Elemental Chromium from Paint
Chromium(III) Oxide is a common green pigment, it is literally easy to get and i was wondering if the following reaction can be done.
Cr<sub>2</sub>O<sub>3</sub> + 6HCl = 2CrCl<sub>3</sub> + 3H<sub>2</sub>O
CrCl<sub>3</sub> + Al = Cr + AlCl<sub>3</sub>
Could all that take place at room temperature? and does a solution containing Chromium(III) Chloride react with Aluminum or any other metal more
reactive then it?
Also How high of temprature would you have to reach for the following reaction to take place
Cr<sub>2</sub>O<sub>3</sub> + 3C = 2Cr + 3CO
|
|
MrHomeScientist
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1806
Registered: 24-10-2010
Location: Flerovium
Member Is Offline
Mood: No Mood
|
|
Your first scheme of an aqueous reaction of the chloride with aluminum would work, to yield fine Cr powder. Assuming you can dissolve the oxide in
acid, that is. That can be difficult depending on how the oxide was prepared. I don't know enough to comment on the reduction with carbon, but I'm
sure it's possible.
To make lumps of Cr metal, you can use the thermite reaction with powdered Al:
Cr<sub>2</sub>O<sub>3</sub> + 2Al --> Al<sub>2</sub>O<sub>3</sub> + 2Cr
I've done this many times. It's difficult to ignite if your powders aren't very fine and well-mixed.
|
|
blogfast25
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
Correct, MrHomeScientist.
To make Cr thermites run better add a small amount of finely ground K2Cr2O7 to the mix: about 0.05 mol per mol of the oxide (adjust the amount of Al
accordingly). This makes the thermite run hotter, smoother and should increase Cr yield.
But reduction with carbon would require blast furnace type conditions...
[Edited on 19-7-2012 by blogfast25]
|
|
Chemistry Alchemist
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 403
Registered: 2-8-2011
Location: Australia
Member Is Offline
Mood: No Mood
|
|
Ive got a Oxytorch which reaches really high temperatures, if i focus the energy to a single point, is that enough to smelt the chromium oxide?
|
|
woelen
Super Administrator
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 7998
Registered: 20-8-2005
Location: Netherlands
Member Is Offline
Mood: interested
|
|
Cr2O3 from potteries cannot be dissolved in acids. It is calcined oxide and such oxides are VERY inert and even boiling in conc. HCl or 50% H2SO4 does
not dissolve any of it. You need molten NaOH or molten NaHSO4 to dissolve this oxide and these are not pretty at all to deal with.
I think that the Cr2O3/C mix can be used to create Cr, but I have no personal experience with that at all. Probably you need very high temperatures in
a vessel in which air is excluded. Probably the Cr produced in that way is impure and may contain dissolved carbon.
|
|
Chemistry Alchemist
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 403
Registered: 2-8-2011
Location: Australia
Member Is Offline
Mood: No Mood
|
|
Would there be a way to purify the metal afterwards? Maybe if your yield is high enough, could you add the chromium metal back into HCl and dissolve
it to remove carbon, and then add Aluminum to it afterwards to get back the chromium and then melt it afterwards again?
|
|
blogfast25
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
If you have purity concerns about the oxide, why not synth it yourself?
Reduce potassium dichromate in acid conditions with methylated spirits, now you have basically a Cr (III) salt with some ethanoic and methanoic acid.
Neutralise carefully (Cr (III) is amphoteric!) to precipitate blueish/green Cr(OH)3.nH2O. Wash with copious amounts of hot water to remove salts.
Softly calcine till dryness, now you have Cr2O3. Good purity Cr2O3 will give good quality metal in thermite
|
|
MrHomeScientist
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1806
Registered: 24-10-2010
Location: Flerovium
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by blogfast25 ![](images/xpblue/lastpost.gif) | Correct, MrHomeScientist.
To make Cr thermites run better add a small amount of finely ground K2Cr2O7 to the mix: about 0.05 mol per mol of the oxide (adjust the amount of Al
accordingly). This makes the thermite run hotter, smoother and should increase Cr yield.
But reduction with carbon would require blast furnace type conditions...
[Edited on 19-7-2012 by blogfast25] |
Interesting, thanks for the tip! I think I recently ran out of the oxide, but I'll certainly give the dichromate addition a try next time I run this
type of thermite. Someday soon I'm going to make a thermite montage video that has lots of different types, and perhaps a thermite 'guide' that has
tips like yours.
I also finally found some ground fluorite on eBay, so I scooped that up and I'll be trying your titanium thermite formulation as well. Exciting times
ahead!
|
|
francis
Hazard to Self
![*](images/xpblue/star.gif)
Posts: 72
Registered: 1-4-2011
Location: Australia
Member Is Offline
Mood: No Mood
|
|
What sort of paint do you have, as in, what does it say it's used for? And is it solvent based or water based? Out of curiosity, what brand is it?
Cheers
|
|
SM2
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 359
Registered: 8-5-2012
Location: the Irish Springs
Member Is Offline
Mood: Affect
|
|
Why not go to junk yard, and reverse electro-plate off any of Detroit's finest. J/K. I'd be leery messing w/ the hexavalent, but the thermite
process looks tried and true..
careful, heavy metals.
|
|
blogfast25
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
It doesn't 'look' tried and true: it IS true. Both theory (thermodynamics) and practice confirm that Cr metal is easy to produce with aluminothermy,
provided you know what you are doing. I've got the Cr nuggets to prove it.
|
|