know if the paper tube in the OP's picture is the original package - wouldn't really help anyways since it can come in anything or
nothing.
|
|
|
ScienceHideout
Hazard to Others
Posts: 391
Registered: 12-3-2011
Location: In the Source
Member Is Offline
Mood: High Spin
|
|
Is this why you believe it's solder, though? I mean, a lot of metals are extruded...
hey, if you are reading this, I can't U2U, but you are always welcome to send me an email!
|
|
|
elementcollector1
International Hazard
Posts: 2684
Registered: 28-12-2011
Location: The Known Universe
Member Is Offline
Mood: Molten
|
|
True, but that plus other evidence is increasingly leaning towards solder or something similar. For reference, a eutectic lead/tin solder alloy (63%
Sn, 37% Pb) has a density of approximately 8.4 g/cc.
Still, chemical tests will likely tell us something more. OP could also differentiate between silver-based and lead-based by checking if the bulk
metal melts on stovetop heat (though if it's lead, might want to turn the vent fan up. Or use a hotplate in a fume hood).
Elements Collected:52/87
Latest Acquired: Cl
Next in Line: Nd
|
|
|
OldNubbins
Hazard to Others
Posts: 136
Registered: 2-2-2017
Location: CA
Member Is Offline
Mood: Comfortably Numb
|
|
The extrusion marks are only one of the examples I gave. I am convinced it is solder or some other low melt alloy. You don't have to be, you are
welcome to investigate further, unfortunately with the limited amount of information the OP has given, we are at an impasse.
|
|
|
OldNubbins
Hazard to Others
Posts: 136
Registered: 2-2-2017
Location: CA
Member Is Offline
Mood: Comfortably Numb
|
|
| Quote: Originally posted by elementcollector1 |
True, but that plus other evidence is increasingly leaning towards solder or something similar. For reference, a eutectic lead/tin solder alloy (63%
Sn, 37% Pb) has a density of approximately 8.4 g/cc.
Still, chemical tests will likely tell us something more. OP could also differentiate between silver-based and lead-based by checking if the bulk
metal melts on stovetop heat (though if it's lead, might want to turn the vent fan up. Or use a hotplate in a fume hood). |
One way I check for lead is to melt the alloy (solder, babbitt, other low-melts) in question, throw some KNO3 into the melt and give it a mix.
Yellowish litharge should form (PbO), Bob's your uncle!
|
|
|
Fulmen
International Hazard
Posts: 1725
Registered: 24-9-2005
Member Is Offline
Mood: Bored
|
|
I disagree. The seams looks more like mould lines, extruded bars will typically have fine axial lines around the entire perimeter. The surface also
has wrinkles that looks more like cast (or perhaps even stamped) metal.
And just to be clear, not only have I seen cast and extruded lead before, I've even made it and the tooling myself.
Most of the ends aren't really tapered, they look more like they've been cut with bolt cutters. The tapering could be from use if it's solder.
We're not banging rocks together here. We know how to put a man back together.
|
|
|
phlogiston
International Hazard
Posts: 1379
Registered: 26-4-2008
Location: Neon Thorium Erbium Lanthanum Neodymium Sulphur
Member Is Offline
Mood: pyrophoric
|
|
I remember a thread where someone found a mystery metal rod, which turned out to be actual platinum. (185 grams of it!)
Found it: https://www.sciencemadness.org/whisper/viewthread.php?tid=20...
[Edited on 4-5-2019 by phlogiston]
-----
"If a rocket goes up, who cares where it comes down, that's not my concern said Wernher von Braun" - Tom Lehrer |
|
|
Heptylene
Hazard to Others
Posts: 319
Registered: 22-10-2016
Member Is Offline
Mood: No Mood
|
|
I read the thread, apparently there wasn't any real conclusion was there?
Regarding the mystery metal in this thread, those look like extruded metal rods, cut with a hydraulic shear. When you cut thick wire you the same
pattern on the cut end. That narrows it to softer metals that can be extruded that way. I have a bar of cadmium that looks similar, different density
though.
|
|
|
Sulaiman
International Hazard
Posts: 3721
Registered: 8-2-2015
Location: 3rd rock from the sun
Member Is Offline
|
|
ALARM !
... those are very precise numbers,
and different from each other and the original sample.
The test of density is surprisingly quick, easy and accurate.
It does not rely on the accuracy of the only instrument required, the scales,
it only relies on their linearity - for a weight ratio.
The crud will need to be mechanically removed from each stick
(keep the crud from each, separately, until you KNOW that it is worthless)
and, any tiny bubbles on the submerged surface will give significant errors.
I have used this method many times, and cross-checked by other means, 1% accuracy is easily attainable using cheap scales.
(Correction must of course be made for the variation of the density of water with temperature if accurate results are required.)
If there are three of you then each of you should measure all samples - then compare notes.
(using your teacher's results) as a reference - with an open objective mind)
Simple techniques are worth mastering - for confidence in your own abilities.
PLUS
it would enable more concise and precise discussions with other members.
P.S. I was refering to this type of measurement https://www.youtube.com/watch?v=xYdSEAm-7uI
https://www.youtube.com/watch?v=N1HCrNMnb9I
[Edited on 4-5-2019 by Sulaiman]
CAUTION : Hobby Chemist, not Professional or even Amateur
|
|
|
opfromthestart
Harmless
Posts: 46
Registered: 23-12-2018
Member Is Offline
Mood: tetranitrammmonium chlorate
|
|
The samples were tested with an analytical balance(the fancy one with doors, i think about .001g accuracy).
The samples tested around 7.3 but some were as high as 7.6(each was tested 3 times by both the teacher and my classmate, I wasnt there).
When my teacher removed most of the oxidation, the density dropped to 7.06. This sets the pure metal possibilities to Mn, Cr, and In, and possibly a
few I overlooked.
College student and hobby chemist
|
|
|
fusso
International Hazard
Posts: 1922
Registered: 23-6-2017
Location: 4 ∥ universes ahead of you
Member Is Offline
|
|
The few metal oxides that are denser than the metal are some alkali, earth & RE metals...
[Edited on 190506 by fusso]
|
|
|
opfromthestart
Harmless
Posts: 46
Registered: 23-12-2018
Member Is Offline
Mood: tetranitrammmonium chlorate
|
|
| Quote: Originally posted by fusso | The few metal oxides that are denser than the metal are some alkali, earth & RE metals...
[Edited on 190506 by fusso] |
Well, it doesn't react with acid or water so i doubt its any of those.
College student and hobby chemist
|
|
|
fusso
International Hazard
Posts: 1922
Registered: 23-6-2017
Location: 4 ∥ universes ahead of you
Member Is Offline
|
|
Most earth sulphates are insoluble so it may form some protective layer in H2SO4?
|
|
|
opfromthestart
Harmless
Posts: 46
Registered: 23-12-2018
Member Is Offline
Mood: tetranitrammmonium chlorate
|
|
If it would be a RE metal, it would probably have to be Ce, Pr, or Yb based on the density.
College student and hobby chemist
|
|
|
opfromthestart
Harmless
Posts: 46
Registered: 23-12-2018
Member Is Offline
Mood: tetranitrammmonium chlorate
|
|
Cerium and Ytterbium oxide are not black, and Praseodymium is paramagnetic, which the rods are not. So... still probably an alloy.
College student and hobby chemist
|
|
|