What is "Black Ruthenium" plating?
I saw this "Black Ruthenium" pen plating solution on ebay:
http://cgi.ebay.com/PEN-PLATING-SOLUTION-BLACK-RUTHENIUM-30M...
Being that it's $60.00 USD for only 30 ml, I'm thinking it must really be ruthenium, but if it's black, I'm thinking it must be RuO2. Is it possible
to easily plate PGM oxides some how?
|
|
Magpie
lab constructor
Posts: 5939
Registered: 1-11-2003
Location: USA
Member Is Offline
Mood: Chemistry: the subtle science.
|
|
This is just a remembrance from the past but when were making plans to dissolve spent nuclear fuel at work we were concerned with where the
radioactive Ru would end up. Our understanding was that it would go into the off-gas as Ru oxide and end up plating (or attaching) itself to the
nearest available stainless steel.
The single most important condition for a successful synthesis is good mixing - Nicodem
|
|
pyrochem
Harmless
Posts: 21
Registered: 1-1-2006
Location: United States
Member Is Offline
Mood: No Mood
|
|
I happened to see the same item, and I think thin platings of Ru are black/dark. Perhaps it is covered in an oxide layer. One Ru plated item is at http://www.theodoregray.com/PeriodicTable/Elements/044/index... The necklace beads are a sort of dark gray.
|
|
Fleaker
International Hazard
Posts: 1252
Registered: 19-6-2005
Member Is Offline
Mood: nucleophilic
|
|
I think it's some sort of electrolyte, like K2PtCl4 (which will plate out a black platinum deposit) so I think this is something of a similar nature.
Comparing platinum to ruthenium might be going to far, but it should behave relatively similar.
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
I sent the seller an email, asking him about this, but as of yet I've received no reply.
BTW, here's an excerpt from a patent I've uploaded in another thread:
Example XVI
Two titanium rods were degreased and pickled and subsequently placed in a galvanic bath having the following composition:
100 cc. ethanol
100 cc. water
1 g. ruthenium chloride
10 g titanium chloride
and subsequently connected to a source of alternating current of 13 volts and a current density of 15 amp/m^2, temperature 20-30 degrees C., for a
period of about 20 minutes.
After about 20 minutes both rods were coated with a mixture of titanium oxide and ruthenium oxide, the adhesion of which was still further improved by
heating at 400 degrees C for 5 minutes.
The anode thus made is excellently suitable for use in various electrolyses at low current densities.
******************************************
If that's accurate, then I suppose it's possible that this plating solution does plate RuO2.
|
|