does anybody have an idea as to what happened?
hi,
today I took my dry K2CrO4 out of my evaporation dish (I made it from K2Cr2O7 and KOH) and when i washed the dish I got a big surprise!
the entire bottom of the dish was frosted! Could the KOH I used have caused this? i never heated it over 140*C. wouldn't it take a lot longer to do
this?
all above information is intellectual property of Pyro. ![:D](./images/smilies/biggrin.gif)
|
|
Hexavalent
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1564
Registered: 29-12-2011
Location: Wales, UK
Member Is Offline
Mood: Pericyclic
|
|
What's with the magical '140*C'?
Concentrated solutions of alkali metal hydroxides will eat glass anyway, how long was the KOH solution in contact with the glass for?
I've seen this happen a few times and have a got a few beakers in this kinda state.
"Success is going from failure to failure without loss of enthusiasm." Winston Churchill
|
|
Pyro
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1305
Registered: 6-4-2012
Location: Gent, Belgium
Member Is Offline
Mood: No Mood
|
|
3 days. whenever I was there I heated it. but when I was heating it i saw the temp. on my hotplate and it was mostly between 95-120* because
temperature has to do with how fast an alkali attacks glass.
all above information is intellectual property of Pyro. ![:D](./images/smilies/biggrin.gif)
|
|
Hexavalent
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1564
Registered: 29-12-2011
Location: Wales, UK
Member Is Offline
Mood: Pericyclic
|
|
Naturally, as it is a chemical reaction between the KOH and the SiO2 in the glass to make potassium silicate.
Even at these temperatures you mention, a fair amount of dissolving would have taken place, particularly if the solution was concentrated.
"Success is going from failure to failure without loss of enthusiasm." Winston Churchill
|
|
woelen
Super Administrator
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 7990
Registered: 20-8-2005
Location: Netherlands
Member Is Offline
Mood: interested
|
|
Yes, Hexavalent is right. Even at room temperature, strong alkalies can attack glass. I once had a glass jar, which held a saturated solution of NaOH.
I kept it in the jar for a week or so and after that week I could clearly see to what level the liquid was stored.
Never keep strongly alkaline solutions in glass for more than a few hours at room temperature and not more than a few minutes at higher temperature
around 100 C.
|
|