jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
Hello 12AX7,
Being that I haven't had a chance to try making any anodes yet, I can't say how critical the conditions are for the anodizing method I
found, but I would be surprised if things like temperature, concentration of acid, current density, etc. didn't affect the quality of the
results.
With regard to your theory that the "contact resistance" between Pb and PbO2 may be high, I'm wondering what would happen if you change
your method of making electrical contact? IOW what if you somwhow clamp to the outside of the PbO2, rather than rely on the Pb-PbO2 interface to
conduct current?
Lastly, with regard to plating PbO2 from a lead salt, check out the link below. That guy just used copper for the cathode and he apparently had no
problems, but he was using lead nitrate.
Regards,
Joe
http://www.satollo.com/en/chemistry/csld-ceramic-substrate-l...
|
|
|
12AX7
Post Harlot
Posts: 4803
Registered: 8-3-2005
Location: oscillating
Member Is Offline
Mood: informative
|
|
I doubt the PbO2 is in wide flakes, it's just generally loose stuff.
So the technique is just amps and Pb(NO3)2? Why doesn't this plate Pb?
Tim
|
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
Strictly speaking, maybe it does actually plate lead first, and then the lead is immediately oxidized? I don't know.
|
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
Another Idea
Taking the plastic substrate idea one step further, I wonder if the anode could be made of epoxy mixed with powdered PbO2, and either used like that
or with a subsequently plated PbO2 coating?
|
|
|
12AX7
Post Harlot
Posts: 4803
Registered: 8-3-2005
Location: oscillating
Member Is Offline
Mood: informative
|
|
Or for that matter, get a paint base and fill it to 90% PbO2 like conductive Al/Zn paint. I seem to remember linseed oil is already quite popular
with electrode builders.. 
Tim
|
|
|
unionised
International Hazard
Posts: 5126
Registered: 1-11-2003
Location: UK
Member Is Offline
Mood: No Mood
|
|
I wonder if I should start a new thread for this and call it "anything but silicon as an electrode, mainly dealing with PbO2".
Anyway what I did, with a view to at least starting to answer the question that this thread is about, was to use a lump of silicon as the anode in a
cell with salt water as the electrolyte and a platinum casthode.
Result; a distinct smell of chlorine. I'm suprised, I would have expected the silicon to be atacked.
Of course, that's not the whole story, you would need to run a real chlorate cell with the stuff to prove the point.
Amazing what a little experiment can do.
Unfortunately, as it's buried at the end of a whole bunch of stuff about lead anodes, I don't supose anyone will ever find this data unless
people decide to delete or move their off-topic postings.
And I don't care that half of the off-topic posts are by the original author.
[Edited on 11-7-2005 by unionised]
|
|
|
12AX7
Post Harlot
Posts: 4803
Registered: 8-3-2005
Location: oscillating
Member Is Offline
Mood: informative
|
|
| Quote: | Originally posted by unionised
And I don't care that half of the off-topic posts are by the original author.
|
Thread drift stimulates the mind. Something wrong with that? 
Tim
|
|
|
jpsmith123
National Hazard
Posts: 764
Registered: 24-6-2005
Member Is Offline
Mood: No Mood
|
|
Unionised:
Sorry that the discussion has wandered.
It seems that there are already so many chlorate/perchlorate cell related discussions here, I hesitated to start yet another. (Moreover, I'm new
here and I'm still learning the rules).
Should I start another discussion regarding PbO2 anodes?
In any case, with regard to your experiment, may I ask, what kind of silicon did you use?
Lastly, with regard to chlorine, I guess your experiment shows that chlorine won't attack silicon in an aqueous environment?
12AX7:
I just now saw the following paper for the first time:
http://www.geocities.com/CapeCanaveral/Campus/5361/chlorate/...
The "contact resistance" thing might be one reason people seem to have so much trouble with PbO2.
|
|
|
unionised
International Hazard
Posts: 5126
Registered: 1-11-2003
Location: UK
Member Is Offline
Mood: No Mood
|
|
Hi
I guess I get overly annoyed about people going off topic. Anyway, I'm afraid I can't say much about the Si. It was a lump I got in with
some stuff I got from ebay.
|
|
|
neutrino
International Hazard
Posts: 1583
Registered: 20-8-2004
Location: USA
Member Is Offline
Mood: oscillating
|
|
There's no need to start a new thread on PbO<sub>2</sub> electrodes; there's already a long one on the subject.
|
|
|