Fe3o4 electrode
I here that there are tow main electrodes for chlorate production by electrolysis pbo2 and fe3o4(that are cheap) how hard would it be to melt fe3o4 in
a normal microwave and how good do they work compared to lead dioxide electrodes and is it possible to get it from a cow magnet
|
|
BromicAcid
International Hazard
Posts: 3237
Registered: 13-7-2003
Location: Wisconsin
Member Is Offline
Mood: Rock n' Roll
|
|
If you have powdered magnetite (or iron oxide black) I don't think you'll be able to fuse it in a microwave from what I've seen
microwaves have trouble melting glass and when magnetite melts it decomposes to ferric oxide, the transition occurring slightly above 1500C. If the
electrode is just magnetite then couldn't a large piece be simply procured from a mineralogical shop? Too bad hematite can’t be used, I see it
all the time at convience stores for a ‘mood’ stone to help calm people. I’m sure this has already been extensively investigated by someone out
there, perchlorate cells were all the rage at one time so you should be learning more soon.
|
|
kclo4
National Hazard
Posts: 916
Registered: 11-12-2004
Location:
Member Is Offline
Mood: No Mood
|
|
on the msds sheets it say it melts Over 1200º F
|
|
Jome
Hazard to Others
Posts: 154
Registered: 10-6-2004
Location: Soutwest sweden
Member Is Offline
Mood: desiccated
|
|
Iron (II, III) oxide, magnetite, Melting point: 1594 degrees centrigrade. Thats a lot. Perhaps fusing it would not require it to be molten, if it
could be made as a fine powder, then perhaps it could be fused like ceramics.
One way to make it a fine powder would be to heat iron sulfate to its decomposition temperature.
|
|
BromicAcid
International Hazard
Posts: 3237
Registered: 13-7-2003
Location: Wisconsin
Member Is Offline
Mood: Rock n' Roll
|
|
That process is called sintering I believe, if you heat the sulfate to the decomposition point I'd think that you would end up with one singualr
oxide not the exact mixture that constitutes your desired product, if you look at a structure of it, it doesn't look that simple, spindles of
alternating iron oxides and such, I'm sure someone has messed around trying to make these type of electrodes before.
|
|
kclo4
National Hazard
Posts: 916
Registered: 11-12-2004
Location:
Member Is Offline
Mood: No Mood
|
|
could you decompose iron acetate to fe3o4 i cant find much info on it