hot acid resistant coating for steel
I would like to coat a steel reaction vessel so it can withstand hot HCl. I am considering enamel but I need a recipe that is used in the industry.
|
|
dann2
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1523
Registered: 31-1-2007
Member Is Offline
Mood: No Mood
|
|
You could coat with Ta, not too simple though.
Can Teflon bags be purchased. You could perhaps place one inside the vessell.
I cannot get a paper on Ta coating to attach, will try later.
It involves a molten Ta salt.
[Edited on 17-9-2011 by dann2]
|
|
Chordate
Hazard to Others
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 108
Registered: 23-2-2011
Member Is Offline
Mood: No Mood
|
|
Used in industry? usually thats done by either teflon, ceramic, or glass coating.
Theres a couple of ways to go about glass coating steel. Industrially, this is done by thermal decomposition of silane. This... is troublesome, Silane
is a pyrophoric gas and decomposes at 400-500 degrees. Lower temps can be achieved by using hydrogen fluoride gas . Industrially: this is doable. To
you or I, this seems like a real good way to die.
Now, a little while ago some chaps figured out how to make really fine particles of sillicon dioxide, which can be turned into a suspension which just
sprays right onto materials and renders them pretty chemically inert. Awesome! They are holding on to their method and their supplies very
tight-fistedly. This is unsurprising, because microstructured sillicon dioxide is probably not the healthiest thing to be handling either.
That said there are a few people out there who will apply such a coating for you professionally. I just have no idea how much it costs. Glass coating
is nice for its thermal properties
Alternatively, there are some people who make chemically resistant thermal-set epoxies which are designed to be applied to steel. These guys came up on a quick google search. Googling for chemical resistant epoxy though will give you an idea of whats out there.
|
|
Endimion17
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1468
Registered: 17-7-2011
Location: shores of a solar sea
Member Is Offline
Mood: speeding through time at the rate of 1 second per second
|
|
Steel reaction vessel? Is it steel because the vessel is to be pressurized? If it is, you need to mention that. If there's no extra pressure, why not
simple borosilicate glass?
How hot acid are we talking about, and what's the pressure?
|
|
roy30103
Harmless
Posts: 4
Registered: 15-9-2011
Member Is Offline
Mood: No Mood
|
|
OK, more info
I want steel because of about 100KPa gauge pressure. Bake-ware enamel would probably work fine. I have some frit made from borosilicate glass. I was
wondering what additives to put with the frit.
|
|
dann2
International Hazard
![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif) ![*](images/xpblue/star.gif)
Posts: 1523
Registered: 31-1-2007
Member Is Offline
Mood: No Mood
|
|
Paper here on Ta coating.
[Edited on 18-9-2011 by dann2]
Attachment: Tantalum Plating.rar (1.7MB) This file has been downloaded 353 times
|
|