Plastics recycling: why not treat waste as crude oil ?
Several articles appear in the media on plastic waste and it is so hard to dispose it off or recycle it.
https://www.smh.com.au/national/nsw/not-sure-what-can-and-ca...
Plastic is made from polymerized hydrocarbons, sometimes added chlorine (PVC) or fluorine (Teflon / PFAS).
When heated to 200-300 C, most will turn into a soup like hot crude oil and can be cracked to make new hydrocarbons to be processed.
When heated even more (500 or more C) it will decompose and the resulting gases can be processed to new hydrocarbons.
Am I too simplistic ?
I guess such a process is more expensive that making HCs from virgin crude oil.
What are your thoughts ?
|
|
|
12thealchemist
Hazard to Others
Posts: 181
Registered: 1-1-2014
Location: The Isle of Albion
Member Is Offline
Mood: Rare and Earthy
|
|
The problem is you have to put in a lot of heat and energy to convert the plastic to crude oil, and it's cheaper to get brand new crude oil than to
back-convert plastic. The principle is sound - I've done it myself, and to great success, but it's very energy inefficient.
(Energy = gas, electricity, coal, etc.)
An answer, I suppose, is to use an incinerator for that which cannot be destructively distilled, and use the heat from that to thermolyse the
remaining plastics.
|
|
|
B(a)P
International Hazard
Posts: 1139
Registered: 29-9-2019
Member Is Offline
Mood: Festive
|
|
IMHO the issue is the unquenchable desire for plastic products. If we burn the plastics more need to be made. We need to stop using them or develop
technologies to properly recycle them.
|
|
|
madcedar
Hazard to Others
Posts: 116
Registered: 10-9-2009
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by metalresearcher  | Several articles appear in the media on plastic waste and it is so hard to dispose it off or recycle it.
https://www.smh.com.au/national/nsw/not-sure-what-can-and-ca...
Plastic is made from polymerized hydrocarbons, sometimes added chlorine (PVC) or fluorine (Teflon / PFAS).
When heated to 200-300 C, most will turn into a soup like hot crude oil and can be cracked to make new hydrocarbons to be processed.
When heated even more (500 or more C) it will decompose and the resulting gases can be processed to new hydrocarbons.
Am I too simplistic ?
I guess such a process is more expensive that making HCs from virgin crude oil.
What are your thoughts ?
|
I have wondered the same thing for years. It seems like a no brainer to crack the plastic down into petroleum products. Interestingly the article you
link to mentions that plastic bags are the problem and yet the pie chart shows that beverage containers are >50% of the waste. The energy costs
would be of no consequence given that the fuel for running the plant arrives by the truck load for the cost of just picking it up from the normal
garbage runs, something that is already happening anyway. I assume the difficulties in the process is dealing with the metals, wood and garbage that
inevitably ends up in the recycle waste. Those issues would be sorted out and equipment refined over time as experience grows.
|
|
|
MadHatter
International Hazard
Posts: 1339
Registered: 9-7-2004
Location: Maine
Member Is Offline
Mood: Enjoying retirement
|
|
Recycling
I live in Maine, 1 of 10 states that have refundable
deposits on plastic, glass and metal beverage
containers. We have redemption centers for people
to turn them in. The law prohibits containers from
from other states. Any plastic I can't turn in gets
burned along with any paper in the wood stove and
plastic burns hot. Despite this people still throw
cans and bottle on the side of the road. This is
pure laziness. I often take walks and bring a trash
bag with me and collect anything I find on the side
of the road. Their loss, my gain and environment is
a little cleaner for it despite some burning in the
wood stove. Burning is a way to "recover" some of
energy used to manufacture paper and plastic. It
returns heat and may save a few trees(and money).
[Edited on 2019/12/27 by MadHatter]
From opening of NCIS New Orleans - It goes a BOOM ! BOOM ! BOOM ! MUHAHAHAHAHAHAHA !
|
|
|
metalresearcher
National Hazard
Posts: 757
Registered: 7-9-2010
Member Is Offline
Mood: Reactive
|
|
| Quote: Originally posted by MadHatter | I live in Maine, 1 of 10 states that have refundable
deposits on plastic, glass and metal beverage
containers. We have redemption centers for people
to turn them in. The law prohibits containers from
from other states. Any plastic I can't turn in gets
burned along with any paper in the wood stove and
plastic burns hot. Despite this people still throw
cans and bottle on the side of the road. This is
pure laziness. I often take walks and bring a trash
bag with me and collect anything I find on the side
of the road. Their loss, my gain and environment is
a little cleaner for it despite some burning in the
wood stove. Burning is a way to "recover" some of
energy used to manufacture paper and plastic. It
returns heat and may save a few trees(and money).
[Edited on 2019/12/27 by MadHatter] |
Weird that they don't accept foreign (i.e. interstate) containers. That should be ruled federally.
Plastic in the woodstove ??? That is a very bad idea, toxic fumes may expel from your chimney and it will damage your flue as well and increase the
risk of a flue fire and when that occurs and the insurance knows you burn plastic, they may not pay you.
Rather write your local council how they can better handle plastic waste.
|
|
|
andy1988
Hazard to Others
Posts: 135
Registered: 11-2-2018
Location: NW Americus ([i]in re[/i] Amerigo Vespucci)
Member Is Offline
Mood: No Mood
|
|
| Quote: Originally posted by metalresearcher |
When heated to 200-300 C, most will turn into a soup like hot crude oil and can be cracked to make new hydrocarbons to be processed.
When heated even more (500 or more C) it will decompose and the resulting gases can be processed to new hydrocarbons.
|
Here is a recent line of research you can read on that, 850C.
The problem I see convincing municipalities in my area to recycle is that they don't want to pay anything more than what it costs to ship it to the
dump. They imagine innovators and the "free market" will somehow satisfy their demand, and if not, they don't care. Even if you develop a great
process, good luck getting financing for equipment under those constraints. Then again I suppose the new material produced might be worth it?
[Edited on 27-12-2019 by andy1988]
|
|
|
mysteriusbhoice
Hazard to Others
Posts: 477
Registered: 27-1-2016
Member Is Offline
Mood: Became chemistry catboy Vtuber Nyaa
|
|
better off incinerating the plastic in a special furnace to produce electricity directly, thats already a thing!!
|
|
|
rockyit98
Hazard to Others
Posts: 283
Registered: 12-4-2019
Location: The Known Universe
Member Is Offline
Mood: no mood is a good mood
|
|
the true meaning of the three arrows.
for me it's reduce reuse hoard till it's recycling day.
"A mind is a terrible thing to lose"-Meisner
|
|
|
stoichiometric_steve
National Hazard
Posts: 827
Registered: 14-12-2005
Member Is Offline
Mood: satyric
|
|
There is already a process called "Hydrothermal Carbonisation" that was adapted and patented for plastics.
|
|
|
pneumatician
Hazard to Others
Posts: 411
Registered: 27-5-2013
Location: Magonia
Member Is Offline
Mood: ■■■■■■■■■■ INRI ■■■■■■■■■■ ** Igne Natura Renovatur Integra **
|
|
https://www.youtube.com/results?search_query=japanese+plasti...
another for recicle tires producind excess electricity...
human ego and avarice my friend.
|
|
|
RogueRose
International Hazard
Posts: 1592
Registered: 16-6-2014
Member Is Offline
|
|
I was reading some things about what to do with mixed plastic waste, like highly degraded plastic bags (heavy duty 1-2 ton tote bags and such) and
other plastics that crumble after exposure to UV, as it's really bad to recycle it, and a suggestion was to use to to generate H2 similar to water-gas
generation that makes H2 and CO IIRC. Heating the plastic to where it vaporizes w/o O2 and running the gas through hot charcoal or coal and it
supposedly breaks it down into a high quality stream of H2 and probably CO and CO2. IDK if the H2 can be separated out and the CO used to heat the
plastic, but that would be a good use I would think.
As for the mention of tires, I've seen a number of good uses and one that has been used for some time is in the production of lime/CaO or cement as it
needs a lot of heat and tires burn very hot. The problem is that there is significant SO2 emissions from this. Another use for tires that I've seen
is using it in paved roads where saftey, low noise or high longevity is a high priority. The rubber is used in the top layer and it greatly reduces
stopping distances, increases grip on tires (going around turns and such) even while wet, it also allows for much more quiet running of vehicles on
roads. Finally, it supposedly can allow the surface to last up to 2-3x longer than a standard asphalt finish, IDK how thick/deep it needs to be or
what % is needed to be added, but all of these seem to be pretty nice features of using chipped or powdered recycled tires. It can also be used as
the complete surface of a road or driveway where they do tar and chipping (different than being mixed into the asphalt), and again it supposedly has
the features I mentioned above.
|
|
|
Panache
International Hazard
Posts: 1290
Registered: 18-10-2007
Member Is Offline
Mood: Instead of being my deliverance, she had a resemblance to a Kat named Frankenstein
|
|
Recycling
An expensive but virtuous process that turns waste that nobody wants into raw materials that nobody wants.
Are there thermal lava flows anywhere predictable enough to use as a heat source for the cracking?
The Germans and the Japanese have blast furnaces utilising pellets of compressed polyolefins, heated to red heat as carbon source. Unsure of how
economical they are but sound theory.
I've always thought we should bail up the polymer waste into huge cubes and build a replica great pyramid of Giza...sure would create some jobs and
tourism for the town building it in addition to the revenue for accepting the waste.
I worked on recycled polyethylene back in the 90's it's exceedingly difficult. You need such little contaminant for everything to go to shit. Makes ok
railway sleepers for use in constructing piers.
|
|
|