Best acid combination to erode steel.
I was considering the possibility of doing some "chemical machining" on steel. Common steel, not ss.
Could anyone come up with a better etching mix than HCl + H2O2? Is that a good mix at all?
And, please, I have easy acess to industrial chemicals, but not to research chemicals (Aldrich kind) so zoobydoobyisocyanate is out of question.
I have already done CM quite well on copper and brass using ferric chloride.
|
|
|
Hermes_Trismegistus
National Hazard
Posts: 602
Registered: 27-11-2003
Location: Greece, Ancient
Member Is Offline
Mood: conformation:ga
|
|
Alternative to HCl + H2O2
Arguing on the internet is like running in the special olympics; even if you win: you\'re still retarded.
|
|
|
rikkitikkitavi
Hazard to Others
Posts: 192
Registered: 17-6-2002
Member Is Offline
Mood: No Mood
|
|
try hot diluted sulfuric acid, about 15-50 %. preferably boiling , it will not give off gases like HCL and heat increases corrosion rate dramatically.
Cold conc HCl compared to warm conc HCl is also a big difference
/rickard
|
|
|
Hermes_Trismegistus
National Hazard
Posts: 602
Registered: 27-11-2003
Location: Greece, Ancient
Member Is Offline
Mood: conformation:ga
|
|
| Quote: | Originally posted by rikkitikkitavi
try hot diluted sulfuric acid, about 15-50 %./rickard |
Pretty loose def'n of dilute you got there Partner!
(p.s. Maybe 9/11 wasn't a terrorist attack, perhaps they were just landing "near" JFK's runway #4)
Arguing on the internet is like running in the special olympics; even if you win: you\'re still retarded.
|
|
|
JustMe
Hazard to Others
Posts: 111
Registered: 7-8-2003
Member Is Offline
Mood: No Mood
|
|
This may turn out to be REALLY dumb, but I thought I'd throw it out, because he said it wasn't stainless steel.
A LOOOOONG time ago I was show a quick and easy way to corrode steel wool, it works immediately, but I've never tried it on bulk steel. Simply
mix equal quantities of Vinegar (5% acetic acid) and commercial bleach (~5% sodium hypochlorite). It generates Hypochlorous acid continously...
resulting in instant rust. YMMV
Oh uh, I just re-read the post, he want's etching, not corroding. Well, never mind.
|
|
|
atombum
Harmless
Posts: 20
Registered: 7-6-2004
Member Is Offline
Mood: No Mood
|
|
Aqua Regia perhaps? ....and then there's also the chlorine fluorides, not acid in their anhydrous state, but said to be able to even cut steel,
and just about anything else.
|
|
|
Mr. Wizard
International Hazard
Posts: 1042
Registered: 30-3-2003
Member Is Offline
Mood: No Mood
|
|
Tacho, if you just want to etch steel, as in an engraving or writing your name on a tool or knife blade, try using a NaCl solution on a sponge hooked
to the - NEG side of a battery charger (3 -12 volt DC) and the thing to be etched hooked to the + PLUS side, where the nascent Cl is liberated.
Protect the surface of the blade with wax by melting on a thin layer, scratch the pattern through the wax and on the first pass with the electrolytic
sponge it will darken any exposed metal. Even fine lines scratched through the wax will be sharply defined. The etching is quite permanent, as I found
out after trying to redo some mistakes. With a good photo resist as used in circuit board production, and a computer generated negative or mask, you
could even transfer simple images.
I've been told that Chlorine gas. used in many facilities in my area, will quickly eat through a steel pipe if the chlorine becomes contaminated
with water.
|
|
|
Dodoman
Hazard to Self
Posts: 79
Registered: 2-8-2004
Member Is Offline
Mood: No Mood
|
|
I didn't know that about Cl and water. Anyway i gave it a go and it works very fast. Nice tip 
|
|
|
chloric1
International Hazard
Posts: 1146
Registered: 8-10-2003
Location: GroupVII of the periodic table
Member Is Offline
Mood: Stoichiometrically Balanced
|
|
Ferric Chloride
You know I would add a small amount of HCl to your Ferric Chloride and use and electrolytic method simular to Mr. Wizard's. May cut quicker or
deeper.
Fellow molecular manipulator
|
|
|
Tacho
National Hazard
Posts: 582
Registered: 5-12-2003
Member Is Offline
Mood: No Mood
|
|
Thanks all,
H2SO4 75% and H2SO4(75%)+H2O2(200vol, 35%?) are worse than HCl (37%)+H2O2(200vol, 35%?). The best etching I got is 0,17mm for a 6 hours bath (using
HCl). I’m looking for 1mm/hour etching. I’ll try Mr. Wizard’s suggestion tomorrow.
|
|
|
Tacho
National Hazard
Posts: 582
Registered: 5-12-2003
Member Is Offline
Mood: No Mood
|
|
Using NaCl and electricity was, so far, the best method. More than a mm of steel disappeared in less than ½ hour under 15V and strong current.
Thanks Mr.Wizard.
Now I have that feeling: “how come I didn’t think of that before…”
|
|
|
Mr. Wizard
International Hazard
Posts: 1042
Registered: 30-3-2003
Member Is Offline
Mood: No Mood
|
|
Tacho, Thanks for the feedback. I've never used it for anything but engraving knife blades, or tools, so 0.5 mm in 30 minutes is surprising.
Are you using a mask (resist or wax) and how much surface area are you cutting?
I've also been told by professionals that Chlorine will ignite and burn steel if heated over either 86C or 186C, I don't remember which. It
is supposed to evolve brown clouds of FeCl3 smoke.
[Edited on 31-10-2004 by Mr. Wizard]
|
|
|
Tacho
National Hazard
Posts: 582
Registered: 5-12-2003
Member Is Offline
Mood: No Mood
|
|
I am willing to cut steel plates and steel pipes. More immediately, I am considering the possibility of making a screw for an oil extracting screw
press out of a steel pipe and some epoxy resin, or from a solid steel rod.
I have been doing my tests on a 1.6mm diameter steel wire. It took about 6 hours for the acids to reduce the diameter to 1.25mm. I was surprised
because I was expecting faster results. Using the electrolytic way, the submerged wire had a sharp needle shape in about 30 minutes. So I assume a
0.8mm in ½ hour. Results could be different for a plate (sheet?) but , comparatively, electrolytic is clearly faster.
|
|
|
Hermes_Trismegistus
National Hazard
Posts: 602
Registered: 27-11-2003
Location: Greece, Ancient
Member Is Offline
Mood: conformation:ga
|
|
Peroxymonosulphuric acid
Sorry tacho, I didn't mention that conversion to Caro's acid requires both high-test sulphuric and peroxide.
but considering the price of salt and electricity I'd say that you cannot beat that other method with a stick.
Arguing on the internet is like running in the special olympics; even if you win: you\'re still retarded.
|
|
|
Tacho
National Hazard
Posts: 582
Registered: 5-12-2003
Member Is Offline
Mood: No Mood
|
|
I have never seen Caro's acid in action, but I have a feeling that it's too dangerous for my taste. That's why I used only 75% H2SO4 in
my mix.
After all...
"...pirahna bath spatter + eyeballs = ray charles. "
[Edited on 1-11-2004 by Tacho]
|
|
|
tokat
Hazard to Self
Posts: 64
Registered: 1-6-2004
Location: 6feet south
Member Is Offline
Mood: No Mood
|
|
in enginering they use nitric acid, and phospric acid in 50%/50% MIX. AS A EICHING MIX.
|
|
|
tom haggen
Hazard to Others
Posts: 488
Registered: 29-11-2003
Location: PNW
Member Is Offline
Mood: a better mood
|
|
What do you think would happen if you mixed HCl with caros acid?