what material use to lacquer beryllium?
I have a beryllium cube that I want to protect from the environment. It is special high purity, so it is oxidizing much faster than beryllium normally
does (in other words, my question is not SHOULD I protect it, it's HOW should I protect it).
What type of readily available clear lacquer or varnish should I use to get the most protection that won't just peel off in a couple weeks?
\"…\'tis man\'s perdition to be safe, when for the truth he ought to die.\"
|
|
|
Eclectic
National Hazard
Posts: 899
Registered: 14-11-2004
Member Is Offline
Mood: Obsessive
|
|
Heat in kiln to 500 C to build up adherent protective coating of BeO?
I had some Aircraft parts I burned the potted copper windings out of. It did not seem to harm the Be a bit a bright red heat
|
|
|
UnintentionalChaos
International Hazard
Posts: 1454
Registered: 9-12-2006
Location: Mars
Member Is Offline
Mood: Nucleophilic
|
|
Quote: Originally posted by Eclectic  | Heat in kiln to 500 C to build up adherent protective coating of BeO?
I had some Aircraft parts I burned the potted copper windings out of. It did not seem to harm the Be a bit a bright red heat
|
I was under the impression that beryllium would ignite and burn at those kind of temperatures and that it behaved somewhat like a cross between
aluminum and magnesium. Oxidation resilient at room temperature but burns with a vengeance when heated enough.
I have a piece of machinable stock that I suspect is intended for making X-ray windows (not the punched sheet kind). The density is very close to the
theoretical density of beryllium and fingerprints on it slowly turn a darker gray over time, but exposure to the atmosphere does nothing.
Assuming it is indeed beryllium, why not just drop it in some mineral oil or kerosene? Then you need not worry about the "coating" ever getting crummy
looking or peeling off.
Department of Redundancy Department - Now with paperwork!
'In organic synthesis, we call decomposition products "crap", however this is not a IUPAC approved nomenclature.' -Nicodem
|
|
|
Fleaker
International Hazard
Posts: 1252
Registered: 19-6-2005
Member Is Offline
Mood: nucleophilic
|
|
I think iamthewaffler knows what's beryllium and what isn't. Also, if the cube were small enough to put into a jar or mineral oil or kerosene, I'm
sure he would've done it.
I'm sure there are numerous things that would work for this.
I wonder if carnauba wax would do it? It is very hard, clear when applied thin, and ought to protect against oxygen. It's also commercially available
and dissolves up nicely in gasoline or xylene/toluene. Only problem I can see is acidity.
I tihnk acrylic might be your best option.
Neither flask nor beaker.
"Kid, you don't even know just what you don't know. "
--The Dark Lord Sauron
|
|
|
Eclectic
National Hazard
Posts: 899
Registered: 14-11-2004
Member Is Offline
Mood: Obsessive
|
|
You really should need do nothing to protect it....It should form tightly adhering impervious coating of the oxide, much like aluminum and titanium.
|
|
|