Non-hygroscopic replacement for sodium bisulphate
Sodium bisulphate is commonly used to "burn out" cellulose fibers from fabrics to make fabric patterns with "cut outs"... ala: http://www.prochemicalanddye.com/home.php?cat=255
The process is generally to apply a sodium bisulphate solution, allow the water to evaporate leaving the fabric impregnated with the dry(ish)
bisulphate (hydrate), and then heat the item which results in severe attack to the cellulose.
I'd like to find a substance that behaves identically, but is not hygroscopic. Reason being that the sodium bisulphate absorbs so much water that, in
the interim, the fabric is damp feeling and floppy and it makes it hard to work with. Any ideas?
I tried citric and oxalic acid on a lark - they do not have any appreciable action on the cellulose. Things like DAP (diammonium phosphate) seem like
they might be promising, but are still at least slightly hygroscopic.
|
|
|
DJF90
International Hazard
Posts: 2266
Registered: 15-12-2007
Location: At the bench
Member Is Offline
Mood: No Mood
|
|
conc. Sulfuric acid? Instant burn holes 
|
|
|
amaurer
Harmless
Posts: 22
Registered: 25-7-2012
Member Is Offline
Mood: No Mood
|
|
I suppose thats a fair answer... ... but I should have mentioned that the "dry"
nature of the bisulphate process is important.
The entire issue is that I need to handle the item between the time that the bisulphate/whatever has dried and the time that the heat is applied to
"activate" it. If there is any sigificant moisture (like there is with bisulphate) its impossible to handle, too floppy.
|
|
|
Lambda-Eyde
National Hazard
Posts: 860
Registered: 20-11-2008
Location: Norway
Member Is Offline
Mood: Cleaved
|
|
Maybe potassium bisulfate would be less hygroscopic?
This just in: 95,5 % of the world population lives outside the USA
Please drop by our IRC channel: #sciencemadness @ irc.efnet.org
|
|
|
Si-Sa-Sulfur
Harmless
Posts: 2
Registered: 25-7-2012
Member Is Offline
Mood: No Mood
|
|
Assuming you need an acid for the staining, I don't think you'll be able to find a non-hygroscopic staining agent.
The acid group almost assures a hygroscopic nature, and certainly a very heavily hydrophilic one. The best you can get is mildly-hygroscopic, at least
with the "mineral" acids.
If I were you I'd give the DAP a try.
[Edited on 25-7-2012 by Si-Sa-Sulfur]
Thanks for reading and considering the post above.
|
|
|
amaurer
Harmless
Posts: 22
Registered: 25-7-2012
Member Is Offline
Mood: No Mood
|
|
Not for the staining, I'm actually after the embrittlement that allows area to be cracked/washed away. Its for making irregular holes in the fabric
without taking time to cut each one out.
|
|
|
DJF90
International Hazard
Posts: 2266
Registered: 15-12-2007
Location: At the bench
Member Is Offline
Mood: No Mood
|
|
I reckon lambda-eyde might be onto something with his suggestion...
|
|
|
amaurer
Harmless
Posts: 22
Registered: 25-7-2012
Member Is Offline
Mood: No Mood
|
|
Is there any measurement of hygroscopy so I could compare the two?
|
|
|
AJKOER
Radically Dubious
Posts: 3026
Registered: 7-5-2011
Member Is Offline
Mood: No Mood
|
|
Try Tetra-amminecopper(II) sulfate, [Cu(NH3)4(H2O)n]SO4. It is a blue solid hydrate reputedly related to Schweizer's reagent, tetra-amminediaquacopper
dihydroxide, [Cu(NH3)4(H2O)2](OH)2, which exists in aqueous solutions only (hence not the answer), that is capable of dissolving cellulose fibers.
On heating Tetra-amminecopper(II) sulfate, any hydrolysis that occurs within the hydrated salt could yield Schweizer's reagent and H2SO4, both of
which attack cellulose.
[Edited on 26-7-2012 by AJKOER]
|
|
|
woelen
Super Administrator
Posts: 8014
Registered: 20-8-2005
Location: Netherlands
Member Is Online
Mood: interested
|
|
Potassium bisulfate is not an option. I have both the sodium salt and the potassium salt. The latter is MUCH more hygroscopic, it becomes wet in plain
air, not just humid.
|
|
|
Si-Sa-Sulfur
Harmless
Posts: 2
Registered: 25-7-2012
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by amaurer  | | Not for the staining, I'm actually after the embrittlement that allows area to be cracked/washed away. Its for making irregular holes in the fabric
without taking time to cut each one out. |
If the embrittling must be done with an acid, the hygrophillic nature of acid groups will still get you. Same thing with basic compounds.
Some ionic liquids are able to dissolve cellulose. The copper ammonia complex already mentioned in this thread will also dissolve cellulose, but it's
also hydroscopic.
Thanks for reading and considering the post above.
|
|
|
liquidlightning
Hazard to Self
Posts: 66
Registered: 10-5-2012
Location: Washington
Member Is Offline
Mood: Witty
|
|
Zinc chloride maybe? Although that too is hygroscopic...
|
|
|
bahamuth
Hazard to Others
Posts: 384
Registered: 3-11-2009
Location: Norway
Member Is Offline
Mood: Under stimulated
|
|
Perhaps a dry conversion of a bicarbonate salt to carbonate may be doable, given that carbonate is strong enough to chew through cellulose which i am
not sure it does...
Any sufficiently advanced technology is indistinguishable from magic.
|
|
|
liquidlightning
Hazard to Self
Posts: 66
Registered: 10-5-2012
Location: Washington
Member Is Offline
Mood: Witty
|
|
So, we need something that is non-hygroscopic, hydrate, and corrosive to cellulose. Melts at a low temp, etches fabric, then dries due to water of
hydration evaporating. I can't think of anything that fits the bill.
|
|
|
amaurer
Harmless
Posts: 22
Registered: 25-7-2012
Member Is Offline
Mood: No Mood
|
|
Yeah maybe its a tall order. It doesn't need to melt, really.
The way the process works now is that the sodium bisulphate is dissolved in water (often with a thickener like xantham gum to prevent running) and
then applied to the fabric to be removed. Then its allowed to dry, presumably leaving the sodium bisulphate hydrate inside the fabric.
It can stay like that nearly indefinitely without issue, except for the fact that the moisture trapped by the bisulphate will make even the stiffest
fabrics feel damp and floppy.
Then heating past ~250F causes the bisulphate to attack the fabric.
I'm not really sure chemically how that last step works. I assume, perhaps, that the water from the hydrate a requirement for the bisulphate to act
on the cellulose? or is the bisulphate itself melting (I think the MP of the hydrate is quite low) and reacts without water?
[Edited on 26-7-2012 by amaurer]
|
|
|
liquidlightning
Hazard to Self
Posts: 66
Registered: 10-5-2012
Location: Washington
Member Is Offline
Mood: Witty
|
|
Hydrates will sometimes dissolve in their own water of hydration at even fairly low temps, like 35-40C. They don't exactly "melt" per se.
Sodium Bisulfate monohydrate "melts" at 58.5C
Anhydrous melts at 315C.
Besides, why does it matter if it is hygroscopic? Aren't you supposed to thoroughly wash after the process is done? I mean, what happens if it starts
to rain and you have bisulphate/other corrosive substance in your clothes.
[Edited on 26-7-2012 by liquidlightning]
[Edited on 26-7-2012 by liquidlightning]
|
|
|
amaurer
Harmless
Posts: 22
Registered: 25-7-2012
Member Is Offline
Mood: No Mood
|
|
Its just a handling issue. By the time you'd be wearing it yes it'd be washed and bisulphate free. But while you're working with the fabric prior to
washing the moisture content is problemmatic.
|
|
|
liquidlightning
Hazard to Self
Posts: 66
Registered: 10-5-2012
Location: Washington
Member Is Offline
Mood: Witty
|
|
As far as I know, solids won't react the way you want, it needs to be dissolved, or molten. That's just as far as I know though, might be something
out there.
|
|
|
amaurer
Harmless
Posts: 22
Registered: 25-7-2012
Member Is Offline
Mood: No Mood
|
|
Well I'm no chemist but thats my understanding as well. I do know that the process still works even if I get it as dry as possible... for example,
putting the fabric under silica gel, or in the oven at 170F, for several hours gets rid of the damp behavior but it will return in short order if left
in the air.
But the cellulose burns out fine even when as "dry" as I can get it.
[Edited on 26-7-2012 by amaurer]
|
|
|
liquidlightning
Hazard to Self
Posts: 66
Registered: 10-5-2012
Location: Washington
Member Is Offline
Mood: Witty
|
|
Water of hydration remains at 170C.
|
|
|
amaurer
Harmless
Posts: 22
Registered: 25-7-2012
Member Is Offline
Mood: No Mood
|
|
I don't doubt it. Maybe its also deliquescent too? Its holding a lot of moisture beyond the hydrate, for sure.
|
|
|
![[*]](images/xpblue/default_icon.gif){kind=icon}