For anyone that wants here is the book mentioned above
Attachment: William M. Yen Marvin J. Weber - Inorganic Phosphors_ Compositions, Preparation and Optical Properties (2004).pdf (6.6MB)
This file has been downloaded 1339 times
Green QD's so far
Feel free to correct grammar or incorect knknowledge. We are all learning.
|
|
|
vano
National Hazard
Posts: 661
Registered: 22-3-2019
Location: Georgia
Member Is Offline
|
|
Good book Housane.
|
|
|
Bedlasky
International Hazard
Posts: 1239
Registered: 15-4-2019
Location: Period 5, group 6
Member Is Offline
Mood: Volatile
|
|
Housane: Thank you very much! This is really useful source.
[Edited on 9-2-2021 by Bedlasky]
|
|
|
Bezaleel
Hazard to Others
Posts: 444
Registered: 28-2-2009
Member Is Offline
Mood: transitional
|
|
What a find! Thanks for posting it here.
|
|
|
Dr. Noreen Wakeman
Harmless
Posts: 1
Registered: 15-2-2021
Member Is Offline
Mood: impassioned
|
|
I've found many phosphor dyes just by using a black light on different markers I have. My original
intention was to use it as a homemade TLC plate backing with the intent of allowing me to observe the different components without wasting acid. If
you aren't trying to make invisible ink, I recommend this process as you can easily remove the ink from these markers by taking out the ink reservoir
and putting it in boiling 0.01M NaCl water. The ink will flow out of the foam reservoir and into the water thus giving you the ink.
To know too little is ignorance
To know too much is intelligence
Sanity lies in-between
Yet I never resided betwixt them
I am either too dumb to understand
Or too knowledgeable to be at peace
Choose wisely when to learn and when not to learn
|
|
|
stibium
Harmless
Posts: 7
Registered: 9-12-2015
Member Is Offline
Mood: No Mood
|
|
I found a link with a lot of pictures, ideas, projects and recipes about fluorescent and phosphorescent materials:
https://www.flickr.com/photos/28617364@N04/albums/with/72157...
|
|
|
QuantumDot
Harmless
Posts: 7
Registered: 16-4-2019
Member Is Offline
|
|
I've found two papers claiming to have made photoluminescent Cu and Mn doped ZnS nanoparticles using room temperature wet chemical methods...
*without* firing in a furance. They only dried the material at 70C in a hot air oven.
Low temperatures, no inert atmospheres. Seems too good to be true!
Extracts from the "materials and methods" sections:
Manganese doped:
" Chemical precipitation technique used in this study has the distinct qualities such as low processing temperature (<100 °C), simplicity of
processing, low cost and high rate of powder collection. Synthesis of pure ZnS nanoparticles by wet chemical method was reported by the authors
previously [21]. We followed the same procedure in the synthesis of manganese doped ZnS nanoparticles. Twenty five milliliter each of zinc acetate Zn
(CH3COO)2, MnCl2 and Na2S solutions in water were used for the preparation of Mn2+ doped ZnS nanoparticles. 0.001 M solution of MnCl2 was added drop
wise to 1 M zinc acetate Zn(CH3COO)2 solution. One molar Na2S solution was added drop wise with continuous stirring using magnetic stirrer. The
solution was stirred for 20 min keeping temperature constant. The resulting white colloidal suspension was filtered, and the filtrate was washed with
de-ionized water and dried by keeping in an oven at 70 °C for 1 day. Three samples were prepared at room temperature, 50 and 70 °C. "
Copper doped:
" ZnS:Cu nanoparticles have been prepared by chemical precipitation technique without any capping agent, similar to our previous work [29]. Cu doped
ZnS have precipitated from a mixture of zinc acetate [Zn (CH3COO)2] and copper nitrate [Cu(NO3)2] with sodium sulphide [Na2S] in water in ratio of 1:1
for Zn:S. The precipitate thus formed was filtered, washed with distilled water and dried by keeping in a hot air oven at 70 °C for 16 h. In this way
five samples were synthesised at room temperature with different Cu (0.0005, 0.001, 0.002, 0.003 & 0.004 M) concentrations. The same procedure was
also followed for the synthesis of all the ZnS:Cu nanoparticles at 50 °C, 70 °C and 90 °C keeping Cu concentration (0.001 M) same. "
I've also attached their original paper where they first synthesized (undoped) ZnS nanoparticles.
Attachment: bindu2015.pdf (819kB)
This file has been downloaded 261 times
Attachment: bindu2012.pdf (668kB)
This file has been downloaded 268 times
Attachment: bindu2021 (1).pdf (762kB)
This file has been downloaded 281 times
|
|
|
Neal
Hazard to Others
Posts: 143
Registered: 24-12-2021
Location: Chicago, IL, USA.
Member Is Offline
|
|
I did not know polyurethane can phosphoresce, or fluoresce. I recall polyurethane is something you can put on wood to prevent sunlight changing the
color.
And I was recently aware that certain rocks can fluoresece.
|
|
|
knowledgevschaos
Harmless
Posts: 41
Registered: 9-8-2023
Location: Sci-Hub and the hardware store
Member Is Offline
Mood: Hungry for information
|
|
Phosphorescent calcium sulfide can be made through heating 1 part crushed oyster shells with 2 parts sulfur. Apparently oyster shells are better than
pure calcium carbonate, because minerals and impurities in the shells act to dope the calcium sulfide. I haven't been able to make this yet but I'm
looking forward to trying.
https://sciencenotes.org/make-glow-dark-powder-oyster-shells...
|
|
|