Amos
International Hazard
Posts: 1406
Registered: 25-3-2014
Location: Yes
Member Is Offline
Mood: No
|
|
Viridian pigments
As some of you may know, I'm currently on a quest to produce a full set of artist's paints myself using chemistry. Just recently I decided to try a
procedure for producing the pigment viridian, a hydrated chromium(III) oxide, using the procedure found here.
4 grams of sodium dichromate dihydrate(ceramic grade) and 13 grams of boric acid(roach killer) were mixed and added to a small iron dish lined with
aluminum foil. The mixture is shown below.
The dish was then put into a rudimentary wood-burning furnace/kiln which was heated to roughly 500 °C for two hours, which was as much time as I
could spare at the time. The high temperature was maintained by me manually driving air into the burning chamber of the furnace by fanning it with a
board; I've got hand blisters to prove it 
The dish removed from the furnace contained a large greenish plume of glassy material. It was filled with air pockets and had gained considerable
volume due to the water vapor and oxygen released during the reaction. Inevitably some of the aluminum foil lining stuck to and partially fused with
the mass, but the lining itself ensured that the contents of the dish were easily removed.
After allowing it to cool, the unsightly thing was broken into smaller pieces and tossed into a beaker containing ~400mL of water. The water in which
the fused mass had been cast became bright yellow, indicating dissolved sodium chromate from the decomposition of the dichromate used as a starting
material. Many of the pieces were quick to crumble in the solution and sink to the bottom, but those with the most intense green color and which
contained the greatest amount of glass floated and did not break up further; these were collected separately from the green mud which precipitated at
the bottom.
The floaters were immediately dried, ground into powder, and then ground again under water and re-dried. The solids that settled to the bottom of the
beaker were first treated with sodium hydroxide solution to dissolve any residual aluminum from the lining of the heating dish, then filtered out,
dried, and ground.
The picture below shows the pigments thus obtained from the process and a test with a brush for each. The pigment produced from the solids that
floated upon being cast into water is at the top, and was more blue in color. The second pigment, produced from the solids that settled to the bottom,
is at the bottom of the picture and has a more typical chromium(III) oxide color. The pigment in the middle is a mix of the two.
This was a really fun experiment to try out, especially given its rustic nature, and I'm quite happy with the results. On to yellows for my next paint
pigments!
[Edited on 3-28-2015 by Amos]
|
|
|
careysub
International Hazard
Posts: 1339
Registered: 4-8-2014
Location: Coastal Sage Scrub Biome
Member Is Offline
Mood: Lowest quantum state
|
|
Thanks, that is neat!
I find the olde arts fascinating, and would like to try my hand at a few...
|
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
Interesting. Any idea in what way this pigment differs substantially from plain Cr<sub>2</sub>O<sub>3</sub>, which is after
all what gives 'Viridian' its vibrant green colour?
|
|
|
Amos
International Hazard
Posts: 1406
Registered: 25-3-2014
Location: Yes
Member Is Offline
Mood: No
|
|
Quote: Originally posted by blogfast25  | | Interesting. Any idea in what way this pigment differs substantially from plain Cr<sub>2</sub>O<sub>3</sub>, which is after
all what gives 'Viridian' its vibrant green colour? |
Since most of the resources aren't quite as scientific in nature, they're kind of vague, however, the consensus seems to be that the oxide readily
hydrates after substantial heating and cooling. This paper also mentions that a byproduct of the calcination process includes a hydrated chromium oxide borate that is also green in color.
Oh, and if the rain and cold ever stops here , I'll be firing up the furnace
again and hopefully decomposing chromium hydroxide to make chromium(III) oxide via another route, and I'll compare it to the viridian I made. I also
want to make the viridian again and fire it longer, to see if I get more of the first pigment I described, with more of a bluish color.
[Edited on 3-28-2015 by Amos]
|
|
|
chloric1
International Hazard
Posts: 1141
Registered: 8-10-2003
Location: GroupVII of the periodic table
Member Is Offline
Mood: Stoichiometrically Balanced
|
|
| Quote: Originally posted by blogfast25 | | Interesting. Any idea in what way this pigment differs substantially from plain Cr<sub>2</sub>O<sub>3</sub>, which is after
all what gives 'Viridian' its vibrant green colour? |
To me it seems that the blue hue is causes by hydration or maybe hydrogen bonding between borate and hydroxyl groups. Is it possible to create a
section on sciencemadness about artistic applications of chemcals? A board concerning, pigments, patinas, ceramics and glazes, painting mediums and
filler materials. I believe a large percentage of us could contribute. 
BTW that is good work Amos. I grateful that you shared this with us.
[Edited on 11/8/2015 by chloric1]
Fellow molecular manipulator
|
|
|
Bert
Super Administrator
Posts: 2821
Registered: 12-3-2004
Member Is Offline
Mood: " I think we are all going to die. I think that love is an illusion. We are flawed, my darling".
|
|
| Quote: |
The high temperature was maintained by me manually driving air into the burning chamber of the furnace by fanning it with a board; I've got hand
blisters to prove it
|
I have used a cheap blow dryer from a yard sale on the cold air setting. Doesn't take much power to run, without the heating elements. I just use a
small inverter and my truck batteries for a typical smelt, without even killing the batteries... Fueled with charcoal this will make an extremely hot
fire, hot enough to ruin my makeshift refractory furnace lining!
Rapopart’s Rules for critical commentary:
1. Attempt to re-express your target’s position so clearly, vividly and fairly that your target says: “Thanks, I wish I’d thought of putting it
that way.”
2. List any points of agreement (especially if they are not matters of general or widespread agreement).
3. Mention anything you have learned from your target.
4. Only then are you permitted to say so much as a word of rebuttal or criticism.
Anatol Rapoport was a Russian-born American mathematical psychologist (1911-2007).
|
|
|
chloric1
International Hazard
Posts: 1141
Registered: 8-10-2003
Location: GroupVII of the periodic table
Member Is Offline
Mood: Stoichiometrically Balanced
|
|
| Quote: Originally posted by Bert |
| Quote: |
The high temperature was maintained by me manually driving air into the burning chamber of the furnace by fanning it with a board; I've got hand
blisters to prove it
|
I have used a cheap blow dryer from a yard sale on the cold air setting. Doesn't take much power to run, without the heating elements. I just use a
small inverter and my truck batteries for a typical smelt, without even killing the batteries... Fueled with charcoal this will make an extremely hot
fire, hot enough to ruin my makeshift refractory furnace lining! |
Well then you have something that will meet most of our needs here. Smelting copper alloys, calcinations, etc.. Do you use briquettes or hardwood
chacoal?
Fellow molecular manipulator
|
|
|
Bert
Super Administrator
Posts: 2821
Registered: 12-3-2004
Member Is Offline
Mood: " I think we are all going to die. I think that love is an illusion. We are flawed, my darling".
|
|
I have used both. Natural charcoal burns faster, is cheaper, and if used in reverberatory configured furnace, seems to have a more "luminous" flame.
Rapopart’s Rules for critical commentary:
1. Attempt to re-express your target’s position so clearly, vividly and fairly that your target says: “Thanks, I wish I’d thought of putting it
that way.”
2. List any points of agreement (especially if they are not matters of general or widespread agreement).
3. Mention anything you have learned from your target.
4. Only then are you permitted to say so much as a word of rebuttal or criticism.
Anatol Rapoport was a Russian-born American mathematical psychologist (1911-2007).
|
|
|
Amos
International Hazard
Posts: 1406
Registered: 25-3-2014
Location: Yes
Member Is Offline
Mood: No
|
|
Thanks, chloric. I've actually found a very reliable procedure for making beautiful Chrome Orange, too. I've just been too lazy to make a thread on
its preparation.
|
|
|
![[*]](images/xpblue/default_icon.gif){kind=icon}